Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 12, Article number: 12467 (2022 ) Cite this article Type Of X Ray Tube
![Novel 3-D printed radiation shielding materials embedded with bulk and nanoparticles of bismuth | Scientific Reports](http://kehu02.grofrom.com/www.sailray-tube.com/03e68998d6f64865ae8b18c6639aefa7.jpg)
In the present study, a new type of radiation shielding material was developed by using a 3-D printing technique which enables to create a light radiation shielding materials of a great variety of shapes and dimensions. Micro and nano bismuth particles were incorporated as a filler between the inner layers of polylactic acid thermoplastic polymer (PLA Plastic) designed of the investigated 3-D printed prototypes to achieve the desired radiation attenuation. The effect of particle size on the attenuation parameters were studied over the energy range from 0.0595 to 1.41 MeV. The mass and thickness needed to reduce the intensity of the incoming radiation to half of its original value were determined experimentally for pure polymer (ABS Plastic), polymer with bulk Bi, and polymer with nano Bi. The results reveal that bismuth NPs with average particle size of about 17 ± 3 nm have a greater mass attenuation capability than normal bulk bismuth particles, meaning they are more efficient and a lighter shield can be produced. The enhanced shielding ability of nano bismuth particles was contributed to the excellent particle distribution, leading to an increase in the probability of photons interacting with the bismuth atoms. The bismuth NPs 3-D printed objects can be considered as a promising radiation shielding candidates and also could be utilized in manufacturing of radiation medical phantom.
Said M. Kassem, MIA Abdel Maksoud, … YY Ebaid
Andrew Creegan, Poul M. F. Nielsen & Merryn H. Tawhai
Seyed Musa Safdari, Shahryar Malekie,… Morteza Akbari
Radiation is strongly utilized in medicinal disciplines such as diagnostic radiology, radiotherapy and medical medicine. Energy generation, agriculture, manufacturing, and many others also can be considered as fields of radiation applications. Ionizing radiation, such as X-rays and gamma-rays, has enough energy to remove electrons from atoms in the human body, which can develop adverse harmful effect if not effectively attenuated. In order to mitigate these undesired effects, shielding materials are designed to eliminate a considerable portion of incoming photons through absorption process. The attenuation capability of a material varies depending on the energy and the type of radiation it may interact with. However, as a basic rule of thumb, high-Z and high-density elements are often desirable within shields because their great efficiency to attenuate high energy radiation1,2,3,4,5,6.
Lead has a high density, low cost, and has great attenuation near its k-absorption edge. However, lead has a major drawback due to its adverse environmental impact as well as being heavy in applications such as lead aprons. As a result, researchers have devoted their attention in finding alternatives to lead that can safely be used across various fields, and especially in medicine. Some of these substitutes include tungsten and bismuth7,8. Aside from bulk lead, pure polymer and polymer based composites have also been used as radiation shields, especially for non-ionizing radiation9,10,11,12. By introducing micro- and nanoparticles into the polymers, the radiation shielding efficiency of the polymers increases. Nanoparticles have been found to provide the greatest benefit because of the resulting greater surface-area-to-volume ratio, which leads to greater photon absorption. These fillers can also improve their mechanical, electrical, optical and chemical properties. Metal oxides such as PbO, WO3, Gd2O3, and Bi2O3 have been investigated as fillers in polymers used in radiation shielding applications. By introducing these oxides into the polymers13,14,15,16.
Much literature has been conducted to evaluate the effect grain size for varying metal and metal oxide particles. Holynska17 found that the impact of the particle size on the shielding ability of the samples greatly diminishes as energy increases, meaning that smaller particles perform better against lower energy photons. Additionally, when testing WO3, PbO, and Bi2O3 micro and nanoparticles, it was discovered that Bi2O3 nanoparticles and PbO microparticles have the best mass attenuation coefficients, which correlates with the best shielding ability18. Li et al.19, compared micro and nano gadolinium oxide Gd2O3 and found that the nano-Gd2O3 composites were more effective against X-rays and gamma-rays than the microparticles Gd2O3 composites by around 28%. Other studies have included the bulk versions of their metal oxides as another point for comparison. El-Khatib et al.20, studied high density polyethylene (HDPE) and tested the shielding abilities of pure HDPE, HDPE with micro CdO, and HDPE with nano CdO. They concluded that the HDPE with nano CdO has the best shielding ability. Zakaly et al.21 and El-Sharakawy et al.22 have developed new nano-composites radiation shielding materials prepared from polypropylene (PP) with CdO-NPs dispersed with different concentrations and bentonite containing Bi2O3 NPs additive, respectively. Studies have focused on enhancing the radiation-shielding properties by increasing the content of nanoparticles.
