Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 13, Article number: 22749 (2023 ) Cite this article Lanthanum chloride
![A novel facile synthesis of metal nitride@metal oxide (BN/Gd2O3) nanocomposite and their antibacterial and anticancer activities | Scientific Reports](http://cdn.globalso.com/epomaterial/H492c52401ab74a1f94d083e5c83cf11dk1.jpg)
In this study, a novel core/shell nanocomposite structure (h-BN@Gd2O3 NCs) was created for the first time by combining hexagonal boron nitride (h-BN) with doped gadolinium oxide (Gd2O3) using different laser pulse numbers, i.e., 150, 338, and 772 pulses. We employed various analytical techniques, including mapping analysis, FE-SEM, EDS, HRTEM, SAED, XRD, zeta potential analysis, DLS, FTIR, Raman spectroscopy, and PL measurements, to characterize the synthesized h-BN, c-Gd2O3, and h-BN@Gd2O3 NCs (338 pulses). XRD results indicated hexagonal and cubic crystal structures for BN and Gd2O3, respectively, while EDS confirmed their chemical composition and elemental mapping. Chemical bonds between B–N–Gd, B–N–O, and Gd–O bands at 412, 455, 474, and 520 cm−1 were identified by FTIR analysis. The antimicrobial and anticancer activities of these NCs using agar well diffusion and MTT assays. They exhibited potent antibacterial properties against both Gram-positive and Gram-negative pathogens. Furthermore, NCs have reduced the proliferation of cancerous cells, i.e., human colon adenocarcinoma cells (HT-29) and human breast cancer cells (MCF-7), while not affecting the proliferation of the normal breast cell line (MCF-10). The anticancer efficacy of NCs was validated by the AO/EtBr assay, which confirmed apoptotic cell death. Blood compatibility on human erythrocytes was also confirmed by hemolytic and in vitro toxicity assessments. The compiled results of the study proposed these nanoparticles could be used as a promising drug delivery system and potentially in healthcare applications.
Nanotechnology has revolutionized therapeutic approaches by creating materials at the nanoscale. Nanoparticles possess unique properties that differ from larger particles, influencing their interactions within biological systems. Size is important in biological processes such as crossing barriers and immune recognition. Nanotechnology offers advantages over conventional methods by enhancing cellular retention and penetration. Particles larger than 100 nm but with exceptional properties are also considered nanomaterials1,2. Currently, there is a pressing need for an advanced treatment approach that can effectively overcome the barrier posed by the cell membrane and ensure targeted drug delivery and sustained retention at the desired site. In comparison to conventional agents, drugs engineered at the nanoscale can offer a multitude of pharmacological advantages. The creation of unique and superior "Nano-drugs" is possible by fusing the extensive understanding of nanoparticles (NPs) with the most recent knowledge of cellular and molecular activities3. These NPs possess the remarkable ability to encapsulate, incorporate, or conjugate various drug molecules, enabling precise delivery to specific targets3,4,5. Cancer, among other devastating diseases, remains a major cause of mortality and demands urgent intervention. Breast cancer, in particular, continues to claim a significant number of lives worldwide6. The utilization of existing chemotherapy drugs has its drawbacks, including high costs, toxicity, and severe side effects. Therefore, in order to solve this urgent crisis, it is essential to investigate alternative medicines, such as nanomedications and nanoformulations for drug delivery.
Metal oxide nanoparticles (MONPs) and metal nitride nanoparticles (MNNPs) are highly sought-after nanomaterials in the realm of biologically active nanoparticles. This is mainly because of their compact size and high surface-to-volume ratio, making them increasingly utilized in medical and consumer products. Recently, MONPs and MNNPs have attracted great interest as antibacterial and anticancer drugs due to their exceptional performance, enhanced properties, cost-effectiveness throughout their life cycle, and extensive applicability in various industrial sectors and biomedical applications7. Despite significant advancements in nanotechnology, the effects of gadolinium oxide (Gd2O3) and boron nitride (BN) NPs on cancer cell lines are not yet definitively understood. Previous research on NPs has indicated their relative toxicity to cancer cells while sparing healthy cells4. Notably, considerable attention is being directed towards Gd2O3 and BN NPs due to their cost-effectiveness, being approximately 10 times cheaper than silver and gold in the market8. Thus, utilizing BN and Gd2O3 NPs would not only provide an effective method but also prove economically advantageous. Furthermore, BN and Gd2O3 NPs have demonstrated antibacterial properties against both Gram − ve and Gram + ve microorganisms, displaying high sensitivity even at low concentrations of BN and Gd2O3 NPs9,10,11.
Gd2O3 has emerged as a promising candidate with potential antibacterial properties. Recent research has focused on exploring the efficacy of Gd2O3NPs in inhibiting bacterial growth and eliminating bacterial biofilms12. These nanoparticles have shown promising results in combating various types of bacteria, including both Gram + ve and Gram − ve strains. The antibacterial effects of gadolinium oxide nanoparticles can be attributed to their capacity to generate reactive oxygen species (ROS) when exposed to light or heat. This ROS production induces oxidative stress and damages bacterial cells, leading to their demise. Additionally, Gd2O3NPs have proven effective in disrupting bacterial biofilms, which are notorious for their resilience against antibiotics9,12.
BN is a compound comprised of boron and nitrogen atoms structured in a hexagonal lattice formation. It possesses exceptional characteristics that make it a highly promising material for a variety of applications, including those within the medical field13. In terms of antibacterial uses, BNNPs have demonstrated the potential to inhibit bacterial growth. These nanomaterials are capable of physically interacting with bacterial cell membranes, resulting in membrane disruption and subsequent bacterial death11. Moreover, BNNPs exhibit antibacterial activity by releasing ions, such as borate and nitrate ions, which impede bacterial function and hinder their growth. When considering its applications in the realm of cancer treatment, BN has been examined for its potential as a drug delivery system and photothermal therapy agent. Its remarkable thermal conductivity allows for the efficient conversion of light into heat, which facilitates the targeted destruction of cancer cells during photothermal therapy14. Additionally, BNNPs can serve as carriers for anticancer drugs, enhancing their stability and enabling more precise administration to tumor sites. It is important to note that while both Gd2O3 and BN exhibit promise in antibacterial and anticancer applications, further research is necessary to optimize their efficacy, comprehend their mechanisms of action, and assess potential side effects when used in clinical settings10,11.
Scientists are interested in hybridizing elements on the nanoscale due to their unique physicochemical features. This results in a new class of nanoparticles called "core–shell nanoparticles" that combine different types of nanoparticles. The surface-to-volume ratio increases, altering the characteristics, and the shell layer can enhance the core material's attributes15. The study found that Gd2O3 is the best shell material for h-BN due to its ability to undergo cell transition. This structure has potential applications in medicine and pharmaceuticals. Currently, a large number of chemical, physical, biological, and hybrid methods are available to synthesize different types of nanoparticles16. The nanoparticles formed using each method show specific properties17.
Pulse laser deposition (PLD)18,19, sol–gel preparation20,21, a high-speed stirring method22,23 and hydrothermal procedures13,24, 25 are a few of the methods that may be used to create NPs. However, a hybrid technique combining pulse laser ablation in liquid (PLAL) with laser fragmentation in liquid has gained favor since it is economical and ecologically beneficial. This hybrid approach has the benefit of requiring less expensive equipment and only a few minutes of setup time.
The process of creating nanomaterials through PLAL (Pulsed Laser Ablation in Liquid) involves absorbing a laser pulse from a material, which leads to the formation and cooling of a plasma plume. This leads to shock waves, creating bubbles in a liquid. Laser fragmentation, on the other hand, exposes micro- or Nano-powders suspended in a liquid to laser radiation. This melts particles in the laser beams' focus, interacting with the liquid's vapors and causing fragmentation. This method is used to reduce nanoparticle size and modify their morphology26,27,28.
Hybrid techniques involve combining two or more techniques to produce a new composition in suspension. An innovative method known as laser exfoliation and fragmentation in liquid (LEFL) has been developed, which utilizes a laser beam and probe sonication to separate BN layers into atomically thin sheets29. This process also creates binding sites on the surface of these sheets, enabling interaction with other two-dimension (2D) nanomaterials like graphene and NPs such as Gd2O3. By employing laser ablation in liquid, researchers can achieve precise control over the synthesis process, allowing for the production of hybrid nanocomposites (HNCs) from BN and Gd2O3 with tailored properties for specific applications, such as drug delivery systems or biomedical imaging30.
Currently, there is a research gap regarding the synthesis of the BN, Gd2O3, and BN@Gd2O3 NCs. To address this gap, we propose a novel two-step PLAL method that combines probe sonication and fragmentation. Our study aimed to investigate the influence of laser pulse quantity on the structural, morphological, and optical properties of the core–shell nanoparticles BN@Gd2O3. Therefore, the best conditions for synthesizing BN, Gd2O3, and BN@Gd2O3 were identified and subsequently analyzed. The primary objective of our research is to synthesize BN@Gd2O3 core–shell NPs for their potential use as an antibacterial agent. Additionally, this study is the first to investigate the effects of BN@Gd2O3 nanoparticles on Gram-ve bacteria (Escherichia coli and Proteus mirabilis) and Gram + ve bacteria (Streptococcus mutans and Staphylococcus aureus). A cytotoxic assay using MCF-10, MCF-7, and HT-29 to evaluate the impact of the synthesized h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs was also conducted.
The analytical-grade chemical materials of boron nitride and gadolinium oxide were purchased from Xian Lyphar Biotech Co., Ltd., China, and Sky Spring Nanomaterial, Inc., USA, respectively. From Sigma Chemical Co., St. Louis, USA, fetal bovine serum and 3-(4,5-dimethylthiazal-z-yl)-2,5-diphenyltetrazolium (MTT) were obtained. Dulbecco's Modified Eagle Medium (DMEM) was purchased from Euro Clone, Milan, Italy. The antibiotics penicillin and streptomycin (BioSource International, Nivelles, Belgium). Muller-Hinton agar medium, obtained from Mast, Liverpool, England.
