Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 7, Article number: 2503 (2017 ) Cite this article In Bar
![Combined magnetron sputtering and pulsed laser deposition of TiO 2 and BFCO thin films | Scientific Reports](http://cdn.globalso.com/rsmtarget/TiB2.png)
We report the successful demonstration of a hybrid system that combines pulsed laser deposition (PLD) and magnetron sputtering (MS) to deposit high quality thin films. The PLD and MS simultaneously use the same target, leading to an enhanced deposition rate. The performance of this technique is demonstrated through the deposition of titanium dioxide and bismuth-based perovskite oxide Bi2FeCrO6 (BFCO) thin films on Si(100) and LaAlO3 (LAO) (100). These specific oxides were chosen due to their functionalities, such as multiferroic and photovoltaic properties (BFCO) and photocatalysis (TiO2). We compare films deposited by conventional PLD, MS and PLD combined with MS, and show that under all conditions the latter technique offers an increased deposition rate (+50%) and produces films denser (+20%) than those produced by MS or PLD alone, and without the large clusters found in the PLD-deposited films. Under optimized conditions, the hybrid technique produces films that are two times smoother than either technique alone.
The growth of thin films and nanostructures can be pursued using a number of technologies, the most successful of which also allow for tailoring the structure so as to optimize optical, electrical, tribological and other properties1,2,3,4.
These properties, among others, depend critically on the film density, surface morphology5, 6 and crystallographic structure. Amongst various deposition technologies, physical vapor deposition (PVD) techniques for thin film production have found widespread use in many industrial sectors. Magnetron sputtering (MS) is a thin-film PVD technique that is widely used to synthesize highly uniform and smooth films7 on large surface areas. It offers several advantages compared to thermal or e-beam deposition techniques, since the higher energy in MS atoms can improve adhesion and help to define the deposited film structure. Control over the deposition process could further be improved if the operating pressure of MS, which is typically in the few to tens of mTorr range, could be reduced. The minimum pressure required in a conventional MS system is defined by the ionization rates in the plasma7. Operating at higher pressures has a direct effect on the structure and density of deposited films, since the sputtered species lose part of their energy through interaction with the background gas molecules.
Pulsed laser deposition (PLD) is another important PVD technique for thin film and nanostructure growth1, 8,9,10, which can be applied at any pressure, offering more versatility. The ability to control the background pressure and the substrate-to-target distance enables the possibility of controlling the density of the deposited film11. However, despite its popularity and widespread use within the research community, the PLD process has faced some challenges related to scaling up for large-area deposition. Another drawback relates to the large clusters that often form during the ablation process8, 9; these clusters can introduce undesired inhomogeneity and roughness into the films. Reduction of the pulsed laser energy density helps to reduce or eliminate macroparticle formation, but also lowers the deposition rate.
Several approaches and techniques have been developed to address these challenges relating to film quality in both MS and PLD12,13,14. Unbalanced magnetron sputtering15, the high power impulse MS (HIPIMS) process16, and plasma assisted PLD17 are recent developments that can improve certain characteristics of the deposited films. Techniques to overcome the limitations of PLD for large surface applications are also being proposed and demonstrated18, 19.
One promising approach is to combine magnetron sputtering and pulsed laser deposition (MSPLD) into a hybrid system. In most implementations, MSPLD comprises the use of two targets (one for sputtering and one for PLD) that can be used simultaneously20,21,22,23,24. This technique has shown promise for the preparation of functional gradient transition metal carbides and multilayer structures in the TiC and diamond-like carbon (DLC) material systems as well as for other nanocomposites25,26,27,28,29. Another hybrid approach involved combining PLD with radio frequency (RF) sputtering at the substrate, where the applied RF power can be used to exercise some control over film properties such as composition and crystallinity30, 31.
Here, we implement a different hybrid approach that circumvents some of the limitations of traditional MS and PLD by using a single target for both the MS and PLD. Under this hybrid approach, the pulsed laser can be used to trigger and maintain the magnetron discharge at lower pressures, adding another control mechanism for tuning the deposited film structure.