In this work, the radiation protection properties were experimentally studied using a HPGe detector and different point sources of bismuth metallic microparticles and nanoparticles used as fillers in PLA plastic matrix by using 3D printing technique. This new material created through this technique is efficient and lightweight for easy shielding as well as easy to design samples in a variety of shapes and sizes, so it can be used to manufacture medical radiation phantom by controlling bismuth concentration and designing the object.
The fabrication of 3D-printers plastics embedded with nano-bismuth can be achieved by dispersing the bismuth into plastic filament or by introducing the bismuth particles inside the unfilled designed layers of the printed objects. In order to produce filament embedded with bismuth, ABS plastic should be used since the ABS plastic and bismuth have close melting temperature, so the bismuth can be fused into ABS in the extruder machine (during manufacturing the filament), on the other hand PLA plastic is more easy to be printed than ABS and has greater density than ABS therefore PLA with bismuth as filler has been selected in the present study.
The shape of the object and the plastic shells and bismuth layers were designed by 3D-printers software “Ultimaker Cur” which is easy to use powerful software enable designers to draw, design and control the 3D-printers. This software was operated by dividing designed model file into layers and generating a printer-specific g-code which can be sent to the printer to create the desired physical object. The selected shape has been chosen to be simple cylindrical shape with dimension of 2 cm as diameter and 1 cm as height with plastic as 20% of volume of the object and 80% volume as unfilled space which will be filled by bismuth metal particles, three shells of plastics at the top, bottom and around the object that represent the necessary outer envelope of 3D-printed structure.
Figure 1a describes the designed shape and its inner layers which will be filled by bismuth. The object that produced and investigated in present study represents a prototype model, in real application any other printable shape can be manufactured and filled by bismuth particles. Used filaments were produced by the ESUN Company with diameter 1.75 mm and melting temperature 200 °C and 3D-printing machine model Creality CR10 with nozzle diameters of 0.4 mm, bed temperature of 65 °C and printing speed of 50 mm per minute (see Fig. 1b,c).
Machines used in 3D-printing, (a) horizontal cross section of the designed shape, (b) Esun Filaments and (c) 3D-printing machine model Creality CR10.
The high purity analytical grade bulk bismuth metal in the form of powder was supplied by cornel chemical laboratory in Egypt with a density of 9.8 g/cm3 while Nano metal bismuth particle powder were prepared by Nano tech Company in Egypt with lower density of 7.0 g/cm3. Bismuth metal particles have been added manually during the printing till the layers completely filled, the quantity of bulk bismuth oxide required to fill the space of the inner layers were slightly variable and more than the constant quantity of bismuth nano particles that filled same spaces of the same layers. Two sets of samples containing bismuth nano particles and bulk bismuth particles were produced; each set consists of six samples. Solid 100% filled of PLA plastic samples were also printed to represent the blank samples (without bismuth); another sample without bismuth was manufactured but with 20% to 80% ratio of plastics filled to unfilled layers ratio, in order to determine the mass of bismuth inside the samples and the densities of samples accurately.
The density of each sample was calculated theoretically due to the regular and constant geometry of printed objects as well as it was measured experimentally by Archimedes method using distilled water as the immersion fluid for confirmation by using the following relation:
where ρL is the density of the immersion liquid (density of distilled water is 1.000 g/cm3), Wa and Wb are the weight of samples in air and the immersion fluid, respectively. The compositions, masses and densities of the prepared samples are tabulated in Table 1. The initial thickness of the samples was 1 cm; other values can be obtained by making a combination of multiple samples of the same type.
A scanning electron microscope (SEM) (JSM-5300, JEOL) was utilized, and the samples were cut to be exposed to the electron beam and fixed with a double coated carbon tap, which also dissipated the electron beam charge and heat buildup. The samples were covered with a fine layer of gold under a vacuum before the SEM observation, using an ion sputtering coating device (JEOL-JFC-1100E). The SEM was operated at 25 kV at a magnification order of 35,000. The samples were examined by SEM to assess the homogeneity distribution of the bismuth particle for both bulk and nano Bi inside the layers of PLA as well as to determine the average particle size of Bi inside the samples, as shown in Fig. 2.
SEM images for (a) micro Bi, (b) nano Bi, (c) PLA with micro Bi, and (d) PLA with nano Bi.
