Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Nature Communications volume  15, Article number: 1748 (2024 ) Cite this article refractaloy bar

The 2000 series aluminium alloys are qualified for widespread use in lightweight structures, but solidification cracking during fusion welding has been a long-standing issue. Here, we create a zirconium (Zr)-core-aluminium (Al)-shell wire (ZCASW) and employ the oscillating laser-arc hybrid welding technique to control solidification during welding, and ultimately achieve reliable and crack-free welding of 2024 aluminium alloy. We select Zr wires with an ideal lattice match to Al based on crystallographic information and wind them by the Al wires with similar chemical components to the parent material. Crack-free, equiaxed (where the length, width and height of the grains are roughly equal), fine-grained microstructures are acquired, thereby considerably increasing the tensile strength over that of conventional fusion welding joints, and even comparable to that of friction stir welding joints. This work has important engineering application value in welding of high-strength aluminum alloys.

Today, lightweight materials are an important component in promoting energy and environmental sustainabiliy1,2. Every additional 100 kg decrease in vehicle weight leads to a reduction in CO2 emissions of 8.7 g per km and fuel consumption of 0.4 l per 100 km3. Therefore, the assembly of lightweight structural parts into a functional unit holds great significance across multiple industries, including aerospace, railway, automotive and shipbuilding4. Welding is an important process for assembling lightweight materials.

Aluminium (Al) alloys are typical lightweight materials and have found extensive applications in recent decades5,6. Owing to their exceptional strength at low weight7,8, the 2xxx series alloys are often employed in aerospace and military field. One of the most widely studied members is Al alloy 2024 (AA2024). For the welding of AA2024, friction stir welding (FSW) is favored by most experts9. However, the FSW process tends to be constrained by complicated shape of structural parts and requires special set-up. While fusion welding is undoubtedly more flexible and efficient, numerous scholars have conducted research on the welding of AA2024, such as arc welding10, laser welding11, electron beam welding12 and hybrid welding8. And they highlight that one of the primary problems of fusion welding is solidification cracking, which considerably hinders its widespread use.

AA2024 tends to have a relatively wide temperature range that leads to wide mushy zone where liquid and solid phases coexist during solidification, and often solidifies in the form of columnar dendrites during the fusion welding13. As the solidification process advances, the proportion of liquid phase decreases. When the tensile stress resulting from solidification shrinkage exceeds the strength of the almost completely solidified microstructure and the liquid feeding is insufficient during solidification, solidification cracking would occur between the dendrites13.

To expand the potential use of AA2024 in aerospace and military applications, many efforts have been made to address the solidification cracking issues14,15,16. The development of filler materials provides effective methods for inhibiting solidification cracking8,17,18. As we know, the filler material is usually similar to the base metal to preserve its original properties without compatibility problems. Based on this principle, ER2319 filler material, an Al-Cu wire, should be the priority selection for welding AA2024. However, this strategy is not suggested due to the occurrence of solidification cracking. Instead, ER4043 or ER4047 filler materials—a binary Al-Si system—are widely suggested to join these materials13,17. This is because the introduction of Si element could promote to form a substantial quantity of low-melting-point eutectic, which is able to rapidly fill the channels between the dendrites and cure the cracking through the healing effect13. It should be noted that Al-Si systems filler material can mitigate solidification cracking, but the weld joints generally exhibit unsatisfactory mechanical properties. For example, the tensile strength of weld joints fabricated with Al-Si wires converges at approximately 280 MPa8, while the strength of AA2024 used in the aerospace community exceeds 400 MPa. Thus, achieving high-strength and crack-free welding of AA2024 remains a barrier.

Delightfully, fine equiaxed microstructures exhibit superior strain accommodation capabilities in the mushy zone by mitigating coherency that constrains the dendrites orientation and facilitates cracking19. Meanwhile, fine equiaxed microstructures also present good performance15, which has been proven by numerous scholars. Nevertheless, how to obtain the fine equiaxed microstructure has been a primary problem. Promisingly, introducing nucleation particles to produce identical ultrafine equiaxed structure has been an effective method. It can enlarge the equiaxed region of the thermal gradient-growth velocity curve20, which could easily assist to generate equiaxed microstructure21. Furthermore, the emergence of nucleation particles could increase the undercooling at the solid/liquid interface and decrease the critical nuclear radius22, thereby effectively facilitating the grain refinement during solidification. To obtain ultrafine equiaxed microstructures, the nucleation particles need to have similar lattice parameters to α-Al22,23,24. Thus, common elements for inoculation treatments, such as Zr, Ti, and Sc, have been chosen to form Al3X (X = Zr, Ti, or Sc) owing to their small lattice mismatch with α-Al. The lattice parameter of Al3Zr, Al3Sc and Al3Ti is 4.08 Ǻ, 4.103 Ǻ and 3.967 Ǻ, respectively, which is similar to that of Al of 4.049 Ǻ23. Compared to Al3Sc or Al3Ti phase, the lower misfit value (0.765%) between the Al3Zr phase and α-Al phase can decrease the nucleation barrier for precipitation24. Moreover, the Al3Zr phase can serve as excellent heterogeneous nucleation sites of α-Al due to the close structural resemblances between the two phases25. For example, two kinds of cube-on-cube orientation relationships (OR) exist between L12-Al3Zr and α-Al: Al(001)//L12-Al3Zr(001), Al[110]//L12-Al3Zr[110] and Al(100)//L12-Al3Zr(100), Al[010]//L12-Al3Zr[010]26.