To demonstrate the advantages of the hybrid technique we have studied the growth of TiO2 thin films on Si(100), as well as the growth of complex bismuth-based perovskite Bi2FeCrO6 (BFCO) on LaAlO3 (LAO) (100). TiO2 is a widely studied semiconducting material with attractive characteristics such as a high refractive index, wide band gap, and photocatalytic properties. BFCO has been recently widely studied due to its multi-ferroic and photovoltaic properties. We have investigated the effects of substrate temperature, operating pressure, pulsed laser and MS power density on the properties of films, and the process has been optimized for power efficiency. Our results show that the hybrid technique leads to improved quality of the deposited films, as well as increasing film uniformity and deposition rate.
Figure 1 shows a schematic diagram of the hybrid system. In a hybrid PLD/MS system, the plasma plume liberated by the laser pulse triggers and maintains the magnetron discharge at a lower pressure than in a standard MS system. This increased pressure leads to an increase in the plasma density and sputtering rate. Both neutral species and ions pass through the confining magnetic field and are deposited on the substrate, directly influencing the deposited film thickness and structure. The combined PLD/MS system increases the deposition rate through two mechanisms: (1) increased plasma sputtering rate and (2) direct PL deposition of neutral atoms and clusters.
Combined Pulsed Laser Deposition + Magnetron Sputtering System. The target is exposed to the PLD laser (the dark purple vertical plume in the picture) and to the plasma generated by the sputtering system (in light purple in the picture) at the same time. B represents the magnetic field while E is the electric field.
Figure 2 displays representative AFM images of TiO2 samples obtained using MS, PLD and the hybrid technique at an operating pressure of 5 mTorr. Regardless of which technique is used, the surface roughness of the TiO2 films decreases with decreasing argon pressure (Fig. 3a). Samples fabricated at 1 mTorr, corresponding to the minimum operational pressure, have low roughnesses (~0.18 nm RMS) that are identical within uncertainty for all deposition techniques. However, the growth rates were very slow at 1 mTorr. At low power and pressure, sputtering is inefficient since the collisions are limited, reducing the yield, while the low power limits the movement of the ions. At 5 mTorr the hybrid system consistently operated at a higher growth rate (+50%) while achieving roughness values significantly lower than those obtained through PLD or MS alone (0.25 ± 0.01 nm RMS vs. 0.34 ± 0.02 nm RMS and 0.34 ± 0.02 nm RMS). At higher pressure the surface mobility of the deposited species is reduced due to the impinging argon flux, which manifests in the formation of grains with an average lateral size of 35 ± 4 nm (Figure S2).
AFM images (on an area of 1 μm × 1 μm.) of the TiO2 films realized with the three different techniques (a) Magnetron Sputtering (MS), (b) Pulsed Laser Deposition (PLD) and (c) hybryd technique (MS/PLD) at 5 mTorr.
Morphological parameters of thin films. (a) AFM-measured roughness of 5 μm × 5 μm TiO2 films as a function of argon pressure. (b) Growth rate of TiO2 films at different values of pressure.
Figure 4 displays the x-ray reflectivity (XRR) data for TiO2 samples obtained using different pressures and deposition techniques. The period of oscillation depends on the film thickness, with shorter periods corresponding to thicker films32. XRR data also indicate a critical angle, θ c, which is related to the density of the film. For θ < θ c total reflection occurs, whereas above θ c , the XRR signal decreases rapidly with increasing incident angle. The film deposited with the hybrid technique at 5 mTorr exhibits a larger critical angle (Fig. 4b), indicating that it has a higher density compared to the other film.
Reflectivity of TiO2 samples on Si(100) substrates. (a) XRR of the samples deposited at 40mTorr with the three different techniques. In the inset the model used for fitting the data: between the TiO2 and Si layers it was necessary to add a thin layer of SiO2 (size not in scale), consistent with the presence of a thin native oxide layer at the surface. (b) XRR of samples at 5 mTorr. (c) Comparison of the samples deposited with hybrid technique at two different pressure, 5 and 40 mTorr. (d) Scattering Length Density values for TiO2 layers deposited with the three techniques (MS,PLD and hybrid MS/PLD) at two different pressures, 5 and 40 mTorr. The horizontal dashed line represents the tabulated SLD of bulk TiO2 (34.46 × 10−6 Å−2)33.
On average, slower decays in reflectivity were observed for the samples grown with the hybrid technique, indicating that the surface roughness is smaller. An exception is the sample obtained at 40 mTorr with the hybrid technique, which has the largest XRR-determined roughness, consistent with AFM measurements. In general at higher pressure the surface mobility of diffusing species is reduced due to reduced energy of impinging particles, leading to rougher surfaces.