Spherical-shaped bismuth nanoparticles with an average size of 17 ± 3 nm were achieved and demonstrated by SEM as shown in Fig. 2b, while the average size of bulk bismuth was 50 ± 8 nm. The morphological results shown in Fig. 2c,d indicated a clear difference in the distribution of nanoparticles rather than micro in PLA, where it was found that nanoparticles are more distributed and homogeneous, which improves its shielding properties.
The attenuation coefficients were determined experimentally by using a narrow beam technique23, the collimated beams of gamma photons of different energies penetrate the sample, the transmitted photons counted by using Canberra High Purity Germanium detector (HPGe) of the model: CS20-A31CL, coupled with multichannel analyzer (MCA). The detector relative efficiency was 24.5% for 1333 keV of Co-60-line. The characteristic of Eu-152 radioactive point source that utilized in this experiment in order to produce gamma photons with different energies are listed in the Table 2. The arrangement of attenuation experiment was shown in Fig. 3. The initial intensity (without sample) and transmitted intensity of each gamma line of interest were counted for a fixed time by evaluating the counts under the photo peak which represents the intensity of gamma rays. The counting time had been selected to acquire at least 105 counts under each peak so that the statistical uncertainty kept less than 1%. The spectrum was processed by the Genie 2000 data acquisition and analysis software made by Canberra. A proper energy and efficiency calibrations had been done before to the measurement process.
The arrangement of attenuation experiment.
The linear attenuation coefficient (LAC) represents the probability of photon interaction through a certain distance inside material and can be expressed by the following relation24,25:
where, \( I_{0} ,\,I\;{\text{and}}\;x \) represent the initial intensity, transmitted intensity and the absorber thickness, respectively. The thickness and mass needed to reduce the intensity of the incoming radiation to half of its original value called the half value layer (HVL) and the half mass value (HMV), respectively and given by the following equation25:
where, \( \rho \;{\text{and}}\;R \) are the density and the radius of sample material, respectively. Similarly, The thickness and mass needed to reduce the intensity of the incoming radiation to tenth of its original value called the tenth value layer (TVL) and the tenth mass value (TMV), respectively and given by the following equation:
The shielding efficiency of an absorber sample can be investigated using a parameter called the radiation protection efficiency (RPE) and given by the next equation26,27:
Table 3 lists the linear experimentally determined attenuation coefficients (LAC) for all the tested samples between 121.7 and 1408 keV. To determine the accuracy of these measurements, the experimental LAC values for the blank polymer (the polymer without any Bi) was compared against the LAC values obtained from the XCOM database. By comparing the results from these two methods, the accuracy of the experimental method can be assessed. The percent difference between these two methods was within ± 5% deviation, proving the accuracy of the experimental data. The greatest deviation occurred at 1086 keV and is equal to a 4.85% difference. It is vital to first ensure the precision of the results for the blank polymer since XCOM cannot predict the LAC for the sample that contains nanoparticle Bi. Once the results for the blank polymer are determined to be accurate within a desirable deviation, the same experimental setup can be used to assess the samples with bulk and nanoparticle Bi without worrying about the reliability of the process. Furthermore, the table lists the LAC values of bulk and nano Bi to compare them against each other. These values demonstrate that the LAC of bulk Bi is greater than the blank and nano Bi samples. For examples, at 344.3 keV, the blank polymer has an LAC equal to 0.129 cm−1, the bulk Bi sample has an LAC equal to 0.677 cm−1, and the nano Bi sample has an LAC equal to 0.493 cm−1. The bulk Bi sample has the greatest LAC because it has the greatest density out of the three investigated samples.
In Fig. 4, the half value layer (HVL) for the pure polymer, polymer with bulk Bi, and polymer with nano Bi were determined in the same energy range used for the LAC values. Both the polymers containing Bi have a lower HVL than the pure polymer, which means that the addition of Bi leads to a decrease in the thickness of the sample needed to attenuate the intensity of the incoming photons to half of their original value. Additionally, it can be seen that the effect of Bi on the HVL values is clearer at lower energies than at higher energies. For example, at 121.7 keV, the HVL values are equal to 3.981, 0.350, and 0.415 cm for the pure polymer, polymer with bulk Bi, and polymer with nano Bi respectively. Meanwhile, at 1408 keV, the HVL values are equal to 10.491 cm, 8.123 cm, and 8.699 cm, respectively. This result signifies that the radiation shielding advantage of the polymers with a Bi decrease as the energy increases. When comparing the HVL values of the bulk and nanoparticle polymers, it can be observed that the HVL for the bulk Bi polymer is lower than the nanoparticle Bi, which is related to the greater density of the bulk Bi sample, lowering HVL.