In this work, we create a zirconium (Zr)-core-aluminium (Al)-shell wire (ZCASW) and employ the oscillating laser-arc hybrid welding technique to control solidification during welding, and fine grain (approximately 4 μm), crack-free of AA2024 weld joints are obtained. The welds display a surprisingly high ultimate tensile strength of 349 MPa that is even comparable to that of FSW. This suggests that the introduction of the ZCASW could enable fusion welding of AA2024 for structural designs in the aerospace industry. The filler material overcomes the dilemma of the trade-off between strength and cracking that remains an open question in applications of high-performance alloys. This welding technology provides a foundation for broad industrial applications because it could meet the demands for efficiency in automated welding.

Figure 1a illustrates the oscillating laser-arc hybrid welding process of AA2024, where the filler material is melted by the arc heat source, and the oscillating laser beam is applied behind the arc to promote the alloy element distribute homogeneously. The innovative ZCASW is fabricated by assembling 7 fine wires (diameters of 0.6 mm). The Zr wire serves as the central wire, around which six Al wires are twisted and wound (see Methods). Figure 1b displays the schematic diagram and product of the ZCASW filler material. A key benefit of this kind of configuration lies in how the grain refiner elements are incorporated into the molten pool. During welding, the first metallurgical bond among elements occurs with the formation of droplet, and then each droplet becomes increasingly larger until it enters the molten pool, where it could be mixed and stirred to obtain the second metallurgical bond driven by the oscillating beam. This leads to a more effective and homogeneous transition of alloying elements. Furthermore, a simple approach for the preparation of the ZCASW filler material solely relies on the physical strand mechanism instead of conventional casting process, which has shorter preparation times and less cost of critical raw materials to some extent. In terms of use, we also demonstrate that the ZCASW filler material meets the efficiency demands for automated welding, just like conventional welding wire. Therefore, we believe that this welding wire has significant promise for use in industrial manufacturing. To obtain fine equiaxed microstructures to resist solidification cracking, Zr is selected as the grain refiner, which results in the formation of a favorable Al3Zr nucleation phase. This phase could significantly improve grain refinement efficiency and provide a low-energy nucleation barrier for α-Al according to classical nucleation theory22,24. Figure 1c displays the crystallographic data of α-Al and L12-Al3Zr and their lattice match relationships15,26,27.

a Schematic diagram of the welding process. b Longitudinal and cross-sectional schematic diagram and product of the ZCASW filler. c Schematic representation of the crystallographic data of α-Al and L12-Al3Zr15,26,27, illustrating how the lattice-matched Al3Zr phase could induce low-energy-barrier epitaxial growth of α-Al (OR1 represents orientation relationship 1 and OR2 represents orientation relationship 2).

We perform laser welding experiments using the ZCASW filler to fuse AA2024 sheets with dimensions of 150 mm × 100 mm × 8 mm. Meanwhile, we perform control experiments using standard ER2319 (Al-Cu) filler and ER4043 (Al-Si) filler. Figure 2a shows the surface topography of the welding seam fabricated with the ZCASW filler and perfect formation is obtained. Figure 2b and Fig. 2c demonstrate the longitudinal and cross section morphology of the welding seam, respectively. No cracks can be observed under the optical microscope. To visualize the weld surface morphology, we employ a 3D depth-of-field optical microscope to measure the height of the top surface of welding seam that presents favorable uniformity, as shown in Fig. 2d. To further visualize the 3D nature of internal imperfections, a 2 mm × 2 mm × 5 mm microvolume is excised for examination by X-ray micro computed tomography technology. Figure 2e, f, g show the 3D-reconstruction volumes of the defects inside the welding seam using the ER2319 filler, the ER4043 filler and the ZCASW filler, respectively. Of notes, the cracks (rendered in yellow) appear in the Fig. 2e. Figure 2f displays the anticipated effect and no crack appears. Figure 2g exhibits no cracks as well, indicating that this filler material is remarkably effective.

a The surface topography of the welding seam fabricated with ZCASW filler. b The longitudinal section morphology of the welding seam. c The cross-sectional morphology of the welding seam. d The morphology and height measurements of the weld surface (Color bar represents the height of the surface of welding seam). e–g 3D-reconstruction volumes of the defects inside the welding seam fabricated with the ER2319, the ER4043 and the ZCASW fillers, respectively (Color bar denotes pores diameter).

The shape of the solid primary dendrites/crystals is known to influence cracking susceptibility during solidification. In general, solidified microstructures with coarse dendrites have higher solidification cracking susceptibility (SCS) than those with fine dendrites13,15. To further validate these results, we conduct microstructure analysis from the perspective of the dendrite morphology and the interdendritic region morphology in the melting zones fabricated with different fillers.

Here, we first discuss the effect of the dendrite morphology in detail. Figure 3a presents the melting zone fabricated with the ER2319 filler material. Owing to the wide mushy zone and the nonlinear relationship between the solid fraction and temperature of the high-strength Al alloy4, the melting zone solidifies into large dendrites. Figure 3b shows the inverse pole figure (IPF) of the melting zone. To quantify the dendrite size, we count and obtain an average size of 36 µm from the melting zone (Fig. 3c). It should be noted that large dendrites could lead to the long interdendritic liquid channels during solidification. As the temperature and liquid volume fraction decrease, the long liquid channels could be trapped or hindered by the developing dendritic solid network. Solidification cracking would occur when liquid feeding becomes insufficient to compensate for solidification shrinkage and thermal contraction28,29. Figure 3d displays the melting zone fabricated with the ER4043 filler material. The average dendrite size in the melting zone is 38 µm (Fig. 3f), which is close to that of the ER2319 filler (36 µm). No solidification cracking is found in the melting zone. However, several compromises must be made in the employment of this method. The molten filler alloy locally dilutes the molten AA2024 base alloy, which reduces the concentration of strengthening alloy4. This generally leads to the reduction in the strength of welded joints.