The section on materials and methods describes the synthesis of h-BN and Gd2O3 nanoparticles. In our previous work29, we demonstrated laser exfoliation and fragmentation of BN in a liquid. To synthesize the nanoparticles, an Nd: YAG laser with 2 ns pulse duration at 3 Hz was used to focus on the Gd2O3 target and BN powder. The resulting ablated samples were collected by centrifuge to remove large particles before further use in vitro.
To create h-BN@Gd2O3 HNCs, we followed a two-step process. First, we prepared an h-BN suspension using similar steps as described in "Synthesis of h-BN and Gd2O3 NPs". In the second step, we ablated the Gd2O3 pellet using the same laser with a fluence of 1.27 Jcm-2 in colloid h-BN Ns solution at different numbers of laser pulses (150, 338, and 772). A schematic diagram of the procedure for the formation of h-BN@Gd2O3 NCs via the hybrid technique is shown in Fig. 1. Figure 2 shows a schematic diagram of the mechanisms of the formation of h-BN@Gd2O3 NCs via laser ablation in liquid technique. Selecting the appropriate parameter, such as the number of laser pulses, is crucial in antibacterial and cancer treatment experiments. This choice enables us to achieve the necessary high concentration for optimal results in eliminating bacteria or cancer cells. In addition, it helps us determine the ideal parameter for synthesis, which is 10 mJ with 338 pulses, as it yields the most favorable outcome.
(A) Illustration of the hybrid approach to preparing h-BN@c-Gd2O3 colloids. (B) Photographs for the prepared colloids of h-BN@c-Gd2O3 NCs.
Illustration of the mechanism for the formation of h-BN@c-Gd2O3 NCs colloids.
Several methods were used to examine the materials' morphology, structure, chemical, and optical properties. Field Emission Scanning Electron Microscopy (FE-SEM) with Energy Dispersive Spectroscopy (EDS) and mapping analysis were conducted using the Inspect F50 system (a small amount, one drop, of the prepared sample was deposited on a glass substrate). Transmission electron microscopy with high resolution (HR-TEM) from JEOL in Tokyo, Japan, was employed with Selected Area Electron Diffraction (SAED). A small amount (one drop) of the prepared sample was deposited on a gold mish, and then the samples underwent a coating process with a thin layer of gold to enhance imaging quality and reduce charging effects. X-ray crystallography (XRD) data were collected using a Shimadzu X-ray diffractometer at 40 kV and 25 mA with Cu-Kα radiation at 1.5405 Å. Nano plus DLS Nano Particle Sizer was used to assess the particle size and zeta potential (the colloidal sample was placed in a glass cuvette). Instruments of various types were used to evaluate chemical and optical qualities. A Perkin-Elmer spectrometer was used to collect FT-IR spectra in the 400–4000 cm−1 range. A THERMO SCIENTIFIC DXR FT-Raman spectrometer was used to record the Raman spectra. The laser source had a 2-mW output at 532 nm. Using a Shimadzu UV-2600 spectrometer, the UV absorbance spectra of the colloidal suspensions were determined between 200 and 500 nm. Shimadzu Spectra fluorophotometer model RF-5301pc was used to measure Photoluminescence Spectroscopy) PL (, and the colloidal sample was placed in a quartz cuvette.
Using an agar well diffusion experiment, the antimicrobial activity of the produced materials (h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs) was examined against both Gram-ve (Escherichia coli and Proteus mirabilis) and Gram + ve (Streptococcus mutans and Staphylococcus aureus) bacterial isolates, which were identified using the VITEK system (VITEK, Biomérieux, Marcy-l’Etoile, France), kindly provided by the Medical Microbiology Laboratory, Biotechnology Division, Department of Applied Science, University of Technology, Baghdad, Iraq. The McFarland standard was used to obtain suspensions at 1.5 × 108 colony-forming units (CFU) mL-1. Muller-Hinton (MH) agar was aseptically put onto sterile Petri plates in an amount of 20 mL. Using a sterile wire loop, the bacteria were extracted from their stock cultures. Using a sterile point, 6 mm-diameter wells were drilled into the agar plates after the organisms had been cultured. In the dreary wells. Before measuring and recording the average zones of inhibition diameter, the cultivated plates containing the test organisms and samples (h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs at a concentration of 50 µg mL−1 of each) were incubated overnight at 37 °C for 24 h in an upright position, and inhibition zones were measured in millimeters by measuring the diameter of circular inhibition zones around the well using a physical ruler. Deionized distilled water (DDW) was used as a control. The assay for antibacterial activity was performed in triplicate31.
The human colon adenocarcinoma cells (HT-29), Michigan Cancer Foundation-7 (MCF-7; human breast cancer cells), and normal breast MCF-10 were provided by the American Type Culture Collection (ATCC, Manassas, USA). The cells were grown in DMEM supplemented with 10% FBS, 2 mM l -glutamine, and 20 mM HEPES and employed using tissue culture-treated flasks (T 25 cm2; Falcon, USA) under the conditions of 5% CO2 and 37 °C.
To assess the cell viability and cytotoxicity of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs, cells were seeded (MCF-7, MCF-10, and HT-29: 4–6 × 104 cells per well in 100 μl culture media) in 96-well plates (SPL Life Sciences, Korea) and cultivated overnight. Afterward, cells with 70–80% of confluence were treated with diverse concentrations of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs (1, 5, 10, 15, 25, 50, and 75 µg/ml) and incubated for 24 h. Prior to conducting the experiment, the plates were incubated at 37 °C for 24 h with 20 μL of MTT (5 mg/ml in PBS), specifically thiazolyl blue tetrazolium bromide solution. Subsequently, the plates were kept in the dark for 4 h. The change from yellow MTT dye to purple formazan indicates the metabolic activity of the cells. Afterward, the MTT solution was removed, and each well was treated with 100 μL of dimethyl sulfoxide (DMSO) to dissolve the formazan. Using a Sat Fax 2100 microplate reader from Stat Fax, USA. Absorbance at a wavelength of 545 nm was measured to quantify the extent of dye conversion. The proportion of dye conversion by untreated cells was utilized to determine the viability and/or metabolic activity of the cells32. The formula (1) below was applied to determine the inhibition percentage:
where Abc and Abs were the optical density of the control and tested samples, respectively.
To assess the apoptosis effects of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs in HT-29 and MCF-7 cells, dual-labeling using AO/EtBr dye was carried out according to the method of Al-Jubori and his co-workers33. Briefly, cells were seeded (density 1 × 105 cells per mL) using DMEM in 96-well microtiter plates and incubated overnight. IC50 concentrations of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs were then applied for 24 h, followed by washing with PBS, applying dual fluorescent dyes (100 μL) to the cells, and finally visualized under a fluorescent microscope.
Fresh samples of blood were taken from five healthy donors and distributed into heparin-coated tubes based on the method of the NIH (National Institute of Health) and FDA (Food and Drug Administration) and as per the declaration and regulation of Helsinki of 1975 as a statement of ethical principles. Permission was obtained from the hospitals of the medical city in Baghdad, Iraq, and approved by the institutional ethical committee of the Department of Applied Sciences, University of Technology, Baghdad, Iraq (Ref. No. 216AS18/1/2021). Study participants were informed about the value of the study before we collected any samples. Informed consent was obtained from the study participants.
A hemolysis test was performed for the h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs samples based on a previously described method33. Briefly, whole blood (100 μL) was mixed with PBS (700 μL) and 100 μL of h-BNNs, c-Gd2O3Ns, or h-BN@Gd2O3NCs at seven concentrations (1, 5, 10, 15,25,50, and 100 μg mL−1) were added; phosphate buffer saline served as a negative control (0% hemolysis), whereas deionized distilled water served as a positive control (100% hemolysis). After shaking for 1 h at 37 °C, the reaction mixture is centrifuged at 700 rpm for 5 min, and the absorbance of the supernatant at 541 nm is measured. The hemolysis value percentages were therefore expressed in the following equation (2).
We utilized Graph Pad Prism version 8, Image J, and Origin 2021 software to analyze the results obtained from the conducted experiments. A one-way ANOVA was used to analyze the data, and then significant differences were set at * p ≤ 0.05, ** p ≤ 0.01, or *** p ≤ 0.01. Data were presented as mean ± standard deviation.
Figures 3 and 4 illustrate the morphology, structure, and particle size of the BNNs, Gd2O3Ns, and h-BN@Gd2O3 obtained with varying numbers of laser pulses. The FESEM analysis revealed that the structures change as the number of laser pulses increases in DDW. In Fig. 3a, the h-BNNs exhibit small particles with irregular spherical shapes and nanosheets, these results validate those of Guerra et al., Thangasamy et al., and Kumar et al.34,35,36. On the other hand, Gd2O3Ns (Fig. 3b) display nanofiber-like, needle-like, and sheets (leaf-like) morphologies with significant heterogeneity, clearly demonstrating the flaky structure of the prepared Gd2O3. The Gd2O3 nanocrystalline flakes are flat and have irregular shapes, as observed in the micrographs, these results validate those of Almeida et al., and Jeon et al.37,38. However, in the case of the nanocomposites during the synthesis of h-BN@Gd2O3, the h-BN and c-Gd2O3 particles tend to coalesce, as depicted in Fig. 3c–e. The results indicated that the h-BNNs consisted of spherical-shaped particles, while Gd2O3 exhibited numerous flake-like and sheets (leaf-like) morphologies with a layered structure, making it easy to identify the Nano type. Most of the nanostructures are interconnected, forming networks that do not exhibit well-ordered patterns, and their sizes and thicknesses vary.
The FESEM of (a) h-BNNs, (b) c-Gd2O3Ns, (c) h-BN@Gd2O3NCs at (150 pulse), (d) h-BN@Gd2O3 NCs at (338 pulse), and (e) h-BN@Gd2O3NCs at (772 pulse).
The HRTEM and particle size of (a,b) h-BNNs, (c,d) c-Gd2O3Ns, (e,f) h-BN@Gd2O3NCs at (150 pulse), (g,h) h-BN@Gd2O3 NCs at (338 pulse), and (i,j) h-BN@Gd2O3NCs at (772 pulse).