The HVL for the pure PLA, PLA with bulk Bi, and PLA with nano Bi at different energies.
The tenth value layer (TVL) of a sample is defined as the thickness of the material needed to reduce the intensity of the incoming radiation to one-tenth of its original value. Figure 5 illustrates the TVL of the three tested polymers. Since TVL is closely related to HVL, the same trends can be observed in both figures. As the incoming photon energy increases, the TVL values all increase with it. The TVL of the pure polymer sample, for example, increases from 12.226 cm at 121.7 keV to 18.479 cm at 344.3 keV, 28.810 cm at 964.1 cm, and 34.851 cm at 1408 keV. In addition, the TVL values following the order of: TVLpure polymer > TVLnano Bi2O3 > TVLbulk Bi2O3. At 778.8 keV, for instance, the pure polymer has a TVL equal to 26.046 cm, the nano Bi has a TVL equal to 17.238 cm, and the bulk Bi has a TVL equal to 12.743 cm. The order of these values is still correlated with the densities of the samples. Since the polymer with bulk Bi has the lowest TVL at all tested energies, this sample is the most space-efficient and has the greatest potential for radiation shielding applications. The discrepancy between the TVL results also decreases with increasing energy. At the lowest tested energy, the lowest and greatest TVL has a difference of 12.063 cm, while at the highest energy their difference is equal to 7.866 cm, it should be noted that since TVL requires greater attention than HVL, the TVL values are all greater than their respective HVL values.
The TVL for the pure PLA, PLA with bulk Bi, and PLA with nano Bi at different energies.
The mass of a material needed to reduce the intensity of the incoming radiation to half of its original value is defined as its HMV. The HMV of the three investigated samples are graphed in Fig. 6 at the first four energies, the HMV of the pure polymer is greater than the HMV for the bulk and nano Bi samples. For example, at 244.7 keV, the pure polymer has an HMV equal to 18.22 g, while the polymer with bulk Bi has an HMV equal to 4.43 g and the nano Bi polymer has a HMV equal to 2.08 g. As energy further increases, however, (E ≥ 1086 keV) the bulk Bi polymer has the greatest HMV. At 1086 keV, for instance, the HMV values are equal to 113.11 g, 146.14 g, and 60.34 g for the pure polymer, polymer with bulk Bi, and polymer with nano Bi, respectively. These results indicate that at all energies the polymer with nano Bi has a much lower HMV than the other samples, which is greatly important for real applications. In other words, a much lighter sample can be used to attenuate the same amount of photons, making this shield more practical and viable as a portable or movable radiation shield. In contrast, the polymer with bulk Bi offers great attenuation, but is much heavier than the nano Bi, making it impractical for some applications.
The HMV for the pure PLA, PLA with bulk Bi, and PLA with nano Bi at different energies.
Like HMV, TMV is the counterpart where the intensity of radiation is reduced to a tenth of its original value. This naturally results in the TMV values being much greater than the HMV results. Figure 7 illustrates the TMV of the three investigated polymers. Due to the similarity between the two parameters, the same trends can be observed in both figures. First, the TMV of the polymers increase with increasing energy. For example, the TMV of the polymer with bulk Bi increases from 7.78 g at 121.7 keV to 22.76 g at 334.3 keV, 126.27 g at 964.1 keV, 155.97 g at 1112 keV, and 180.48 g at 1408 keV. At energies below 1086 keV, the TMV follow the order of pure polymer > bulk Bi > nano Bi. For instance, at 344.3 keV, the pure polymer has a TMV of 68.47 g, the polymer with bulk Bi has a TMV of 22.76 g, and the polymer with nano Bi has a TMV of 10.27 gm. At energies greater than 1086 keV, however, the TMV of the bulk Bi sample surpasses the pure polymer. At 1112 keV, the pure polymer has a TMV equal to 114.45 g and the bulk Bi sample has a TMV of 155.97 g. This figure reaffirms the conclusion that the nano Bi is more practical for real world applications due to the much lower mass needed to attenuate the same amount of photons, even if a greater thickness might be needed compared to bulk Bi. Therefore, when selecting the most desirable radiation shield for a specific application, both the thickness and the mass of the shield must be carefully considered and compared against each other.
The TMV for the pure PLA, PLA with bulk Bi, and PLA with nano Bi at different energies.