Figure 4d shows the Scattering Length Density (SLD) obtained from analysis of the XRR data for TiO2 layers obtained at 40 mTorr and 5 mTorr. The SLD is directly related to the density of the film, with higher values indicating more tightly packed scattering entities. This analysis reveals that independent of the deposition pressure, the hybrid technique produces films with 15–25% higher SLD than MS alone. At the optimal pressure of 5 mTorr the film has the highest value of SLD, which is similar to the tabulated value for bulk TiO2 (34.8 vs 34.5 10−6Å−2)33
The hybrid technique was also used to fabricate BFCO films on LAO(100), to investigate whether the use of sputtering combined with PLD could enhance the growth rate and/or uniformity of the film. Since epitaxial growth is necessary to control the crystalline phase and cation ordering of BFCO, which are linked to its functional properties34, we focused on obtaining epitaxial film growth using the hybrid technique.
Through a systematic variation of parameters, we identified the optimum growth conditions (temperature at 750 °C and pressure at 10 mTorr, laser power 4.4 W and MS discharge 30 W) for which the film presented a smooth surface with an AFM-measured RMS roughness of less than 6 nm. To evaluate the crystallinity of the samples, we measured XRD patterns. Diffraction from samples fabricated on Si(100) did not reveal any crystalline phases. Diffraction from films grown on LAO(100) is shown in Fig. 5.
XRD of BFCO samples on LAO (100). Preparation by hybrid MS/PLD at 750 °C is the only route tested that leads to a pure BFCO phase.
The sample made with the hybrid technique at 750 °C on LAO(100) produces only diffraction peaks from the substrate and the BFCO layer. Only the 00l (l = 1, 2, 3) cubic reflections of the films are visible, indicating that the films are highly (001)-oriented. These peaks are consistent with data found in literature35,36,37 and confirm the epitaxial growth of the film.
Rocking curve measurements (Fig. 6c) reveal the highly crystalline quality of the BFCO layer, with a full width half maximum (FWHM) of 0.2° around BFCO(002). The epitaxial ordering of BFCO using the hybrid technique is confirmed by the diffraction pattern analysis (φ-scan) reported in Fig. 6b and d, in which we observe a fourfold symmetry of the epitaxial relationship between the BFCO layer and the LAO substrate.
Detailed diffraction data from the BFCO layer grown at 750 °C with the hybrid technique. (a) 2θ-scan and (c) rocking curve of BFCO(002) peak. The red line is a Lorentzian fit to the data (black). Corresponding φ-scan measurements around the (200) reflection on the bare substrate (b) and the BFCO film (d) confirm the epitaxial growth of the film.
The film grown at 560 °C using the hybrid technique (blue line in Fig. 5) exhibits additional reflections that can be attributed to the presence of Bi-rich phases36,37,38. The film also has a higher RMS roughness value (~12 nm), and AFM shows large particles 196 ± 50 nm in lateral size and 48 ± 19 nm in height uniformly covering the surface (Fig. 7b and Figure S3). For films fabricated using only sputtering, the result is similar: non-epitaxial growth with some secondary phases (BFC*), as indicated in the diffractogram (black line in Fig. 5). AFM data obtained from this film show elongated structures with grains ~290 ± 63 nm in lateral size and 14 ± 5 nm in height (Fig. 7a and Figure S3). The differences between the MS and the PLD processes for BFCO on Si(100) are clearly visible in the SEM images displayed in Fig. 7d and Fig. 7e. The film deposited by PLD contains droplets with a lateral size of ~480 ± 76 nm (Figure S4) and height of 100 nm, whereas the film grown by MS is uniform and much finer-grained. Figure 7f shows the film growth with the hybrid technique on LAO(100). In general the film is uniform, with occasional grains visible on the surface.
AFM images on an area of 5 μm × 5 μm of different BFCO thin film samples: (a) BFCO on LAO(100) deposited with MS at 750 °C, (b) BFCO on LAO(100) deposited with MS/PLD at 650 °C, (c) BFCO on LAO(100) deposited with MS/PLD at 750 °C. SEM images of films prepared by sputtering, PLD and by hybrid technique: (d) MS deposition of BFCO on Si(100), (e) PLD deposition of BFCO on Si(100), (f) MS/PLD deposition on LAO (100) at 750 °C. The scale bar is 1 μm.