The HRTEM was used to capture images of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs, which were synthesized using different numbers of laser pulses, resulting in a variety of morphologies. The TEM analysis findings were consistent with those obtained from the FESEM images. Specifically, Fig. 4a shows well-dispersed and uniform h-BNNs with both spherical and nanosheet shapes36. These NPs' average particle size was found to be 30 nm. On the other hand, Fig. 4b reveals the presence of diverse Gd2O3 nanostructures, including needle-like and sheet-like structures. These NPs' average particle size indicated that these Gd2O3Ns had varying lengths ranging from 40 to 140 nm and diameters ranging from 5 to 30 nm. It is interesting that the number of laser pulses had a considerable impact on the size and morphology of the synthesized h-BN@Gd2O3 NCs, as observed in Fig. 4c–e. As the number of laser pulses increased, the average crystallite size of the Ns decreased. The core–shell structure of the prepared h-BN and c-Gd2O3 NPs was confirmed by the TEM images. In this structure, the dark points represent the h-BNNs (core) surrounded by the light points, which represent the Gd2O3Ns (shell).
The h-BN@Gd2O3 NCs, synthesized with 338 pulses, underwent EDS analysis to determine their chemical composition. Figure 5 (left lane) presents the EDS spectra of the h-BN@Gd2O3 NCs deposited on a glass substrate along with the corresponding weight percentages of elements. The analysis revealed the presence of boron (B), nitrogen (N), gadolinium (Gd), oxygen (O), and silicon (Si) elements in the h-BN@Gd2O3 NCs. The O elements can be attributed to interactions with the atmosphere, Gd2O3 target, and DDW. As a result, the prepared NCs are obviously devoid of additional contaminants. Due to the poor electron scattering by light components, this method is not suited for directly measuring the presence of hydrogen (H) in the Nanocomposite. Nevertheless, micro-Raman, FTIR, and XRD analyses can be used to infer the existence of the H element. The findings of the EDS mapping and spectrum show that the h-BN@Gd2O3 NCs (core–shell) successfully formed and that the distribution of the elements in the sample was uniform. In the right lane of Fig. 5a, the SEM image of the sample is shown, while Fig. 5b–f correspond to the formation of silicon (from the glass substrate), boron, nitrogen, gadolinium, and oxygen nanoparticles in the sample, respectively.
EDS spectrum and analyzed weight % of B, N, O, Si, and Gd (inset) for the h-BN@Gd2O3 NCs at (338 pulses). (a) FE-SEM image of h-BN@Gd2O3 NCs at (338 pulses), and corresponding EDS elemental mapping for (b) Si, (c) B, (d) N, (e) Gd, and (f) O.
Figure 6 shows the XRD pattern for all samples that were synthesized using the hybrid approach. For determining the physical structure of nanoparticles, XRD is a valuable technique. We can see that the diffraction peaks of the h-BNNs were found at 2 = 26.225°, 41.525°, 42.125°, and 55.225°, and these peaks corresponded to the Miller indices (002), (100), (101), and (004), respectively. The creation of h-BN is indicated by the strongest diffraction pattern between 25 and 30°, which is compatible with JCPDS 34-0421 and JCPDF 45-089334,36. The diffraction peaks of Gd2O3Ns were observed at 2θ = 11.525°, 17.025°, 20.875°, 23.225°, 28.475°, 31.275°, and 35.225°, corresponding to (100), (211), (101), (222), (123), and (411) planes, respectively, according to JCPDS 03-065-3181, JCPDS 88-2165, and JCPDS 12-0797, which indicates cubic phase crystallites of Gd2O337,38,39. Using Debye–Scherrer Eq. (3), the average crystal size was calculated.
where is Bragg's diffraction angle, is the angular peak width at half maximum (in rad), and is the X-ray wavelength (= 1.54060). The average crystallite sizes for h-BNNs, c-Gd2O3Ns, h-BN@Gd2O3 (150 pulses), h-BN@Gd2O3 (338 pulses), and h-BN@Gd2O3 (772 pulses) were determined to be 7.04 nm, 0.68 nm, 2.59 nm, 3.75 nm, and 4.88 nm, respectively. Table 1 provides the calculated crystallite size for each sample. These findings corroborate the FESEM results, indicating the successful formation of nanometer-sized particles. These results are in full agreement with previously reported data conducted by other researchers29,34, 37, 39. When compared to the XRD patterns of h-BNNs and c-Gd2O3, the diffraction patterns of h-BN@Gd2O3 produced at different laser pulse levels correspond to both the h-BNNs peak and the c-Gd2O3Ns peak. This confirmation supports the creation of a hybridized material (core/shell) without any chemical interaction between them. A slight increase in the intensity of the diffraction peaks has been observed, but there has not been a significant broadening of the peak. This is because more laser pulses lead to a higher quantity of NCs in the colloidal solution40,41,42. This observation implies an enhancement in crystallinity due to doping. The data indicate that both BN and Gd2O3 influenced the crystallite sizes of the NCs.
XRD pattern of the prepared sample, h-BN Ns, c-Gd2O3 Ns, and h-BN@Gd2O3 NCs with different laser pulses.
The insights garnered from HRTEM and SAED analyses provide a pivotal understanding of the structural attributes of various materials, including h-BNs, c-Gd2O3 Ns, and h-BN@Gd2O3NCs, as illustrated in Fig. 7. In Fig. 7A, the presence of a 3.2 Å d-spacing and the alignment with hkl (002) planes affirm crystallinity, validating the successful synthesis of the hexagonal phase with anticipated interplanar distances. SAED patterns further verify crystallographic orientation and atomic arrangement. The congruence among d-spacing, hkl planes, and SAED reinforces the high-quality synthesis of h-BN through laser exfoliation and fragmentation in deionized water (DDW). Both c-Gd2O3Ns and h-BN@Gd2O3 NC samples exhibit robust crystallinity, evident from well-defined lattice fringes across a significant proportion of particles (Fig. 7B, C). HRTEM images vividly capture regular lattice fringes, reflecting consistent atom spacing, while SAED patterns present concentric rings, indicating a polycrystalline nature of the sample. The d-spacing values deduced from HRTEM and SAED analyses were cross-referenced with those derived from XRD data, resulting in alignment and confirming the cubic crystal structure for c-Gd2O3Ns (hkl (100), (211), (222), (123), and (411)) and for h-BN@Gd2O3 NCs (hkl (100), (211), (002), (411), (123), (100), (004), (444), (110), and (411)). These findings collectively endorse the credibility of HRTEM and SAED methodologies in characterizing nanoscale crystal structures. Notably, these results harmonize seamlessly with the XRD findings discussed earlier, solidifying their reliability. These revelations hold promise for potential applications spanning electronics, optoelectronics, and nanocomposites.
HR-TEM micrographs “interplanar lattice spacing” and SAED patterns for sample synthesized (A) h-BNNs, (B) c-Gd2O3Ns, and (C) h-BN@Gd2O3 NC (338 pulses). The TEM results are in good agreement with the XRD results.
Using DLS, it was possible to ascertain the hydrodynamic diameter of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs (338 pulses) in DDW medium, which provides information about their particle size (Fig. 8). The hydrodynamic size of h-BNNs was measured at 981 nm with a polydispersity of 0.332 (Fig. 8A). For c-Gd2O3 Ns, the hydrodynamic size was 432 nm with a polydispersity of 0.240 (Fig. 8B). As for h-BN@Gd2O3 NCs (338 pulses), the hydrodynamic size was recorded as 573.64 nm with a polydispersity of 0.241 (Fig. 8C). It's crucial to remember that the DLS particle size was discovered to be greater than the results from XRD and TEM, as it represents the hydrodynamic size. Furthermore, the results indicate that h-BNNs exhibited higher dispersibility in DDW compared to Gd2O3 Ns, as evidenced by their respective hydrodynamic sizes. The value of the zeta potential (ζ) provides important details regarding the potential stability of the colloidal system. Charged particles are repelled by an increase in zeta potential, which prevents them from aggregating in the suspension. A ζ value of at least 30 mV is often displayed by stable systems41. When a ζ nanoparticle's value is between −10 and + 10 mV, it is said to be virtually neutral, however when it ζ exceeds + 30 mV or drops below −30 mV, it is classified as strongly cationic or strongly anionic. In our study, we measured ζ of three samples: h-BNNs (− 15.20 mV, mobility (μ/s)/(V/cm): −1.19, as shown in Fig. 9A), c-Gd2O3Ns (−7.17 mV, mobility (μ/s)/(V/cm): −0.56, as shown in Fig. 9B). This negative charge may play an important role. h-BN@Gd2O3 NCs (338 pulses) (13.53 mV, Mobility (μ/s)/(V/cm): 1.06, indicating incipient instability, as shown in Fig. 9C. The zeta values and the results show that the h-BNNs sample has a high modulus value of ζ = −15.20 mV. This is explained by the fact that the laser exfoliation and fragmentation process leaves hydroxyl groups (OH) on the surface of the BNNs, which improves the suspension's stability43. Understanding the zeta potential is important as it helps to comprehend the in vivo destination of materials as it relates to cellular processes like aggregation, adhesion, and activation. This evaluation of stability in the synthesized materials is essential when they are dispersed in DDW. However, it is important to note that other factors such as particle size, surface charge density, and the presence of stabilizing agents also play significant roles in determining the overall stability of nanoparticles44.
DLS measurement to determine the size distribution used in stability tests of (A) h-BN, (B) c-Gd2O3, and (C) h-BN@Gd2O3 NCs (338 pulses).
Zeta potential distribution curves were used in stability tests of (A) h-BN, (B) c-Gd2O3, and (C) h-BN@Gd2O3 NCs (338 pulses).