a, d, g Ultra-depth-of-field microscope characterization of welds fabricated with the ER2319, the ER4043 and the ZCASW filler materials, respectively. b, e, h The IPF of the melting zones fabricated with the ER2319, the ER4043 and the ZCASW filler materials. c, f, i Dendrites size statistics of the melting zones fabricated with the ER2319, the ER4043 and the ZCASW filler materials. j STEM-HAADF image in one equiaxed dendrites region and corresponding EDX mapping of the main elements (Al, Zr, Cu and Mg) shown in (k). l Diffraction pattern of the L12-Al3Zr precipitate in the [0\(1(\_)\) \(1(\_)\) ] direction. m Diffraction pattern of the interface between the Al matrix and L12-Al3Zr in the [0\(1(\_)\) 1] direction. n HRSTEM-HAADF image taken at the α-Al/L12-Al3Zr interface along the [0\(1(\_)\) 1]Al([0\(1(\_)\) 1]L12-Al3Zr) zone axis, with the inset showing the corresponding FFT pattern. o Magnified view of the marked yellow area in (n), showing atomic coincidence across the interface between these two crystals.

The use of the ZCASW filler material successfully alters the solidification mechanism during welding of AA2024. The welds are free of cracks under the premise of ensuring good formation. Figure 3g shows the homogeneous microstructure throughout the melting zone fabricated with the ZCASW filler, which is remarkably distinct from those obtained with ER2319 and ER4043 filler materials. The dendrites exhibit highly equiaxed morphology with an average size of 4.0 µm (Fig. 3i), and the interdendritic regions are smooth. In general, the molten pool is dominated by large dendrites during welding due to the primary solidification condition favouring epitaxial growth, unless vigorous nucleation events occur ahead of the solid/liquid front30. StJohn et al. 31 reported that equiaxed and fine microstructures were favored by potent nucleation particles at high number densities as well as large values of the growth-restricting factor (Q), which can be expressed as Q = mlC0(k-1)30. Here, ml represents the gradient of liquidus, C0 represents the initial composition of alloy, and k represents the partition coefficient. The introduction of Zr not only increases the Q value but also provides potent nucleation particles of Al3Zr30. Therefore, the larger grain-restricting factor and more potent nucleants could contribute to the highly equiaxed and fine microstructure in our welds (Fig. 3g). To further reveal the growth behavior of highly equiaxed dendrites owing to the addition of Zr, typical equiaxed regions with intragranular precipitates are excised by a Focused ion beam (FIB) for Transmission electron microscopy (TEM) analysis. Figure 3j shows a Scanning TEM image acquired in High angular annular dark field (STEM-HAADF) mode in one equiaxed dendrites region. Additionally, the precipitate is very rich in Zr and Al according to the Energy dispersive X-ray spectroscopy (EDX) mapping image (Fig. 3k). To further identify the crystallographic structure of Zr-rich precipitates in the equiaxed dendrites region, Selected area electron diffraction (SAED) is performed. The diffraction spots associated with the Zr precipitates are circled in yellow on the SAED pattern (Fig. 3l). Diffraction patterns for several Zr cubic precipitates reveal an L12 faced-centered cubic structure (FCC), supporting the formation of L12-Al3Zr precipitates. Figure 3m shows SAED patterns of the Al matrix in the [0\(1(\_)\) 1] direction, and the diffraction spots are marked in yellow. The diffraction spots associated with L12-Al3Zr are marked in blue. An orientation relationship (OR) between L12-Al3Zr and α-Al is observed following [0\(1(\_)\) 1]Al//[0\(1(\_)\) 1]L12-Al3Zr. This OR demonstrates the typical cube-on-cube relationship between these two phases25. Figure 3n shows the high-resolution STEM-HAADF images taken at an α-Al/L12-Al3Zr interface, and the incident electron beam is parallel to the [0\(1(\_)\) 1] zone axis of L12-Al3Zr (upper part) and the adjacent Al grain (bottom part). The corresponding Fast Fourier transformation (FFT) pattern is displayed by the insert in Fig. 3n. The interfacial atomic coincidence can be clearly seen in Fig. 3o, which demonstrates a fully coherent interface between these two crystals. Such full coherency is attributed to the smaller interplanar mismatch between these two phases. The planar distances of (200) Al3Zr and (200) α-Al are 0.2084 nm and 0.2064 nm, respectively. Thus, the misfit at the Al3Zr-α-Al interface is calculated to be approximately 0.96%, indicating a highly coherent interface that provides provide a low-energy nucleation barrier for α-Al32,33.

The next point to consider is the variation in the interdendritic phase morphology. Scanning electron microscope (SEM) is employed to investigate the interdendritic phase morphology in the melting zone fabricated with the ER2319 and the ZCASW filler materials. Figure 4a illustrates the typical interdendritic phase distribution in the melting zone fabricated with the ER2319 filler. The interdendritic phase is lamellar and continuously distributes along the interdendritic regions, normally resulting in continuous segregations. This dendrite growth is unexpected since it generally causes the melting zone to have less tensile strength and trigger crack defects even if there is less stress or strain13.

a, b Interdendritic phase in the melting zone fabricated with the ER2319 and the ZCASW filler materials. c Comparison of interdendrictic phase area fractions obtained from different melting zones (Error bars represent standard deviation). d EPMA maps showing the chemical constitutions of the interdendritic phase and Al matrix in the melting zone fabricated with the ZCASW filler. e Interdendritic phase observed by TEM-EDX, showing a STEM-HAADF image. f SAED pattern of the interdendritic phase. g EDX mapping of the main elements (Al, Cu, Mg and Zr). h HRTEM image of the interface between α-Al and Mg2Cu phase, with the inset showing the FFT pattern of Mg2Cu phase.