To verify that the hybrid technique produced a functional BFCO thin film, we investigated its ferroelectric properties by piezoresponse force microscopy (PFM) in several randomly chosen areas. Representative PFM images of the ferroelectric domains in epitaxial BFCO obtained by the hybrid technique are reported in Fig. 8. The out-of-plane and in-plane components of the PFM signal are simultaneously recorded together with topography (Fig. 8a–c). In general, for the out-of-plane measurement (Fig. 8b), yellow areas indicate regions with the z-components of spontaneous polarization oriented upwards while blue areas denote a polarization component oriented in the opposite direction, downwards. In the in-plane measurement, the different colors indicate opposite lateral components of the spontaneous polarization. Figure 8d reports the piezo-response hysteresis loop of the out-of-plane component recorded from the area highlighted in Fig. 8a and b. In Figure S5, we also show the in-plane hysteresis loop recorded on the same area. The existence of hysteresis loops confirm the presence of a switchable ferroelectric polarization, hence confirming the ferroelectric character of the BFCO film produced by the hybrid technique36, 38. We carried out a similar investigation on films grown by PLD and MS alone but no piezoresponse was observed (Figure S6), confirming that the hybrid technique was the only deposition approach capable of synthesizing a functional BFCO film.
AFM/PFM measurements of BFCO produced with the MS/PLD technique. (a) Contact topography AFM image (area 2 μm x 2 μm) (b) simultaneously recorded out-of-plane PFM image (b) and (c) in-plane PFM. The z-range is 25 nm for topography; the z-scale for PFM images is in arbitrary units. The scale bar is 400 nm. (d) Piezoresponse hysteresis loop recorded from the area highlighted by the dotted circle.
We have demonstrated the efficacy of simultaneously combining PLD and MS in a hybrid deposition system for the synthesis of functional materials. TiO2 films grown on Si(100) using the hybrid approach exhibit favorable physical properties. When deposited under optimal conditions, they are smoother and denser (~20% more dense for deposition at 5 mTorr) than films produced by either PLD or MS alone. The hybrid technique was also capable of growing epitaxial films of BFCO on LAO(100), suggesting that it could be useful for the controlled synthesis of multifunctional oxides. For both types of materials, the deposition rate of the hybrid technique is 50% higher than either PLD or MS in isolation. Since only minimal changes are required to modify an existing PLD or MS system for hybrid deposition, this approach may be appealing for industrial applications. These initial results indicate that the hybrid PLD/MS approach could be a useful, easily implemented addition to the existing repertoire of film deposition techniques.
All experiments were carried out on a Glaze series PLD system commercialized by Plasmionique Inc. with a 1″ Magnion series magnetron. Three types of samples were fabricated: films were grown with (i) PLD alone (KrF Lumonics PM-800 excimer laser, λ = 248 nm, pulse duration = 15.4 ns), (ii) MS alone, (iii) the hybrid system (PLD/MS). TiO2 films were deposited on Si(100) at room temperature under three different partial argon pressures: 1, 5 and 40 mTorr. Two different values of laser power were used: 0.56 W and 4.6 W (measured at 20 Hz), and the sputtering power was in the range 35 ÷ 60 W. The repetition rate was fixed at 10 Hz and the deposition duration at 1 hr. Following previous work35, 36, BFCO films were deposited on Si(100) and LAO(100) at different argon/oxygen pressures (ratio 3:1, 10 and 70 mTorr) and temperatures (560–750 °C). The laser power (λ = 248 nm) was varied between 0.56 W and 4.6 W (measured at 20 Hz) and the sputtering power was in the range 26 ÷ 60 W. The minimum working pressure for maintaining a stable plasma was found to be 1 mTorr while the minimum laser power was 0.56 W. Under these conditions the minimum power applied on the magnetron for successful generation of a plasma was 35 W.
XRD and XRR were carried out to analyze the crystal quality, film orientation and film thickness using a high-resolution Panalytical X’pert Pro diffractometer equipped with a Cu Kα source. The XRR data were fitted using the MOTOFIT add-on39 for IGOR Pro data analysis software (WaveMetrics, Inc.), which uses the Abeles matrix method to calculate reflectance in stratified media, allowing for the extraction of parameters such as the roughness of the interfaces and the thickness and the scattering length density of each of the layers in the sample. The reported uncertainty values for the XRR data were generated by MOTOFIT. For a detailed explanation of the method, refer to Supplementary Info.