The FTIR measurements provide more evidence that the final product is a combination of h-BN and c-Gd2O3 Ns. Figure 10 illustrates the results of FTIR studies to examine the chemical compositions and bonding properties of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs. The three samples' spectra have the same characteristics, including a strong absorption peak at 1631 cm−1 and a wide absorption band spanning 3000 cm−1 to 3700 cm−145. Both of these absorptions were linked to the O–H vibration modes of bending and stretching, respectively. However, it was found that the three materials' IR absorption varied noticeably between 400 and 550 cm−1 (Fig. 10 inset). The Black spectrum reveals characteristic peaks at 416 cm−1, 455 cm−1, 490 cm−1, and 520 cm−1, attributed to the bending vibration of B–N and B–N–O, which are indicative of h-BNNs34. The red spectrum displays characteristic peaks at 404, 428, 447, 514, and 524 cm−1, attributed to the bending vibration of Gd-O and Gd-OH, characteristic of c-Gd2O3Ns38,46. Lastly, the blue spectrum exhibits characteristic peaks at 412 cm−1, 435 cm−1, 455 cm−1, 474 cm−1, 513 cm−1, and 520 cm−1, ascribed to the bending vibration of the triangular B–N–Gd, B–N–O, and Gd–O, which suggests the existence of h-BN@Gd2O3 NCs. The strength of other bands found in the FTIR spectrum is noticeably lower. The resulting product is a combination of h-BN and c-Gd2O3 Ns, as further evidenced by the FTIR data. The shifts in FTIR absorption bands in h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs result from various factors, including the effect of the size. Smaller nanoparticles exhibit blue shifts in their FTIR bands due to quantum size effects. Additionally, differences in surface chemistry, confinement effects, aggregation, crystal structure, and chemical reactions contribute to band shifts. The surface chemistry of nanoparticles, their crystal structure variations, and chemical reactions with DDW can influence FTIR spectra.
FTIR spectra of the prepared samples, h-BN Ns, c-Gd2O3 Ns, and h-BN@Gd2O3 NCs.
Raman spectra, the professional technique for material analysis, were utilized in this study to investigate various characteristics such as crystallographic phase, impurities, and structural defects. The Raman analyses employed a laser wavelength of (632.8 nm), and the obtained spectra ranged from 0 to 2000 cm−1 (Fig. 11). A comparison was made between the Raman spectra of h-BN@Gd2O3 prepared using different laser pulses, h-BNNs, and c-Gd2O3Ns prepared by the same technique. The Raman spectrum of the BNNs material exhibited two distinct bands at 1372, 1426, and a small peak in reign < 808 cm−1, corresponding to h-BN. The peak at < 808 cm−1 was attributed to the B1g phonon mode (which corresponds to the breathing mode of boron and nitrogen atoms in the hexagonal BN lattice). The peak at 1372 cm−1 was attributed to the E2g phonon mode (it corresponds to the in-plane vibration of boron and nitrogen atoms in a hexagonal lattice), similar to the G peak observed in graphene. The peak at 1426 cm−1 was attributed to the A1g phonon mode (it is related to the out-of-plane vibrations of boron and nitrogen atoms in a hexagonal BN structure)35,47, 48. In contrast, the Raman spectra of Gd2O3 revealed five prominent peaks at approximately 210, 304, 360, 483, 681, and 722 cm–1, which corresponded to F2g (This mode is associated with oxygen vibrations in the lattice), Ag translatory (It is attributed to stretching vibrations of oxygen atoms), Fg + Ag, and E1g liberation modes49,50, showing the existence of c-Gd2O3Ns for the doped sample's h-BN phase, c-Gd2O3 at the location of nine significant Raman peaks is seen at 210 cm−1, 242 cm−1, 304 cm−1, 360 cm−1, 483 cm−1, 681 cm−1, 722 cm−1, 1372 cm−1, and 1426 cm−1. These findings suggest that the nanostructured h-BN@Gd2O3 samples consist of a mixture of h-BN and c-Gd2O3 nanostructures.
Raman spectrum of the prepared sample, h-BN Ns, c-Gd2O3 Ns, and h-BN@Gd2O3 NCs.
The wave numbers of the corresponding Raman peaks for the hexagonal47 and cubic51 phases of doped and undoped h-BN and c-Gd2O3 are listed in Table 2. Notably, the intensity of the Raman bands in the spectra increased with the number of pulses, indicating a correlation between the concentration of the studied molecules and the intensity of the Raman spectral bands. The observed Raman bands align with those reported by other researchers48,52,53,54,55. Additionally, this study represents the first Raman analysis conducted on the h-BN@Gd2O3 cubic phase. Furthermore, the Raman spectra of h-BN exhibited two broad bands around 1600 cm−1, associated with O2 and H–O–H bending modes, while Gd2O3's Raman spectra showed a wide band at 1000 cm−1, corresponding to the H–O–H bending mode, both originating from the liquid environment. The shift of Raman modes can occur due to various factors, including the presence of oxygen vacancies, defects induced by disorder, or the effects of phonon confinement56.
Figure 12A illustrates the UV–vis intensity of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs, synthesized using a laser energy of 10 mJ with varying numbers of laser pulses (150, 338, and 772). The recorded spectra show a progressive enhancement in absorption intensity between 200 and 250 nm as the number of laser pulses increases.57,58 This trend is likely attributed to all samples' heightened concentration and reduced size of nanoparticles. The UV spectra of h-BNNs and NCs samples reveal an absorption peak below 380 nm, due to fine structural vibrations and band-to-band electron transitions (as depicted in Fig. 12A). Moreover, a smooth decline is observed at longer wavelengths. The higher energy of laser pulses causes target evaporation, melting, and phase transformation at elevated temperatures and pressures, accompanied by an extended irradiation time. Several parameters, including stoichiometry, morphologies, and size distribution, influence the absorption behavior of the NCs59. Importantly, the absorption curves below 380 nm exhibit an increase, indicating a hypsochromic shift (blue shift) in the absorption values with an increasing number of laser pulses. The quantum confinement effect can be credited with this change. Oxygen deficiency and lattice strain resulting from the ablation of Gd2O323,60,61,62.
(A) UV–VIS spectrums, and (B) band gap of the prepared samples, h-BN Ns, c-Gd2O3 Ns, and h-BN@Gd2O3 NCs with different laser pulses (150, 338, and 772).
Figure 12B illustrates the optical band gap of the samples, offering a window for the PL spectrum of the nanoparticles (NPs). The impact of nanocrystal size on the electronic structure of semiconducting NPs is highlighted by the rise in band gap energy coupled with the decrease in particle size. This phenomenon is widely recognized as the quantum confinement effect, and its assessment was conducted using the Tauc method. The Tauc method postulates that the energy-dependent absorption coefficient α can be expressed by Eq. (4)63,64:
Here, the symbol h represents the Planck constant, v indicates the frequency of the photon, Eg represents the band gap energy, and β is a constant. The γ factor varies based on the nature of the electron transition and takes values of 1/2 or 2 for direct and indirect transition band gaps, respectively60. Band gap energies of 5.6, 5.7, 5.6, 4.9, and 5.5 eV were recorded for different materials, including h-BN Ns, c-Gd2O3Ns, and three unique h-BN@Gd2O3 NC samples produced using varying laser pulse numbers (150, 338, and 772). The decrease in band gap energy in the doped samples confirms the effective incorporation of c-Gd2O3Ns into the h-BN structure, highlighting their potential in materials science applications.
Figure 13A–C shows the spectrum using a 532 nm excitation wavelength and deconvolution peaks of PL emission for three different samples: h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs (338 pulses) in DDW. The deconvolution process utilized multi-Gaussian functions to obtain these contributions. In Fig. 13, the PL spectra underwent deconvolution, specifically focusing on the PL peaks, using Origin Lab software, while the other components were fitted with a Gaussian line shape. Following the deconvolution, we assigned labels to the peaks based on their wavelength and color-coded each peak according to its emission band for each sample. Our findings indicate that the PL spectra of h-BNNs exhibit four distinguishable spectral features in the blue range (~ 300 to 550 nm): Violet (370 nm, 3.35 eV), Indigo (422 nm, 2.9 eV), Blue (470 nm, 2.64 eV), and Cyan (500 nm, 2.48 eV) emission. For c-Gd2O3Ns, three distinguishable spectral features were observed in the UV-blue-green range (~ 300 to 500 nm): Violet (369 nm, 3.36 eV), Blue (460 nm, 2.7 eV), and Green (532 nm, 2.3 eV) emission. However, for h-BN@Gd2O3NCs (338 pulses), three spectral features were detected in the UV-blue-green range (~ 300 to 550 nm): Violet (368 nm, 3.36 eV), Blue (470 nm, 2.64 eV), and Green (535 nm, 2.3 eV) emission. Figure 13C represents the ultraviolet, blue, and green regions, the green emission peak corresponds to the single ionized oxygen vacancy65. It is evident from Fig. 13A that the Green bands are absent in the spectrum of h-BNNs, suggesting their origin from the c-Gd2O3 Ns. The Blue band can be attributed to traces of h-BNNs emission originating from the NCs matrix. We observe that the intensities and spectral positions of the bands change with variations in the concentration of NPs, resulting in an increase in the PL of h-BN@Gd2O3 NCs29. The fitting analysis of Fig. 13C reveals that as the concentrations of h-BNNs and c-Gd2O3Ns increase, the intensity of the UV, Blue, and Green bands also increases. Therefore, the fitting results demonstrate that the PL spectra can be described by four PL components, which exhibit different trends with changes in NPs. The above results indicate the successful synthesis of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs, all of which exhibit stable and strong fluorescence in water. The introduction of Gd2O3 to BN nanoparticles can elicit various effects on PL spectra. These effects depend on factors such as the concentration and specific properties of the Gd2O3 and BN NPs. One notable effect is the PL intensity enhancement, where Gd2O3 nanoparticles, under certain conditions, act as sensitizers, boosting the PL intensity of BN nanoparticles. This phenomenon is often observed in rare-earth-doped materials, where Gd2O3 transfers energy to BN, resulting in heightened luminescence (Fig. 13C). Another effect is the emission wavelength shift, where the inclusion of Gd2O3 induces a shift in the emission wavelength of BN nanoparticles. This shift can manifest as a movement toward longer or shorter wavelengths, contingent on the specific interactions between these materials. The doping-related bands have a significant effect, as Gd2O3 introduction can result in new PL bands associated with gadolinium emissions. These bands may intersect or interact with the PL bands of BN, causing changes in the PL spectrum. Gd2O3's capacity for energy transfer is also noteworthy, influencing the excitation and relaxation dynamics of BN nanoparticles. This can lead to alterations in PL kinetics and spectral characteristics. Surface effects are yet another factor to consider, as the characteristics of the surface and interactions at the Gd2O3-BN interface can influence PL spectra. Surface states or introduced energy levels due to the presence of the Gd2O3 layer can affect PL characteristics. The specific effects observed depend on variables like Gd2O3 concentration, nanoparticle size, structure, and synthesis conditions. Understanding these effects is crucial when exploring the potential applications of Gd2O3-enhanced BN nanoparticles in various fields, from optoelectronics to biomedicine.