Figure 4b displays the typical interdendritic phase distribution in the melting zone fabricated with the ZCASW filler. Here, the interdendritic phase is segmented, and its fragments are randomly oriented, shorter than their counterparts fabricated with the ER2319 filler. Meanwhile, the area fractions of interdendrictic phase obtained from different melting zones are further analyzed by SEM images in the Backscattered electron (BSE) diffraction mode. The area fraction of the interdendritic phase in the melting zone fabricated with ER2319 filler is 11.5% (Fig. 4c), and it increases to 15.95% in the melting zone fabricated with ZCASW filler. More interdendritic phase indicates more liquid exists among dendrites during the terminal stage of solidification34, which could sufficiently compensate for solidification shrinkage and thermal contraction. On the other hand, the shorter and randomly oriented interdendritic phase, combined with highly equiaxed and round dendrites, indicate high fluidity of the remaining melt during solidification. The current results are compatible with the less susceptibility to cracking of the melting zone.

To further clearly identify the composition distribution of melting zone, a typical region is selected for Electron probe micro analysis (EPMA) analysis (Supplementary Fig. 6). Figure 4d shows the representative results. The interdendritic phase is highly enriched in the Mg and Cu elements, and Zr dominates the interiors of dendrites. To further identify the crystallographic information of the interdendritic phase, a typical region is excised by FIB for TEM analysis (Fig. 4e). A typical intergranular phase region is placed in STEM-HAADF mode and identified in combination with SAED and EDX mapping analyses. Figure 4f, g show the representative results, which are consistent with the Mg2Cu phase. Figure 4h shows a HRTEM image of the interface between the α-Al and Mg2Cu phase, and the inset illustrates the FFT of the Mg2Cu phase.

To further reveal how the grain refinement affects solidification cracking, we propose an approach combining the phase field (PF) simulation and Kou’s criterion for cracking. The PF simulation is undertaken to investigate the microstructural evolution that significantly influences solidification cracking. The Kou’s criterion for cracking35, which primarily considers grain separation owing to tensile deformation, the growth rate of grains to bond together, and liquid feeding to fill grain boundaries, is employed to investigate the SCS. In this criterion, the maximum |dT/d(fs)1/2| of an alloy, where T refers to temperature and fs represents the solid fraction, is proposed as a simple index for assessing the SCS35. This index is related to the T-(fs)1/2 curve, and a more precise T-(fs)1/2 relationship could more accurately predict the SCS.

Figure 5a simulates the variation in dendrites and liquid channel morphologies during solidification of the melting zone fabricated with the ER2319 (top) and the ZCASW (bottom) fillers. When the average dendrite size is 36 µm, corresponding to ER2319 filler, the microstructure exhibits dendritic growth and the well-developed side branches are accompanied with the primary arms. When the dendrite size decreases to 4.0 µm, corresponding to the ZCASW filler, the microstructure appears to be a nondendritic equiaxed structure, and no side branches formed. These simulated results are consistent with the previous experimental results. An additional point of concern is the liquid channel morphologies at the terminal solidification stage. As for the ER2319 filler, the residual liquid firstly forms continuous elongated liquid channels, and then the liquid channels become undulant due to the appearance of side branches. However, the liquid channels appear significantly shorter between dendrites as for ZCASW filler, and their solidification path is often more tortuous, which makes a great contribution to resisting cracking. In addition, Fig. 5a also illustrates the solute distribution in the melting zones fabricated with the ER2319 and the ZCASW fillers. During dendritic growth, the solute is rejected to the residual liquid by the solid network structure. As the temperature decreases, the concentration of solute Cu is much higher in the liquid. As for the ER2319 filler, it is clearly that solute segregation emerges not only between the primary dendrites but also between the secondary dendrites. However, the solute segregation behavior only occurs between nondendritic equiaxed structure as for the ZCASW filler.

a Simulated liquid channel morphology during dendritic growth of the melting zone fabricated with ER2319 (top) and ZCASW (bottom) fillers. The six panels in each row correspond to the different temperatures. b, c Simulated solute distribution of the melting zone fabricated with the ER2319 filler and the ZCASW filler at 882 K. d Solute distribution along line AA’ in (b) and line BB’ in (c). e T-(fs)1/2 curves and cracking susceptibility indexes calculated from the PF simulations for the melting zone fabricated with the ZCASW (blue) and the ER2319 (orange) fillers (CSI represents cracking susceptibility index).

To better understand the solute segregation behavior, the Cu concentration distribution along line AA’ in Fig. 5b and line BB’ in Fig. 5c is shown in Fig. 5d. Note that the solute distribution maps are acquired at the same temperature. The Cu concentration for both conditions in the residual liquid is much higher than that in the solid network structure, and the peaks of the Cu concentrations are almost identical. However, the average width of the liquid channels for the nearest neighbor dendrites significantly increases with increasing dendrites size. This implies that more solute accumulates in the liquid channels, which suggests a higher segregation degree at a given temperature for larger dendrites size. Notably, strong segregation behavior in liquid channels can impair extensive coalescence of the dendrites and thus make the dendrite susceptible to solidification cracking36.