The average growth rates were calculated from final film thicknesses determined by either XRR, AFM or with a profilometer. At least three measurements were collected using each technique, and the reported uncertainties reflect the spread of values obtained from these measurements.
The morphology of the deposited thin films was characterized using SEM (FE-SEM LEO 1525 microscope) and AFM (Veeco Enviroscope). The RMS roughness values were calculated as an average of different areas (at least three) of 5 × 5 μm2. For PFM, an oscillating testing voltage of 0.5 V was applied between the tip and the substrate. Hysteresis measurements were obtained using an auxiliary digital-to-analog converter of the computer-controlled lock-in amplifier by sweeping an additional direct current (DC) bias voltage between −30 V and +30 V.
Lowndes, D. H., Geohegan, D. B., Puretzky, A. A., Norton, D. P. & Rouleau, C. M. Synthesis of novel thin-film materials by pulsed laser deposition. Science 273, 898–903, doi:10.1126/science.273.5277.898 (1996).
Article ADS CAS PubMed Google Scholar
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 3893, 1312–1315, doi:10.1126/science.1171245 (2009).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710, doi:10.1038/nature07719 (2009).
Article ADS CAS PubMed Google Scholar
Craciun, V., Elders, J., Gardeniers, J. G. E. & Boyd, I. W. Characteristics of high quality ZnO thin films deposited by pulsed laser deposition. Appl. Phys. Lett. 65, 2963–2965, doi:10.1063/1.112478 (1994).
Article ADS CAS Google Scholar
Domine, D., Haug, F. J., Battaglia, C. & Ballif, C. Modeling of light scattering from micro- and nanotextured surfaces. J. Appl. Phys. 107, 044504, doi:10.1063/1.3295902 (2010).
Xi, J. Q. et al. Optical thin-film materials with low refractive index for broadband elimination of Fresnel reflection. Nat. Photon. 1, 176–179 (2007).
Kelly, P. & Arnell, R. Magnetron sputtering: a review of recent developments and applications. Vacuum 56, 159–172, doi:10.1016/S0042-207X(99)00189-X (2000).
Willmott, P. & Huber, J. Pulsed laser vaporization and deposition. Rev. Mod. Phys. 72, 315–328, doi:10.1103/RevModPhys.72.315 (2000).
Article ADS CAS Google Scholar
Ashfold, M. N., Claeyssens, F., Fuge, G. M. & Henley, S. J. Pulsed laser ablation and deposition of thin films. Chem. Soc. Rev. 33, 23–31, doi:10.1039/b207644f (2004).
Article CAS PubMed Google Scholar
Chrisey, D. B. & Hubler, G. H. Pulsed Laser Deposition of Thin Films. (John Wiley & Sons, Inc., 1994).
Riabinina, D., Chaker, M. & Rosei, F. Correlation between plasma dynamics and porosity of Ge films synthesized by pulsed laser deposition. Appl. Phys. Lett. 89, 131501, doi:10.1063/1.2356689 (2006).
Paraguay, D. F., Estrada, L. W. & Acosta, N. D. Growth, structure and optical characterization of high quality ZnO thin films obtained by spray pyrolysis. Thin Solid Films 350, 192–202, doi:10.1016/S0040-6090(99)00050-4 (1999).
Helmersson, U., Lattemann, M., Bohlmark, J., Ehiasarian, A. P. & Gudmundsson, J. T. Ionized physical vapor deposition (IPVD): A review of technology and applications. Thin Solid Films 513, 1–24, doi:10.1016/j.tsf.2006.03.033 (2006).
Article ADS CAS Google Scholar
Sankur, H. O. & Gunning, W. Deposition of optical thin films by pulsed laser assisted evaporation. Appl. Opt. 28, 2806–2808, doi:10.1364/AO.28.002806 (1989).
Article ADS CAS PubMed Google Scholar
Diserens, M., Patscheider, J. & Levy, F. Mechanical properties and oxidation resistance of nanocomposite TiN–SiN x physical-vapor-deposited thin films. Surf. Coat. Technol. 121, 158–165, doi:10.1016/S0257-8972(99)00481-8 (1999).