Deconvolution of fluorescence spectrum for the samples: (A) h-BNNs, (B) c-Gd2O3Ns, and (C) h-BN@Gd2O3NCs (338 pulses).
The well diffusion method has been used to investigate the antibacterial activity of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs (338 pulses) against S. aureus and S. mutans and E. coli and P. mirabilis. The inhibition zones of the prepared colloidal Ns are listed in the graphical representation of all measured zones of inhibition after 24 h of incubation period at 37C˚. The results show that the prepared nanostructures were more effective in the growth of Gram-ve bacteria than Gram + ve bacteria. For h-BNNs, the highest activity was recorded against P. mirabilis with the inhibition zone reaching 16.3 mm, followed by E. coli which exhibited the highest diameter of inhibition zone that reached 15.8 mm after treatment with h-BN@Gd2O3 NCs, and the lowest diameter of the inhibition zone was 15.4 mm after treatment with c-Gd2O3Ns. For Gram + ve bacteria, the highest effect for h-BNNs and h-BN@Gd2O3 NCs) was in S. mutans with an inhibition zone diameter reached 16.7 and 16.2 mm, and the lowest inhibition zone diameter was 13.6 mm for the c-Gd2O3Ns. The inhibition zone of S. aureus was 15.2 mm for h-BNNs, followed by (c-Gd2O3Ns) in diameter reached 15 mm, and the lowest inhibition zone diameter was 13 mm for h-BN@Gd2O3 NCs (Fig. 14).
Antibacterial activity of negative control (DDW), h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs. Zone of inhibition and graphical representation of (A) E. coli, (B) P. mirabilis, (C) S. mutans, and (D) S. aureus. *p ≤ 0.05, ** p ≤ 0.01, *** p ≤ 0.001.
Table 3 presents a comparison between our synthesized nanocomposite and previously reported antibacterial nanomaterials. The results in Table 3 indicate that our prepared h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs nanocomposite were more potent than recorded previously. Therefore, it can be concluded that h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs have the potential to serve as next-generation antibacterial agents for a range of biomedical applications.
The antibacterial efficacy of the synthesized Ns can be attributed to their interaction with cell wall constituents, causing structural changes potentially affecting cell membranes. These findings stem from the close contact between the c-Gd2O3Ns (shell) and the h-BNNs (core), facilitating direct engagement with the membrane and ultimately leading to the rupture of contracted bacteria. The escalating integration of nanostructures in medicine has sparked numerous investigations into their potential antibacterial mechanisms. Metal nitride and oxides, for instance, can modulate bacterial metabolic activity, offering a promising strategy for disease treatment. The effective antibacterial action of nanostructures hinges on their direct interaction with bacterial cells. This interaction is achieved through mechanisms such as electrostatic attraction71, the forces of van der Waals72, the interactions between receptors and ligands73, and hydrophobic bonds74. Subsequently, nanoparticles (NPs) traverse bacterial membranes and accumulate along metabolic pathways, influencing cellular membrane structure and function. NPs also engage with fundamental components of bacterial cells, including DNA, where they induce disruptions through various means, including endogenous and exogenous damage, lysosomes, ribosomes, and enzymes, among others75. This interaction causes oxidative stress, as endogenous sources trigger the formation of ROS during normal cellular metabolism76. These highly unstable free radicals can instantaneously react with other substances. The interaction of free radicals with DNA initiates a cascade of events resulting in genotoxic lesions. This process initiates diverse changes, including heterogeneous alterations, shifts in cell membrane permeability, and disruptions in electrolyte balance, enzyme inhibition, protein deactivation, and modifications in gene expression77,78,79,80. Notably, contemporary research has proposed several prevalent mechanisms, which include oxidative stress81, the release of metal ions82, and non-oxidative pathways83. The various mechanisms through which nanoparticles combat bacteria are explained in Fig. 15.
The mechanism of antibacterial activity of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs.
The cellular toxicity of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs was performed to evaluate the viability of MCF-7, MCF-10, and HT-29 cell lines using the MTT assay. Different concentrations (1, 5, 10, 15, 25, 50, and 75 µg/mL) of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs were used and incubated for 24 h. As the concentration of nanomaterials increases, the violet color of the MTT assay becomes progressively lighter. This color change indicates a decrease in the number of viable cells. The efficacy of nanomaterials against biological systems and cells holds considerable importance for fulfilling biomaterial criteria, rendering them suitable for medical applications. The outcomes of the MTT assay are illustrated in Fig. 16A–C.
Cytotoxicity effects of (h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs) treated with (A) HT-29, (B) MCF-7, and (C) MCF-10 cell lines. The data were collected over a 24-h treatment, and the values reflect the mean standard deviation of three experiments.
The findings illustrated that treatment with h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs inhibited the growth of cells significantly (P < 0.05) as compared to those of control cultures, and the reduction was concentration-dependent. The highest inhibition was found in the HT-29 cells, followed by MCF-7 cells, with less cytotoxicity against MCF-10. For HT-29, the inhibitory concentration value (IC50) was 12 µg mL−1, 10 µg mL−1, and 15 µg mL−1, respectively. While IC50 for MCF-7 cells reveals 14 µg mL−1, 15 µg mL−1, and 28 µg mL−1, respectively. The Ns used in this investigation had particles that were 30 nm in size. The outcomes from XRD and the results of PL analysis showed that there are multiple interstitial oxygen vacancies (Oi) at 532 nm linked to the sample's oxygen vacancies (Ov). These alterations are attributed to the substantial quantity of ROS generated across the three samples. These defects allow a greater number of electron–hole pairs to travel toward the nanomaterial matrix's surface within the specimens. Additionally, the samples' aqueous environment (DDW) contains singlet oxygen (1O2), hydroxyl radicals (OH), and superoxide anions (O2), which the electrons and holes interact with and may cause to produce ROS. These free radicals can trigger oxidation and reduction reactions in macromolecules, including proteins, lipids, and nucleic acids, which leads to oxidative stress when they come into contact with the cellular environment. As a result, a state of disequilibrium develops inside the cells as a result of the buildup of ROS, outpacing the biological system's ability to quickly remove these reactive radicals or repair the harm done by tumor cells84,85,86.
In the context of h-BNNs and c-Gd2O3Ns, MTT testing has been conducted to assess their cytotoxicity in MCF-10 cells. The results indicate that both h-BNNs and c-Gd2O3Ns demonstrate minimal cytotoxicity and are deemed compatible with MCF-10 cells, aligning with previously published studies87,88,89,90,91. However, uncertainties persist regarding the toxicity of h-BNNs and c-Gd2O3Ns, and their full biocompatibility remains unproven4,92. These findings suggest the potential utility of these materials in biomedical applications requiring interaction with living tissues. Nevertheless, further research is imperative to comprehensively comprehend their behavior in various biological systems and ensure their safety for medical applications.
Previous studies revealed that the cell viability of cancer and normal cells after treatment with boron nitride decreased as a function of concentration and time. Cancer cell lines MCF-7 and Hela showed 45% and 60% cytotoxicity, respectively at a concentration of 2 mg/mL for 24 h treatment, which further increased up to 60% and 70%, respectively in 48 h treatment. Whereas in normal cell line (HEK-293) 30% cytotoxicity was observed at a higher concentration (2 mg mL−1) and 24 h of treatment, which increased up to 50% after 48 h. It is evident that the cytotoxicity of BN nanostructures is higher in cancer cells as compared with normal cell lines93.
Cytotoxicity associated with h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs involves apoptotic changes and nuclear condensation. To identify and quantify the induction of apoptosis and the formation of necrosis in HT-29 and MCF-7 cells following exposure to h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs, fluorescent AO/EB DNA-binding dyes were utilized. The AO dye was absorbed by viable cells, as indicated by green fluorescence, while the EB dye exclusively interacted with deceased cells, resulting in red fluorescence. Within viable cells (non-treated cells), distinct bright uniform normal green nuclei with an organized structure. While treated cells were significantly enhanced and distinguished according to the fluorescence emission the apoptotic cells have yellow nuclei. (depicted in Fig. 17A–D. The anticancer activity ascribed to BN, Gd, and Ov in h-BN, c-Gd2O3, and h-BN@Gd2O3 NCs, corresponds with increased ROS production. MTT assays performed on HT-29 and MCF-7 cells revealed the potential anticancer effects of h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs. Moreover, the demise of cancer cells induced by nanoparticles occurred through apoptosis, as visualized by AO/EtBr staining.
MCF-7 cells and HT-29 cells with dual-dye AO/EB staining. (A) Non-treated cells (Control) and cells treated with IC50 of (B) h-BNNs, (C) c-Gd2O3Ns, and (D) h-BN@Gd2O3 NCs.
One proposed mechanism of the anticancer activity of these nanoparticles can be attributed to the ability of NPs to produce ROS, which can cause changes in biomacromolecules, such as proteins, nucleic acids, and lipids in response to the effects of the generated oxidative stress in the cells and tissues. ROS produce free radicals that are short-lived and unstable, which influence the nuclear viability and healthiness conditions of the affected organisms, and finally lead to cell death. ROS also causes oxidation of proteins and peroxidation of lipids that leads to damaging the fluidity of the cell membrane, thereby changing the permeability of fluids and ion transports across it, and causing inhibition of metabolic processes31,32.
Finally, h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3NCs emerge as highly promising materials for cancer therapy due to their notable attributes, including strong chemical stability, uniformity, and excellent dispersibility in solution. Unique structural features, such as the spherical nanosheets of BN and the needle-like surface of c-Gd2O3Ns, position h-BNNs and c-Gd2O3 as ideal nanocarriers for targeted delivery of anticancer drugs, potentially enhancing their penetration into endosomes. Future research efforts can be directed towards further functionalizing h-BNNs to enhance their biological performance, similar to BNNTs.