To realize the quantitative description of SCS using Kou’s index, T-(fs)1/2 curves are obtained from PF simulated data (Fig. 5e). Figure 5e compares the T-(fs)1/2 curves of the melting zone fabricated with the ER2319 and the ZCASW fillers. At the terminal solidification stage with high fs, the T-(fs)1/2 curve corresponding to the ER2319 filler is steeper than that corresponding to the ZCASW filler. The SCS indexes proposed by Kou35, i.e., the maximum |dT/d(fs)1/2| near (fs)1/2 = 1, are demonstrated in Fig. 5e. Note that the steeper slope of the T-(fs)1/2 curve near (fs)1/2 = 1 indicates a higher cracking susceptibility35. Moreover, we plot the curves of |dT/d(fs1/2)| vs T at the final solidification stage in the inset of Fig. 5e. It is evident that the cracking susceptibility index corresponding to the ER2319 material is higher than that corresponding to the ZCASW filler. Therefore, the melting zone fabricated with the ER2319 filler has higher SCS than that fabricated with the ZCASW filler.

To reveal the influence of the ZCASW filler on the mechanical properties of the welded joint, we conduct the microhardness and tensile tests. Figure 6a compares the cross-sectional microhardness of the welds fabricated with the ER2319, the ER4043 and the ZCASW fillers. The microhardness of the weld fabricated with the ZCASW filler is obviously enhanced compared with those of the conventional fillers. This can be attributed to an altered chemical composition and commonly known strengthening mechanisms, such as the Hall-Petch effect37.

a The microhardness of welds fabricated with the ER2319, the ER4043 and the ZCASW fillers. b Engineering stress-strain curves of the welds fabricated with the ER23198, the ER40438 and the ZCASW fillers. c A summary of the tensile strength for the welds fabricated with various filler materials. d The estimated strengthening contributions from the precipitation strengthening (Δσppt), grain size strengthening (Δσgb), solid solution strengthening (Δσss) and dislocation  strengthening (Δσdis). σ0 represents the baseline strength of pure aluminium, and σ0.2 represents experimental values of the yield strength.

Figure 6b shows that the average tensile strength of the welds fabricated with the ER2319 and ER4043 fillers is 318 MPa and 290 MPa, which is up to 72% and 66% of that of the parent materials, respectively. While the average tensile strength of the weld fabricated with the ZCASW filler reaches 349 MPa, which is considerably higher than those fabricated with the previous two fillers, i.e., ~79% of that of the parent material (σb = 442 MPa). A summary of the ultimate tensile strengths of the ZCASW welds compared to the welds fabricated with ER2319, the ER4043 and other fillers can be found in Fig. 6c. The weld fabricated with the ZCASW exhibits the best strength, surpassing the majority of values reported in the literature8. Furthermore, the tensile strength of the weld fabricated with the ZCASW filler without post-heat treatment is even comparable to that fabricated with the FSW (σb = 360 MPa)38. To understand the origin of the increase in weld strength, we perform a quantitative analysis of the weld fabricated with the ZCASW filler according to a widely recognized strength mechanism, including grain size strengthening (Δσgb), solid solution strengthening (Δσss), dislocation strengthening (Δσdis), and precipitation strengthening (Δσppt). Table 1 shows the characteristics (radius r, and volume fraction f), grain sizes (d), solute concentrations (cCu and cMg), and dislocation densities (ρ) of the melting zone. According to these characteristic values (see Methods), the strengthening contributions mentioned above can be calculated (see Methods). Considering that these strengthening mechanisms are effectively present at room temperature, it is reasonable to assume that each strength contribution could be linearly superimposed39,40. The relative contributions are displayed in Table 2. In addition, the intrinsic yield strength of pure aluminium (σ0 = 10 MPa41) must be considered. Consequently, the overall increment for yield strength can be summarized as42:

Figure 6d displays the linear superposition of the overall yield strength increments after welding, and the theoretical calculations are consistent with the experimental results. The grain size strengthening makes the most significant contribution to the melting zone at 47.2%, while precipitation strengthening is relatively insignificant. Solid solution strengthening also prevails in the melting zone, accounting for a contribution of 25.4%, and the remainder is dislocation strengthening, with a 21.2% contribution to the melting zone.

Considering the effect of Zr on the AA2024 welds, six ER2319 wires with a diameter of 0.6 mm, and one R60702 wire with a diameter of 0.6 mm were twisted into 1.8 mm diameter ZCASW filler. The R60702 wire was used as the central wire, and six ER2319 wires were twisted and wound around the central wire. The ER2319 wires were the key component of the ZCASW filler due to their similar chemical components to the parent material. The main chemical component of the R60702 wire was Zr, which was prone to react with α-Al to form Al3Zr. Experimental studies32 had shown that Al3Zr phases could act as heterogeneous nuclei and greatly refine the grains of the α-Al. The nominal chemical compositions of the substrate and welding wire are listed in Table 3, and supplementary Table 3 lists the composition of the weld fabricated with the ZCASW filler, and the test was conduct using Inductive coupled plasma optical emission spectrometer (ICP-OES).

A hybrid oscillating laser-arc welding method was adopted to fuse 2024 Al alloy sheets. The ER2319 and ER4043 fillers with a 1.2 mm diameter (chemical composition can be seen in Table 3) and the ZCASW filler with a 1.8 mm diameter were applied in the experiments. Table 4 showed the optimized welding parameters. Figure 1a demonstrates the schematic diagram of welding process.