Schiller, S. et al. Pulsed magnetron sputter technology. Surf. Coat. Technol. 61, 331–337, doi:10.1016/0257-8972(93)90248-M (1993).
De Giacomo, A., Shakhatov, V., Senesi, G. S. & Orlando, S. Spectroscopic investigation of the technique of plasma assisted pulsed laser deposition of titanium dioxide. Spectrochim. Acta B 56, 1459–1472, doi:10.1016/S0584-8547(01)00274-9 (2001).
Lorenz, M. et al. Large‐area double‐side pulsed laser deposition of YBa2Cu3O7−x thin films on 3‐in. sapphire wafers. Appl. Phys. Lett. 68, 3332–3334 (1996).
Article ADS CAS Google Scholar
Dietsch, R., Holz, T., Weißbach, D. & Scholz, R. Large area PLD of nanometer-multilayers. Appl. Surf. Sci. 197–198, 169–174, doi:10.1016/S0169-4332(02)00320-3 (2002).
Voevodin, A., Capano, M., Safriet, A., Donley, M. & Zabinski, J. Combined magnetron sputtering and pulsed laser deposition of carbides and diamond‐like carbon films. Appl. Phys. Lett. 69, 188–190, doi:10.1063/1.117367 (1996).
Article ADS CAS Google Scholar
Voevodin, A. A., Capano, M. A., Laube, S. J. P., Donley, M. S. & Zabinski, J. S. Design of a Ti/TiC/DLC functionally gradient coating based on studies of structural transitions in Ti–C thin films. Thin Solid Films 298, 107–115, doi:10.1016/S0040-6090(96)09145-6 (1997).
Article ADS CAS Google Scholar
Hunter, C. N., Check, M. H., Muratore, C. & Voevodin, A. A. Electrostatic quadrupole plasma mass spectrometer measurements during thin film depositions using simultaneous matrix assisted pulsed laser evaporation and magnetron sputtering. J. Vac. Sci. Technol. A 28, 419–424 (2010).
Novotný, M., Bulíř, J., Lančok, J. & Jelínek, M. A Comparison of Plasma in Laser and Hybrid Laser-Magnetron SiC Deposition Systems. Plasma Processes and Polymers 4, S1017–S1021, doi:10.1088/0957-4484/24/9/095301 (2007).
Burmakov, A. P., Kuleshov, V. N. & Prokopchik, K. Y. Characteristic Features of the Formation of a Combined Magnetron-Laser Plasma in the Processes of Deposition of Film Coatings. Journal of Engineering Physics and Thermophysics 89, 1271–1276, doi:10.1007/s10891-016-1491-8 (2016).
Article ADS CAS Google Scholar
Voevodin, A. A., Hu, J. J., Jones, J. G., Fitz, T. A. & Zabinski, J. S. Growth and structural characterization of yttria-stabilized zirconia–gold nanocomposite films with improved toughness. Thin Solid Films 401, 187–195, doi:10.1016/S0040-6090(01)01615-7 (2001).
Article ADS CAS Google Scholar
Endrino, J. L., Nainaparampil, J. J. & Krzanowski, J. E. Microstructure and vacuum tribology of TiC–Ag composite coatings deposited by magnetron sputtering-pulsed laser deposition. Surf. Coat. Technol. 157, 95–101, doi:10.1016/S0257-8972(02)00138-X (2002).
Jelínek, M. et al. KrF laser deposition combined with magnetron sputtering to grow titanium–carbide layers. Thin Solid Films 506–507, 101–105, doi:10.1016/j.tsf.2005.08.040 (2006).
Bulíř, J., Novotný, M., Jelínek, M., Kocourek, T. & Studnička, V. Plasma study and deposition of DLC/TiC/Ti multilayer structures using technique combining pulsed laser deposition and magnetron sputtering. Surf. Coat. Technol. 200, 708–711, doi:10.1016/j.surfcoat.2005.01.087 (2005).
Jelinek, M., Kocourek, T., Zemek, J., Novotný, M. & Kadlec, J. Thin SiC x layers prepared by hybrid laser–magnetron deposition.Appl.Phys.A 93, 633–637, doi:10.1007/s00339-008-4727-4 (2008).