Previous study has elucidated diverse responses of cancer cell lines to treatments involving boron nitride (BN) and gadolinium oxide (Gd2O3). BN has demonstrated effectiveness against neoplastically transformed IAR-6-1 cells87, breast cancer cells (4T1)89, prostate cancer cells (DU145 and PC3)94, as well as BV2 mouse glioma cells, GMI-R1 rat microglial cells, and human cervical carcinoma cells (HeLa), although its efficacy in other cancer types remains relatively unexplored95. The cytotoxicity of h-BNNDs against HUVEC cells (human umbilical vein endothelial cells) was also investigated by Mao et al.96. They found that the assessment of cell viability combined with cell counting, viability/cytotoxicity assays, and cell apoptosis detection demonstrated that BNNDs could not elicit significant acute cytotoxicity. They proved that the cell viability remained higher than 80% even at high concentrations and long incubation (200 μg mL−1, 48 h).
On the other hand, Gd2O3 nanoparticles have exhibited promise in treating M109 (malignant tumors of the mouse pulmonary system), 4T1 (epithelial breast carcinoma) cell lines88, mouse colon adenocarcinoma CT26 cell line97, HeLa, and COC1/DDP cells in the context of ovarian cancers98. Previous results on the viability of the Ba/F3 cells (a murine interleukin-3 dependent pro-B cell line) and THP-1 cells (human monocytic cell line) showed that the cells were viable after incubation with Gd2O3 nanoparticles and remained intact at the time of MRI measurement99.
The in vitro cytotoxicity test on normal (HaCaT) and cancerous (HeLa) cells reveals that the CNT/Gd2O3 hybrid nanostructure is bio-compatible in comparison to the pure CNTs99.
However, this study underscores the potential of BN, Gd2O3, and their combination in cancer treatment. Nevertheless, further research is imperative to elucidate the underlying mechanisms and optimize their therapeutic applications across wide spectrum of cancer cell lines. However, toxicology investigations using in vivo studies of prepared nanoparticles need more thorough viability studies, and long-term biological effects need to be evaluated.
Additionally, an assessment of the hemolytic effect using an ex vivo incubation with erythrocytes revealed that hexagonal boron nitride (h-BN) nanosheets, cubic gadolinium oxide (c-Gd2O3) nanoparticles, and h-BN@Gd2O3 nanocomposites demonstrated minimal hemolysis rates, registering at less than 5%, even when exposed to concentrations up to 100 μg mL−1 (Fig. 18). The data is consistent with a previous study that demonstrated Gd2O3@PCD-FA showed no cytotoxic effect on MCF10A cells (normal human breast cells) and exhibited acceptable hemocompatibility against human RBCs, revealing their biocompatible properties100. Another study also revealed that BN has no significant hemolysis rate on human RBCs even when the concentration reached 100 μg mL−190. The hemolysis assay serves as a preliminary analytical approach for ascertaining the compatibility of nanoparticles (NPs) with blood and for assessing their effects on erythrocyte well-being. These observations underscore the potential of h-BN@Gd2O3 as a viable candidate for drug delivery and demonstrate its good cytocompatibility for biomedical applications.
Hemolysis evaluation of erythrocytes subjected to incubation with deionized water, PBS, h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs, with accompanying histogram data.
In summary, a novel, cost-effective hybrid method was utilized to synthesize new nanomaterials, namely h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs. The LEFL process involved the use of Nd: YAG lasers with varying wavelengths (1064 and 532 nm) and pulse numbers (150, 338, and 772). The resulting h-BNNs displayed small particles with irregular spherical shapes and nanosheets, while Gd2O3Ns exhibited nanofiber-like, needle-like, and sheet-like structures (leaf-like). TEM analysis corroborated the findings from FESEM images. Phase analysis unveiled hexagonal and cubic structures, with average crystallite sizes of 7.04 nm for h-BNNs, 0.68 nm for c-Gd2O3Ns, and 3.75 nm for h-BN@Gd2O3 NCs. These findings collectively endorse the credibility of HRTEM and SAED methodologies in characterizing nanoscale crystal structures. Notably, these results harmonize seamlessly with the XRD findings discussed earlier, solidifying their reliability. Raman spectroscopy and FTIR spectroscopy provide complementary insights into the structure and composition of materials. Raman spectroscopy detects homo-nuclear molecular bonds and reveals details about both intra- and intermolecular vibrations. On the other hand, FTIR spectroscopy is attuned to hetero-nuclear functional group vibrations and polar bonds, thereby enhancing the understanding of material properties. All samples showed absorption band edge values between 200 and 250 nm. The PL spectrum highlighted the presence of numerous Ov that brought on cell death and the creation of ROS. The samples exhibited higher antibacterial activity against both bacterial strains. Furthermore, all three samples demonstrated substantial anticancer effects against HT-29 and MCF-7 cells. Moving forward, we anticipate that h-BNNs, c-Gd2O3Ns, and h-BN@Gd2O3 NCs could potentially serve as promising anticancer agents and biocompatible, with further in vivo experiments worthy of exploring their antitumor effect.
All data are included in this published article.
Farokhzad, O. C. & Langer, R. Impact of nanotechnology on drug delivery. ACS Nano 3(1), 16–20 (2009).
Article CAS PubMed Google Scholar
McNeil, S.E. Unique benefits of nanotechnology to drug delivery and diagnostics. In Characterization of Nanoparticles Intended for Drug Delivery (ed. Mc Neil, S.E.) 3–8 (Springer, 2011).
Kulshrestha, S. & Khan, A. U. Nanomedicine for anticancer and antimicrobial treatment: An overview. IET Nanobiotechnol. 12(8), 1009–1017 (2018).
Article PubMed PubMed Central Google Scholar
Kakarla, A. B. & Kong, I. In vitro and in vivo cytotoxicity of boron nitride nanotubes: A systematic review. Nanomaterials 12(12), 2069 (2022).
Article CAS PubMed PubMed Central Google Scholar
Parveen, S., Ranjita, M. & Sahoo, S. K. Nanoparticles: A boon to drug delivery. Therapeutics, diagnostics and imaging. Nanomedicine 8(2), 147–166 (2012).
Article CAS PubMed Google Scholar
Elderdery, A. Y. et al. Structural, optical, antibacterial, and anticancer properties of cerium oxide nanoparticles prepared by green synthesis using Morinda citrifolia leaves extract. Bioinorgan. Chem. Appl. 28, 6835 (2022).
Jeronsia, J. E., Raj, D. V., Joseph, L. A., Rubini, K. & Das, S. J. In vitro antibacterial and anticancer activity of copper oxide nanostructures in human breast cancer Michigan Cancer Foundation-7 cells. J. Med. Sci. 36(4), 145–151 (2016).
Abd Elkodous, M. et al. Recent advances in waste-recycled nanomaterials for biomedical applications: Waste-to-wealth. Nanotechnol. Rev. 10(1), 1662–1739 (2021).
Ortega-Berlanga, B. et al. An overview of gadolinium-based oxide and oxysulfide particles: Synthesis, properties, and biomedical applications. Crystals 11(9), 1094 (2021).
Dědková, K. et al. Daylight induced antibacterial activity of gadolinium oxide, samarium oxide and erbium oxide nanoparticles and their aquatic toxicity. Mater. Chem. Phys. 197, 226–235 (2017).
Pan, Y. et al. Antibiotic-like activity of atomic layer boron nitride for combating resistant bacteria. ACS Nano 16(5), 7674–7688 (2022).
Article CAS PubMed Google Scholar
Pandey, S. K., Singh, S. & Mehta, S. K. Biocompatible gadolinium oxide nanoparticles as efficient agent against pathogenic bacteria. J. Colloid Interface Sci. 529, 496–504 (2018).
Article ADS PubMed Google Scholar
Shaybanizadeh, S. & Chermahini, A. N. Fabricating boron nitride nanosheets from hexagonal BN in water solution by a combined sonication and thermal-assisted hydrolysis method. Ceram. Int. 47(8), 11122–11128 (2021).
Emanet, M., Sen, Ö., Taşkin, I. Ç. & Çulha, M. Synthesis, functionalization, and bibio applicationsf two-dimensional boron nitride nanomaterials. Front. Bioeng. Biotechnol. 7, 363 (2019).
Article PubMed PubMed Central Google Scholar
Baig, N., Kammakakam, I. & Falath, W. Nanomaterials: A review of synthesis methods, properties, recent progress, and challenges. Mater. Adv. 2(6), 1821–1871 (2021).
Sidorowicz, A. et al. Nanoparticles from microalgae and their biomedical applications. Mar. Drugs 21(6), 352 (2023).
Article CAS PubMed PubMed Central Google Scholar
Maqbool, Q. et al. New waste-derived TiO2 nanoparticles as a potential photocatalytic additive for lime based indoor finishings. J. Clean. Prod. 373, 133853 (2022).
Mishra, M. et al. Microstructure and optical properties of Gd2O3 thin films prepared by pulsed laser deposition. Surf. Coat. Technol. 262, 56–63 (2015).
Klotzbücher, T., Pfleging, W., Mertin, M., Wesner, D. A. & Kreutz, E. W. Structure and chemical composition of BN thin films grown by pulsed-laser deposition (PLD). Appl. Surf. Sci. 86(1–4), 165–169 (1995).
Kayani, Z. N., Bashir, Z., Mohsin, M., Riaz, S. & Naseem, S. Sol-gel synthesized boron nitride (BN) thin films for antibacterial and magnetic applications. Optik 243, 167502 (2021).
Article ADS CAS Google Scholar
Sivasamy, R., Venugopal, P. & Mosquera, E. Synthesis of Gd2O3/CdO composite by sol-gel method: Structural, morphological, optical, electrochemical and magnetic studies. Vacuum 175, 109255 (2020).
Article ADS CAS Google Scholar
Yulizar, Y., Eprasatya, A., Apriandanu, D. O. B. & Yunarti, R. T. Facile synthesis of ZnO/GdCoO3 nanocomposites, characterization and their photocatalytic activity under visible light illumination. Vacuum 183, 109821 (2021).