Afterwards, all samples were machined via wire electro discharge machining (EDM). Tensile specimens were cut to a thickness of 3 mm using EDM and the surfaces were polished with 240, 400, 800 grit sandpapers in preparation for mechanical testing. Microstructure samples were also cut with EDM and mounted in epoxy resin for polishing. Grinding was performed with 240, 400, 800 and 1200 grit sandpapers. Final polishing of the samples was accomplished with 1 μm diamond and 50 nm Al2O3 polishing compounds. Some polished samples were etched with Keller’s Etchant for 15 s for SEM analysis. Additional samples were used for EBSD analysis. For TEM characterization, a sample of approximately 30 nm thickness was cut from the melting zone using a FIB microscope.

To characterize the spatial distribution of the solidification crack defects, X-ray micro computed tomography technology was performed on a Zeiss Xradia 620. 2 mm × 2 mm × 5 mm microvolume samples were cut for X-ray microtomography. To identify typical minimum detectable defects during scanning, and 3 μm × 3 μm × 3 μm voxels were selected43. The visualization was conducted with an Avizo software.

For microstructural analysis, the polished samples were observed using an optical microscope and SEM. As for EBSD analysis, the samples after grinding were polished with 10% perchloric acid and alcohol solution, and then observed using a GeminiSEM300. The samples for EBSD analysis were further analyzed to determine the elemental distributions across the dendrites and interdendritic regions using an EPMA-8050G. For TEM analysis, both the composition of the precipitates within the dendrites and the interdendritic phases were examined by a Spectra 300 for the 30-nm thick samples.

The microhardness tests were conducted at 2 mm from the upper surface of the welds, with machine settings of 100 g force and 15 s dwell time.

The monotonic tensile tests using an INSTRON-8801were conducted on three kinds of welds fabricated with the ER2319, the ER4043 and the ZCASW fillers, with a minimum width of 12 mm, a gage length of 40 mm and a thickness of 3 mm (Supplementary Fig. 7). The nominal strain rate was 2.0 mm/min. The loading direction was perpendicular to the welding direction.

The phase-field (PF) model developed by Takaki and Ohno44,45 was adopted in this study. An important advantage of this model was that it supported solute diffusion in both the solid and liquid phases. Notably, the side branches were expressed by introducing a fluctuating current J of the Gaussian random number with the variance of \(2{D}_{l}{F}_{u}^{o}q(\phi )(1+(1-k)u)/(\varDelta t\varDelta {x}^{d})\) , where\({F}_{u}^{o}\) represents the constant noise magnitude depending on the interfacial thickness, ∆t is the time step and ∆x is the lattice size.

An Al-4.5 wt% Cu alloy was chosen, and the physical properties was listed in supplementary Table 145,46,47. The governing equations of the PF model were discretized by the normal finite-differential method. The time evolutions were discretized by the first-order Euler scheme. The time-step size was selected according to \(\varDelta t\le {(\varDelta x)}^{2}/5.0{D}_{l}\) . A uniform mesh spacing of\(\varDelta x\) = 0.8\({W}_{0}\)  = 0.025 μm was used, where\({W}_{0}\) refers to the interfacial thickness. The computational domain size was set as 75 μm × 75.4 µm (3000 × 3016 cells), which satisfied the actual requirements. For the cooling rate in this study, we used 2400 K·s−1, which was obtained from the actual measurements (Supplementary Fig. 1). The simulations were accelerated by multiple CPU parallel computations using the message-passing interface library.

According to the classical Hall-Petch equation, the strengthening contribution due to the grain boundaries could be given by the following equation37:

where k is the strengthening coefficient specific to each material and k = 0.12 for aluminium alloy, d is the grain size derived from the EBSD analysis (Fig. 3h, i).

According to the well-known Fleischer equation, the strengthening contribution arising from solute strengthening could be estimated using the following equation48:

where Δσi represents the theoretical strengthening efficiency for each element (ΔσMg = 18.6 MPa/wt.% and ΔσCu = 13.8 MPa/wt.%48). ci is the concentration of the solute element (in wt.%), which were measured by SEM-EDS in the study (supplementary Table 2).

The strengthening contribution arising from dislocation strengthening was estimated using the Bailey-Hirsch equation49:

where α represents a constant, which is set as 0.2 for the face-centered cubic (fcc) alloy. ρGND is the GND density, which was determined by EBSD analysis (supplementary Fig. 4).

The strength increments arising from the Orowan bypassing mechanism could be assessed as follows21:

where M = 3.06 represents the Taylor factor of the fcc alloy system, G = 27 GPa is the shear modulus of aluminium alloy, υ = 0.33 is Poisson’s ratio of the Al alloy, b = 0.286 nm is the Burgers vector value of the Al alloy, r is the mean precipitate radius. \({L}_{p}=r(\sqrt{\frac{2\pi }{3f}}-\frac{\pi }{2})\) represents the inter-precipitate distance, in which f is the precipitate volume fraction. In our case, r and f were extracted from the SEM images using the image processing software (Supplementary Fig. 6).

The data that support the findings of this study are available from the corresponding author upon request. The source data for Figs. 4c, 5d, e, 6a, b, supplementary Fig. 2 and supplementary Fig. 3 used in this study are available in Zenodo with the identifier [https://doi.org/10.5281/zenodo.10562571]50.

The code that support the findings of this study are available from the corresponding author upon request.

Zhang, W. & Xu, J. Advanced lightweight materials for automobiles: a review. Mater. Des. 221, 110994 (2022).

Lu, K. The future of metals. Science. 328, 319–320 (2010).