Article ADS CAS Google Scholar
Klotzbücher, T., Scherge, M., Mergens, M., Wesner, D. A. & Kreutz, E. W. Deposition of carbon nitride thin films in a hybrid r.f.-PLD technique. Surf. Coat. Technol. 98, 1072–1078, doi:10.1016/S0257-8972(97)00286-7 (1998).
Klotzbücher, T., Mergens, M., Wesner, D. A. & Kreutz, E. W. C-BN thin film formation in a hybrid r.f.-PLD technique. Diamond Relat. Mater. 6, 599-603 2432 (1997).
Yasaka, M. X-ray thin-film measurement techniques. The Rigaku Journal 26 (2010).
P. Kienzle NIST. Neutron activation and scattering calculator, www.ncnr.nist.gov/resources/activation/ (2014).
Nechache, R. & Rosei, F. Recent progress in nanostructured multiferroic Bi2FeCrO6 thin films. J. Solid State Chem. 189, 13–20, doi:10.1016/j.jssc.2012.01.022 (2012).
Article ADS CAS Google Scholar
Nechache, R., Harnagea, C. & Pignolet, A. Multiferroic properties-structure relationships in epitaxial Bi2FeCrO6 thin films: recent developments. J. Phys. Condens. Matter 24, 096001, doi:10.1088/0953-8984/24/9/096001 (2012).
Article ADS CAS PubMed Google Scholar
Nechache, R. et al. Epitaxial thin films of the multiferroic double perovskite Bi2FeCrO6 grown on (100)-oriented SrTiO3 substrates: Growth, characterization, and optimization. J. Appl. Phys. 105, 061621, doi:10.1063/1.3073826 (2009).
Nechache, R. et al. Photovoltaic properties of Bi2FeCrO6 epitaxial thin films. Appl. Phys. Lett. 98, 202902, doi:10.1063/1.3590270 (2011).
Nechache, R. et al. Epitaxial patterning of Bi2FeCrO6 double perovskite nanostructures: multiferroic at room temperature. Adv. Mater. 23, 1724–1729, doi:10.1002/adma.201004405 (2011).
Article CAS PubMed Google Scholar
Nelson, A. Co-refinement of multiple-contrast neutron/X-ray reflectivity data using MOTOFIT. J. Appl. Crystallogr. 39, 273–276, doi:10.1107/S0021889806005073 (2006).
This work was supported by the Natural Sciences and Engineering Research Council of Canada (NSERC) through an Engage Grant (H.P.) and a Discovery Grant (F.R.). F.R. also acknowledges the Canada Research Chairs program for partial salary support. J.M. acknowledges support from Queensland University of Technology (QUT). D.B. acknowledges L. Corbellini for XRD experimental assistance and C. Harnagea for help with PFM measurements.
INRS Center for Energy, Materials and Telecommunications, 1650 Boul.Lionel Boulet, J3X 1S2, Varennes, QC, Canada
D. Benetti, H. Pepin, F. Rosei & J. M. MacLeod
Plasmionique Inc., 1650 Boul.Lionel Boulet, J3X 1S2, Varennes, QC, Canada
R. Nouar & A. Sarkissian
School of Chemistry, Physics, and Mechanical Engineering, Queensland University of Technology (QUT), Brisbane, 4001, QLD, Australia
Department of Electrical Engineering, Ecole de Technologie Supérieure, 1100 rue Notre-Dame Ouest, Montréal, QC H3C, 1K3, Canada
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
H.P., A.S., F.R. and J.M. conceived the study. D.B., R. Nouar and R. Nechache performed the experiments, D.B. and J.M. analyzed the data. D.B. drafted the manuscript, and all authors contributed to revisions that brought it to its final form.
Correspondence to F. Rosei or J. M. MacLeod.
The authors declare that they have no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
Benetti, D., Nouar, R., Nechache, R. et al. Combined magnetron sputtering and pulsed laser deposition of TiO 2 and BFCO thin films. Sci Rep 7, 2503 (2017). https://doi.org/10.1038/s41598-017-02284-0
DOI: https://doi.org/10.1038/s41598-017-02284-0
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
![Combined magnetron sputtering and pulsed laser deposition of TiO 2 and BFCO thin films | Scientific Reports](http://cdn.globalso.com/rsmtarget/d12d268c.png)
Aluminium Sputtering Target Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.