Article ADS CAS Google Scholar
Halomoan, I., Yulizar, Y., Surya, R. M. & Apriandanu, D. O. B. Facile preparation of CuO-Gd2Ti2O7 using Acmella uliginosa leaf extract for photocatalytic degradation of malachite green. Mater. Res. Bull. 150, 111726 (2022).
Liu, G., Hong, G., Wang, J. & Dong, X. Hydrothermal synthesis of spherical and hollow Gd2O3: Eu3+ phosphors. J. Alloys Compd. 432(1–2), 200–204 (2007).
Hazarika, S., Paul, N. & Mohanta, D. Rapid hydrothermal route to synthesize cubic-phase gadolinium oxide nanorods. Bull. Mater. Sci. 37, 789–796 (2014).
Ismail, R. A., Mohsin, M. H., Ali, A. K., Hassoon, K. I. & Erten-Ela, S. Preparation and characterization of carbon nanotubes by pulsed laser ablation in water for optoelectronic application. Physica E Low-Dimens. Syst. Nanostruct. 119, 113997 (2020).
Mohsin, M. H., Khashan, K. S., Sulaiman, G. M. & Khalil, K. A. Effect of laser energies on the performance of exfoliation and fragmentation for hexagonal boron nitride by laser. J. Appl. Sci. Nanotechnol. 3(3), 13 (2023).
Khashan, K. S. & Mohsin, M. H. Characterization of carbon nitride nanoparticles prepared by laser ablation in liquid for optoelectronic application. Surf. Rev. Lett. 22(04), 1550055 (2015).
Article ADS CAS Google Scholar
Mohsin, M. H., Khashan, K. S. & Sulaiman, G. M. Optical and structural properties of H-BN@ Gd2O3 nanoflake prepared by laser-induced ablation in liquid. Phys. Scr. 98(5), 055903 (2023).
Avramova, I. et al. Novel approach for synthesis of graphene-like phases by pulsed laser ablation in a flow-mode suspension. Materials 15(22), 7870 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Alhujaily, M. et al. Au/ZnO Nanocomposites Prepared by Laser Ablation for Enhancement of Antibacterial Activity and Cytotoxic Properties against Cancer Cells. Metals 13(4), 735 (2023).
Mahmood, R. I. et al. Biosynthesis of copper oxide nanoparticles mediated Annona muricata as cytotoxic and apoptosis inducer factor in breast cancer cell lines. Sci. Rep. 12(1), 16165 (2022).
Article CAS PubMed PubMed Central Google Scholar
Al-Jubori, A. A. et al. Layer-by-layer nanoparticles of tamoxifen and resveratrol for dual drug delivery system and potential triple-negative breast cancer treatment. Pharmaceutics 13(7), 1098 (2021).
Article CAS PubMed PubMed Central Google Scholar
Guerra, V. et al. 2D boron nitride nanosheets (BNNS) prepared by high-pressure homogenisation: Structure and morphology. Nanoscale 10(41), 19469–19477 (2018).
Article CAS PubMed Google Scholar
Thangasamy, P. & Sathish, M. Supercritical fluid processing: A rapid, one-pot exfoliation process for the production of surfactant-free hexagonal boron nitride nanosheets. CrystEngComm 17(31), 5895–5899 (2015).
Kumar, A., Malik, G., Sharma, S., Chandra, R. & Mulik, R. S. Precursors controlled morphologies of nanocrystalline h-BN and its growth mechanism. Ceram. Int. 47(21), 30985–30992 (2021).
Almeida, M. S. D. et al. Novel Gd(OH)3, GdOOH and Gd2O3 nanorods: Microwave-assisted hydrothermal synthesis and optical properties. Mater. Res. 19, 1155–1161 (2016).
Jeon, S., Ko, J. W. & Ko, W. B. Synthesis of Gd2O3 nanoparticles and their photocatalytic activity for degradation of azo dyes. Catalysts 11(6), 742 (2021).
İrim, ŞG. et al. Physical, mechanical and neutron shielding properties of h-BN/Gd2O3/HDPE ternary nanocomposites. Radiat. Phys. Chem. 144, 434–443 (2018).
Xu, C., Ou, M., Zhou, H. & Yang, C. Preparation and properties of bifunctional Gd2O3/GQD composite nanoparticles. J. Rare Earths 40(7), 1118–1125 (2022).
Sezgin-Bayindir, Z., Antep, M. N. & Yuksel, N. Development and characterization of mixed niosomes for oral delivery using candesartan cilexetil as a model poorly water-soluble drug. AAPS Pharmscitech. 16, 108–117 (2015).
Article CAS PubMed Google Scholar
Khashan, K. S., Sulaiman, G. M., Hamad, A. H., Abdulameer, F. A. & Hadi, A. Generation of NiO nanoparticles via pulsed laser ablation in deionised water and their antibacterial activity. Appl. Phys. A 123, 1–10 (2017).
Nazar, D. A. M., Silva, W. M., de Oliveira, E. F. & de Sousa, E. M. B. Boron nitride nanotubes decorated with magnetite nanoparticles for application as a multifunctional system in cancer treatment. Nano-Struct. Nano-Obj. 24, 100616 (2020).
Bhanvase, B. & Barai, D. Nanofluids for Heat and Mass Transfer: Fundamentals (Academic Press, 2021).
Maqbool, Q. et al. Operando monitoring of a room temperature nanocomposite methanol sensor. Catal. Sci. Technol. 13(3), 624–636 (2023).
Article CAS PubMed Google Scholar
Massard, C., & Awitor, K. O. The use of a suspension of functionalized gadolinium oxide nanoparticles for photocatalytic applications. J. Adv. Mater. Sci. Eng. (2022).
Gorbachev, R. V. et al. Hunting for monolayer boron nitride: Optical and Raman signatures. Small 7(4), 465–468 (2011).
Article CAS PubMed Google Scholar
Hidalgo, A., Makarov, V., Morell, G., & Weiner, B. R. High-yield synthesis of cubic and hexagonal boron nitride nanoparticles by laser chemical vapor decomposition of borazine. In Dataset Papers in Science. Vol. 2013 (2012).
Sarkar, B. J., Deb, A. K. & Chakrabarti, P. K. XRD, HRTEM, Raman and magnetic studies on chemically prepared nanocrystalline Fe-doped gadolinium oxide (Gd 1.90 Fe 0.10 O3 − δ) annealed in vacuum. RSC Adv. 6(8), 6395–6404 (2016).
Article ADS CAS Google Scholar
Eprasatya, A., Yulizar, Y., Yunarti, R. T. & Apriandanu, D. O. B. Fabrication of Gd2O3 nanoparticles in hexane-water system using Myristica fragrans Houtt leaves extract and their photodegradation activity of malachite green. IOP Conf. Ser. Mater. Sci. Eng. (IOP Publishing) 902(1), 012004 (2020).
Sarkar, B. J. et al. Microstructural investigation, Raman and magnetic studies on chemically synthesized nanocrystalline Ni-doped gadolinium oxide (Gd 1.90 Ni 0.10 O3− δ). J. Electron. Mater. 47, 1768–1779 (2018).
Article ADS CAS Google Scholar
Kang, J. G., Min, B. K. & Sohn, Y. Synthesis and characterization of Gd (OH)3 and Gd2O3 nanorods. Ceram. Int. 41(1), 1243–1248 (2015).
Dhananjaya, N. et al. Hydrothermal synthesis of Gd2O3: Eu3+ nanophosphors: Effect of surfactant on structural and luminescence properties. J. Alloys Compds. 587, 755–762 (2014).
Rastogi, P. K. et al. Graphene–hBN non-van der Waals vertical heterostructures for four-electron oxygen reduction reaction. Phys. Chem. Chem. Phys. 21(7), 3942–3953 (2019).
Article CAS PubMed Google Scholar
Le Luyer, C., García-Murillo, A., Bernstein, E. & Mugnier, J. Waveguide Raman spectroscopy of sol–gel Gd2O3 thin films. J. Raman Spectrosc. 34(3), 234–239 (2003).
Santara, B., Pal, B. & Giri, P. K. Signature of strong ferromagnetism and optical properties of Co-doped TiO2 nanoparticles. J. Appl. Phys. 110(11), 34 (2011).
Rahman, A. A., Vasilev, K. & Majewski, P. Ultra-small Gd2O3 nanoparticles: Absorption and emission properties. J. Colloid Interface Sci. 354(2), 592–596 (2011).
Peng, D. et al. Facile and green approach to the synthesis of boron nitride quantum dots for 2, 4, 6-trinitrophenol sensing. ACS Appl. Mater. Interfaces 10(8), 7315–7323 (2018).
Article CAS PubMed Google Scholar
Khashan, K. S. et al. Antibacterial activity of TiO2 nanoparticles prepared by one-step laser ablation in liquid. Appl. Sci. 11(10), 4623 (2021).
Hong, S. M. et al. Simple preparation of anatase TiO2 nanoparticles via pulsed laser ablation in liquid. Bull. Korean Chem. Soc. 34(1), 279–282 (2013).
Apriandanu, D. O. B., Surya, R. M., Beppu, K., & Amano, F. Anion-exchange membrane—Photoelectrochemical water splitting using porous hematite photoanodes. ACS Appl. Energy Mater. (2023).
Apriandanu, D. O. B., Nomura, S., Nakayama, S., Tateishi, C. & Amano, F. Effect of two-step annealing on photoelectrochemical properties of hydrothermally prepared Ti-doped Fe2O3 films. Catal. Today 411, 113826 (2023).
Apriandanu, D. O. B., Nakayama, S., Shibata, K. & Amano, F. Ti-doped Fe2O3 photoanodes on three-dimensional titanium microfiber felt substrate for photoelectrochemical oxygen evolution reaction. Electrochim. Acta 456, 142434 (2023).
Mzwd, E. et al. Green synthesis of gold nanoparticles in Gum Arabic using pulsed laser ablation for CT imaging. Sci. Rep. 12(1), 10549 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Ahmed, A., Siddique, M. N., Alam, U., Ali, T. & Tripathi, P. Improved photocatalytic activity of Sr doped SnO2 nanoparticles: A role of oxygen vacancy. Appl. Surf. Sci. 463, 976–985 (2019).