Article  ADS  CAS  PubMed  Google Scholar 

Bandivadekar, A. E. A. On the Road in 2035—reducing transportation’s petroleum consumption and GHG emissions, (Massachusetts Institute of Technology; Cambridge, MA, USA, 2008).

Sokoluk, M. et al. Nanoparticle-enabled phase control for arc welding of unweldable aluminum alloy 7075. Nat. Commun. 10, 1–8 (2019).

Zhong, Y. K. et al. In-situ anodic precipitation process for highly efficient separation of aluminum alloys. Nat. Commun. 12, 1–6 (2021).

Dursun, T. & Soutis, C. Recent developments in advanced aircraft aluminium alloys. Mater. Des. 56, 862–871 (2014).

Tomczyk, A., Seweryn, A. & Grądzka-Dahlke, M. The effect of dynamic recrystallization on monotonic and cyclic behaviour of Al-Cu-Mg Alloy. Materials. 11, 874 (2018).

Article  ADS  PubMed  PubMed Central  Google Scholar 

Yan, J. et al. Effect of welding wires on microstructure and mechanical properties of 2A12 aluminum alloy in CO2 laser-MIG hybrid welding. Appl. Surf. Sci. 255, 7307–7313 (2009).

Article  ADS  CAS  Google Scholar 

Sree Sabari, S., Malarvizhi, S. & Balasubramanian, V. Characteristics of FSW and UWFSW joints of AA2519-T87 aluminium alloy: effect of tool rotation speed. J. Manuf. Process. 22, 278–289 (2016).

Soysal, T. & Kou, S. Effect of filler metals on solidification cracking susceptibility of Al alloys 2024 and 6061. J. Mater. Process. Technol. 266, 421–428 (2019).

Sheikhi, M., Malek Ghaini, F. & Assadi, H. Prediction of solidification cracking in pulsed laser welding of 2024 aluminum alloy. Acta Mater. 82, 491–502 (2015).

Article  ADS  CAS  Google Scholar 

Hosseini, S. A. et al. Elimination of hot cracking in the electron beam welding of AA2024-T351 by controlling the welding speed and heat input. J. Manuf. Process. 46, 147–158 (2019).

Kou, S. Welding metallurgy, (USA: New Jersey, 2003).

Liu, X. H. et al. Grain refinement and crack inhibition of selective laser melted AA2024 aluminum alloy via inoculation with TiC-TiH2. Mater. Sci. Eng. A. 813, 1–13 (2021).

Martin, J. H. et al. 3D printing of high-strength aluminium alloys. Nature. 549, 365–369 (2017).

Article  ADS  CAS  PubMed  Google Scholar 

Cen, L. et al. Effect of high-frequency beam oscillation on microstructures and cracks in laser cladding of Al-Cu-Mg alloys. Surf. Coat. Technol. 447, 1–10 (2022).

Ahn, J. et al. Effect of filler metal feed rate and composition on microstructure and mechanical properties of fibre laser welded AA. J. Manuf. Process. 25, 26–36 (2017).

Du, J. D. et al. Effect of Ce addition on the microstructure and properties of Al-Cu-Mn-Mg-Fe lithium battery shell alloy. Mater. Charact. 142, 252–260 (2018).

Yuan, L., O Sullivan, C. & Gourlay, C. M. Exploring dendrite coherency with the discrete element method. Acta Mater. 60, 1334–1345 (2012).

Article  ADS  CAS  Google Scholar 

Todaro, C. J. et al. Grain structure control during metal 3D printing by high-intensity ultrasound. Nat. Commun. 11, 1–9 (2020).

Nie, X. J. et al. Effect of Zr content on formability, microstructure and mechanical properties of selective laser melted Zr modified Al-4.24Cu-1.97Mg-0.56Mn alloys. J. Alloy Compd. 764, 977–986 (2018).

Atamanenko, T. V. et al. On the mechanism of grain refinement in Al-Zr-Ti alloys.J. Alloy Compd. 509, 57–60 (2011).

Saha , S. , Todorova , TZ & Zwanziger , JW Temperature dependent lattice misfit and coherency of Al3X ( X = Sc , Zr , Ti and Nb ) particles in an Al matrix .Acta Mater.Rev. 89, 109–115 (2015).

Article  ADS  CAS  Google Scholar 

Jiang, S. H. et al. Ultrastrong steel via minimal lattice misfit and high-density nanoprecipitation. Nature. 544, 460–464 (2017).

Article  ADS  CAS  PubMed  Google Scholar 

Prasad, K. S. et al. On the formation of faceted Al3Zr (beta’) precipitates in Al-Li-Cu-Mg-Zr alloys. Acta Mater. 47, 2581–2592 (1999).

Article  ADS  CAS  Google Scholar 

Srinivasan, D. & Chattopadhyay, K. Non-equilibrium transformations involving L12-Al3Zr in ternary Al-X-Zr alloys. Metall. Mater. Trans. A. 36, 311–320 (2005).

Murty, B. S., Kori, S. A. & Chakraborty, M. Grain refinement of aluminium and its alloys by heterogeneous nucleation and alloying. Int. Mater. Rev. 47, 3–29 (2002).

Coniglio, N. & Cross, C. E. Initiation and growth mechanisms for weld solidification cracking. Int. Mater. Rev. 58, 375–397 (2013).

Rappaz, M., Drezet, J. M. & Gremaud, M. A new hot-tearing criterion. Metall. Mater. Trans. A. 30, 449–455 (1999).

Li, R. D. et al. Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: crack-inhibiting and multiple strengthening mechanisms. Acta Mater. 193, 83–98 (2020).

Article  ADS  CAS  Google Scholar 

StJohn, D. H. et al. The interdependence theory: the relationship between grain formation and nucleant selection. Acta Mater. 59, 4907–4921 (2011).

Article  ADS  CAS  Google Scholar 

Opprecht, M. et al. A solution to the hot cracking problem for aluminium alloys manufactured by laser beam melting. Acta Mater. 197, 40–53 (2020).

Article  ADS  CAS  Google Scholar 

Zhu, X. et al. Crack-free and high-strength AA2024 alloy obtained by additive manufacturing with controlled columnar-equiaxed-transition. J. Mater. Sci. Technol. 156, 183–196 (2023).

Zhao, Y. N. et al. New alloy design approach to inhibiting hot cracking in laser additive manufactured nickel-based superalloys. Acta Mater. 247, 118736 (2023).

Kou, S. A simple index for predicting the susceptibility to solidification cracking. Weld. J. 94, 374S–388S (2015).

Jiang, P. et al. Fine grains reduce cracking susceptibility during solidification: insights from phase-field simulations. JOM. 71, 3223–3229 (2019).

Hansen, N. Hall-Petch relation and boundary strengthening. Scr. Mater. 51, 801–806 (2004).

Liu, X. C., Wu, C. S. & Padhy, G. K. Improved weld macrosection, microstructure and mechanical properties of 2024Al-T4 butt joints in ultrasonic vibration enhanced friction stir welding. Sci. Technol. Weld. Joining 20, 345–352 (2015).

Chen, P. et al. Effect of rotation speed on microstructure evolution and mechanical properties of nugget zone in 2195-T8 Al-Li alloy friction stir welding joints. Mater. Charact. 176, 1–14 (2021).

Liu, H. J. et al. An effect of the rotation speed on microstructure and mechanical properties of the friction stir welded 2060-T8 Al-Li alloy. Mater. Charact. 123, 9–19 (2017).

Lee, S. H. et al. Precipitation strengthening in naturally aged Al-Zn-Mg-Cu alloy. Mater. Sci. Eng: A. 803, 1–8 (2021).

Hu, Y. N. et al. Inhibiting weld cracking in high-strength aluminium alloys. Nat. Commun. 13, 5816 (2022).

Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

du Plessis, A. et al. X-ray microcomputed tomography in additive manufacturing: a review of the current technology and applications. 3D Print. Addit. Manuf. 5, 227–247 (2018).

Takaki, T. et al. Competitive grain growth during directional solidification of a polycrystalline binary alloy: three-dimensional large-scale phase-field study. Materialia. 1, 104–113 (2018).

Takaki, T. et al. Two-dimensional phase-field simulations of dendrite competitive growth during the directional solidification of a binary alloy bicrystal. Acta Mater. 81, 272–283 (2014).

Ahmadein, M. et al. Grain nucleation parameters for aluminum alloys: experimental determination and model validation. Metall Mater Trans. A. 40, 646–653 (2009).

Han, C. et al. Ultra grain refinement and mechanical properties improvement of all-weld-metal for medium-thick Al-Li alloy via laser beam oscillation and in-situ alloying. Opt. Laser Technol. 168, 109965 (2024).

Ma, K. et al. Mechanical behavior and strengthening mechanisms in ultrafine grain precipitation-strengthened aluminum alloy. Acta Mater. 62, 141–155 (2014).

Article  ADS  CAS  Google Scholar 

Hansen, N. Boundary strengthening over five length scales. Adv. Eng. Mater. 7, 815–821 (2005).

Jin, J. High-strength and crack-free welding of 2024 aluminium alloy via Zr-core-Al-shell wire. source data for NC. https://doi.org/10.5281/zenodo.10562571 (2024).

This research has been supported by the National Natural Science Foundation of China under Grant No.U22A20196 (P.J.), 52305467 (S.N.G.), 52075201 (P.J.), 52188102 (P.J.), GuangDong Basic and Applied Basic Research Foundation 2023A1515010081 (S.N.G.), and Fundamental Research Funds for the Central Universities under the Grant No. YCJJ20230360 (L.Y.R.).

The State Key Laboratory of Intelligent Manufacturing Equipment and Technology, School of Mechanical Science and Engineering, Huazhong University of Science & Technology, Wuhan, Hubei, 430074, PR China

Jun Jin, Shaoning Geng, Leshi Shu, Ping Jiang, Xinyu Shao, Chu Han, Liangyuan Ren, Yuantai Li & Lu Yang

Jihua Laboratory Testing Center, Jihua Laboratory, Foshan, PR China

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

J.J., S.N.G. and C.H. conceived the idea and designed the experiments. J.J. and S.N.G. fabricated the ZCASW filler material. J.J. and Y.T.L conducted the welding experiments. J.J., X.Q.W and conducted in X-ray micro CT experiments and analyzed the data. J.J. characterized microstructures. C.H., L.Y.R. and J.J. performed the phase field modeling and analyzed solidification cracking susceptibility. J.J. and L.Y. performed mechanical tests. J.J. and S.N.G. wrote the manuscript. P.J., L.S.S. and X.Y.S. supervised the whole work.

Correspondence to Shaoning Geng or Ping Jiang.

The authors declare no competing interests.

Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Jin, J., Geng, S., Shu, L. et al. High-strength and crack-free welding of 2024 aluminium alloy via Zr-core-Al-shell wire. Nat Commun 15, 1748 (2024). https://doi.org/10.1038/s41467-024-45660-x

DOI: https://doi.org/10.1038/s41467-024-45660-x

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Nature Communications (Nat Commun) ISSN 2041-1723 (online)

welding wire 1 Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.