Article ADS CAS Google Scholar
Raval, A. et al. Antibacterial efficacy and surface characteristics of boron nitride coated dental implant: An in-vitro study. J. Funct. Biomater. 14(4), 201 (2023).
Article CAS PubMed PubMed Central Google Scholar
Ikram, M. et al. Impact of Bi doping into boron nitride nanosheets on electronic and optical properties using theoretical calculations and experiments. Nanoscale Res. Lett. 16(1), 82 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Chaturvedi, K. et al. Robust synthesis and characteristics of novel one-dimensional gadolinium oxide nanorods decorated multiwalled carbon nanotubes based antibacterial nanocomposites for health care applications. Inorgan. Chem. Commun. 157, 111324 (2023).
Ikram, M. et al. Bactericidal behavior of chemically exfoliated boron nitride nanosheets doped with zirconium. Appl. Nanosci. 10, 2339–2349 (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Ikram, M. et al. Evaluation of antibacterial and catalytic potential of copper-doped chemically exfoliated boron nitride nanosheets. Ceram. Int. 46(13), 21073–21083 (2020).
Cvitkovitch, D. G., Li, Y. H. & Ellen, R. P. Quorum sensing and biofilm formation in Streptococcal infections. J. Clin. Invest. 112(11), 1626–1632 (2003).
Article CAS PubMed PubMed Central Google Scholar
Li, H., Chen, Q., Zhao, J. & Urmila, K. Enhancing the antimicrobial activity of natural extraction using the synthetic ultrasmall metal nanoparticles. Sci. Rep. 5(1), 11033 (2015).
Article ADS CAS PubMed PubMed Central Google Scholar
Armentano, I. et al. The interaction of bacteria with engineered nanostructured polymeric materials: A review. Sci. World J. 2014, 112 (2014).
Gao, W., Thamphiwatana, S., Angsantikul, P. & Zhang, L. Nanoparticle approaches against bacterial infections. Wiley Interdiscip. Rev. Nanomed. Nanobiotechnol. 6(6), 532–547 (2014).
Article CAS PubMed PubMed Central Google Scholar
Luan, B., Huynh, T. & Zhou, R. Complete wetting of graphene by biological lipids. Nanoscale 8(10), 5750–5754 (2016).
Article ADS CAS PubMed Google Scholar
Bhattacharya, P. & Neogi, S. Gentamicin coated iron oxide nanoparticles as novel antibacterial agents. Mater. Res. Exp. 4(9), 095005 (2017).
Bhattacharya, P., Dey, A. & Neogi, S. An insight into the mechanism of antibacterial activity by magnesium oxide nanoparticles. J. Mater. Chem. B 9, 5329–5339 (2021).
Article CAS PubMed Google Scholar
Xu, Y. et al. Exposure to TiO2 nanoparticles increases Staphylococcus aureus infection of HeLa cells. J. Nano Biotechnol. 14(1), 1–16 (2016).
Ismail, R. A., Sulaiman, G. M., Mohsin, M. H. & Saadoon, A. H. Preparation of silver iodide nanoparticles using laser ablation in liquid for antibacterial applications. IET Nanobiotechnol. 12(6), 781–786 (2018).
Article PubMed PubMed Central Google Scholar
Yang, W. et al. Food storage material silver nanoparticles interfere with DNA replication fidelity and bind with DNA. Nanotechnology 20(8), 085102 (2009).
Article ADS PubMed Google Scholar
Gurunathan, S., Han, J. W., Dayem, A. A., Eppakayala, V. & Kim, J. H. Oxidative stress-mediated antibacterial activity of graphene oxide and reduced graphene oxide in Pseudomonas aeruginosa. Int. J. Nanomed. 3, 5901–5914 (2012).
Zakharova, O. V. et al. Considerable variation of antibacterial activity of Cu nanoparticles suspensions depending on the storage time, dispersive medium, and particle sizes. BioMed Res. Int. 2015, 15 (2015).
Leung, Y. H. et al. Mechanisms of antibacterial activity of MgO: Non-ROS mediated toxicity of MgO nanoparticles towards Escherichia coli. Small 10(6), 1171–1183 (2014).
Article CAS PubMed Google Scholar
Aloufi, A. S. Green synthesis of strontium-doped tin dioxide (SrSnO2) nanoparticles using the Mahonia bealei leaf extract and evaluation of their anticancer and antimicrobial activities. Green Process. Synth. 12(1), 20228116 (2023).
Imran, H. J., Hubeatir, K. A. & Aadim, K. A. A novel method for ZnO@ NiO core–shell nanoparticle synthesis using pulse laser ablation in liquid and plasma jet techniques. Sci. Rep. 13(1), 5441 (2023).
Article ADS CAS PubMed PubMed Central Google Scholar
Abbas, Z. S. et al. Galangin/β-cyclodextrin inclusion complex as a drug-delivery system for improved solubility and biocompatibility in breast cancer treatment. Molecules 27(14), 4521 (2022).
Article CAS PubMed PubMed Central Google Scholar
Sukhorukova, I. V. et al. Boron nitride nanoparticles with a petal-like surface as anticancer drug-delivery systems. ACS Appl. Mater. Interfaces 7(31), 17217–17225 (2015).
Article CAS PubMed Google Scholar
Mortezazadeh, T. et al. Gadolinium (III) oxide nanoparticles coated with folic acid-functionalized poly (β-cyclodextrin-co-pentetic acid) as a biocompatible targeted nano-contrast agent for cancer diagnostic: In vitro and in vivo studies. Magnet. Resonan. Mater. Phys. Biol. Med. 32, 487–500 (2019).
Li, L. et al. A boron-10 nitride nanosheet for combinational boron neutron capture therapy and chemotherapy of tumor. Biomaterials 268, 120587 (2021).
Article CAS PubMed Google Scholar
da Silva, W. M. et al. Boron nitride nanotubes radiolabeled with 153Sm and 159Gd: Potential application in nanomedicine. Appl. Radiat. Isotopes 157, 109032 (2020).
Emanet, M., Şen, Ö. & Çulha, M. Evaluation of boron nitride nanotubes and hexagonal boron nitrides as nanocarriers for cancer drugs. Nanomedicine 12(7), 797–810 (2017).
Article CAS PubMed Google Scholar
Li, X. et al. Multimodal luminescent-magnetic boron nitride nanotubes@ NaGdF 4: Eu structures for cancer therapy. Chem. Commun. 50(33), 4371–4374 (2014).
Singh, B. et al. Nanostructured boron nitride with high water dispersibility for boron neutron capture therapy. Sci. Rep. 6(1), 1–10 (2016).
Emanet Ciofani, M., Sen, O. & Çulha, M. Hexagonal boron nitride nanoparticles for prostate cancer treatment. ACS Appl. Nano Mater. 3(3), 2364–2372 (2020).
Li, H. et al. Biomimetic boron nitride nanoparticles for targeted drug delivery and enhanced antitumor activity. Pharmaceutics 15(4), 1269 (2023).
Article CAS PubMed PubMed Central Google Scholar
Mao, Y. et al. Hexagonal boron nitride nanodots inhibit cell proliferation of HUVECs and the underlying mechanism. Colloid Interface Sci. Commun. 56, 100738 (2023).
Sarikhani, A. et al. Ultrasmall Fe3O4 and Gd2O3 hybrid nanoparticles for T1-weighted MR imaging of cancer. Cancer Nanotechnol. 13(1), 1–17 (2022).
Paul, R. et al. Synthesis, characterization and in-vitro studies of CNT/Gd2O3 hybrid structure. Carbon Trends 23, 100272 (2023).
Hedlund, A. et al. Gd2O3 nanoparticles in hematopoietic cells for MRI contrast enhancement. Int. J. Nanomed. 7, 3233–3240 (2011).
Mortezazadeh, T. et al. In vitro and in vivo characteristics of doxorubicin-loaded cyclodextrine-based polyester modified gadolinium oxide nanoparticles: A versatile targeted theranostic system for tumour chemotherapy and molecular resonance imaging. J. Drug Target. 28(5), 533–546 (2020).
Article CAS PubMed Google Scholar
The authors would like to extend their appreciation to the Finnish Cultural Foundation and the Tampere Tuberculosis Foundation, both associated with Tampere University, Finland, represented by Ashok Aspatwar, for their technical and financial help.
Department of Applied Sciences, University of Technology, Baghdad, Iraq
Mayyadah H. Mohsin, Khawla S. Khashan & Ghassan M. Sulaiman
Department of Medicinal Chemistry and Pharmacognosy, College of Pharmacy, Qassim University, 51452, Qassim, Saudi Arabia
Department of Pharmacognosy and Medicinal Plants, Faculty of Pharmacy, Al-Azhar University, Cairo, 11884, Egypt
Faculty of Medicine and Health Technology, Tampere University, 33520, Tampere, Finland
Kamal A. Qureshi & Ashok Aspatwar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
M.H.M., K.S.K., G.M.S., conceived and designed the experiments. M.H.M., K.S.K., G.M.S., H.A.M., A.A., performed the experiments and data analysis, M.H.M., K.S.K., G.M.S., prepared and characterized samples, M.H.M., K.S.K., G.M.S., H.A.M., K.A.Q., A.A., writing-review and editing the manuscript.
Correspondence to Ghassan M. Sulaiman or Ashok Aspatwar.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Mohsin, M.H., Khashan, K.S., Sulaiman, G.M. et al. A novel facile synthesis of metal nitride@metal oxide (BN/Gd2O3) nanocomposite and their antibacterial and anticancer activities. Sci Rep 13, 22749 (2023). https://doi.org/10.1038/s41598-023-49895-4
DOI: https://doi.org/10.1038/s41598-023-49895-4
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
![A novel facile synthesis of metal nitride@metal oxide (BN/Gd2O3) nanocomposite and their antibacterial and anticancer activities | Scientific Reports](http://cdn.globalso.com/epomaterial/Lanthanum-Zirconate.jpg)
CAS No 12032-20-1 Scientific Reports (Sci Rep) ISSN 2045-2322 (online)