Figure 8 illustrates the radiation protection efficiency (RPE) of the three investigated samples as a function of the incoming photon energy. This figure demonstrates that RPE decreases as energy increases for all three samples. The maximum RPE occurs at the lowest tested energy, 121.7 keV, and is equal to 86.20% for the polymer with bulk Bi2O3. RPE, then quickly decreases to its minimum value at the highest tested energy. Continuing with this sample, its RPE is equal to 64.91% at 244.7 keV, 16.53% at 778.9 keV, 10.00% at 1086 keV, and 8.18% at 1408 keV. This sharp drop signifies that the samples have a good attenuation capability at lower photon energies, and that their abilities to absorb radiation decreases with increasing energy. Thus, to maintain the same amount of attenuation against higher energy photons, the thickness of the polymer must be increased if the application requires it. Furthermore, the figure shows that both the polymers with Bi2O3 have a higher RPE than the pure polymer. For example, at 964.1 keV, the pure polymer has an RPE of 7.68%, while the polymer with bulk Bi2O3 has an RPE of 11.48%, and the polymer with nanoparticle Bi2O3 has an RPE of 9.47%. This result suggests that the addition of Bi2O3 enhances the RPE of the tested samples.
The RPE for the pure PLA, PLA with bulk Bi, and PLA with nano Bi at different energies.
Finally, the present work was compared with an essential material used for gamma ray shielding such as glass and concrete as well as previous works related to our work such as HDPE embedded in CdO nanoparticles and silicon rubber (SR) embedded with Bi2O3 nanoparticles. The comparison was reported in Table 4 and it was clear that the results of the current work provided light shielding materials with a good attenuation parameters compared to the other scheduled results.
The designed prototypes were designed and created using 3D printing method and this method proved to be capable of creating excellent radiation shielding candidates and good replacements to already available shields based on lead in real applications. Moreover, the suggested technique allows manufacturers to create radiation shields with a large variety of shapes and dimensions that can fit any the requirements of any application. Additionally, the low density nano bismuth particles have a better mass attenuation coefficient than bulk bismuth, which can help develop a lighter and more effective radiation shielding material. This advantage is attributed to the homogenous distribution of nanoparticles with approximately equal size within the printed object layers. This novel technique can be applied to a wide variety of radiation shielding applications from the shielding of low energy X-ray diagnostic to the environmental shielding of nuclear reactor due to its proved great ability of radiation attenuation and being consisting of both light and heavy material and also can be used to produce medical phantoms.
Said M. Kassem, MIA Abdel Maksoud, … YY Ebaid
Andrew Creegan, Poul M. F. Nielsen & Merryn H. Tawhai
Seyed Musa Safdari, Shahryar Malekie,… Morteza Akbari
All data generated or analyzed during this study are included in this published article.
Kumar, A. Gamma ray shielding properties of PbO-Li2O-B2O3 glasses. Radiat. Phys. Chem. 136, 50–53 (2017).
Article ADS CAS Google Scholar
Bagheri, R., Moghaddam, A. K. & Yousefi, A. Gamma-ray shielding study of light to heavyweight concretes using MCNP-4C Code. Nucl. Sci. Technol. 28(15), 1–8 (2017).
Kaur, P., Singh, K. J., Thakur, S., Singh, P. & Bajwa, B. S. Investigation of bismuth borate glass system modified with barium for structural and gamma-ray shielding properties. Spectrochim. Acta A 206, 367–377 (2019).
Article ADS CAS Google Scholar
Issa, S. A. M., Saddeek, Y. B., Sayyed, M. I., Tekin, H. O. & Kilicoglu, O. Radiation shielding features using MCNPX code and mechanical properties of the PbO-Na2O-B2O3-CaO-Al2O3-SiO2 glass systems. Composites B 167, 231–240 (2019).
Abo-El-Enein, S. A., El-Hosiny, F. I., El-Gamal, S. M. A., Amin, M. S. & Ramadan, M. Gamma radiation shielding, fire resistance and physicochemical characteristics o Portland cement pastes modified with synthesized Fe2O3 and ZnO nanoparticles. Constr. Build. Mater. 173, 687–706 (2018).
Dong, M. et al. The potential use of boron containing resources for protection against nuclear radiation. Radiat. Phys. Chem. 188, 109601 (2021).
Gao, H., Wang, C., Yang, Z. & Zhang, Y. 3D porous nickel metal foam/polyaniline heterostructure with excellent electromagnetic interference shielding capability and superior absorption based on pre-constructed macroscopic conductive framework. Compos. Sci. Technol. 213, 108896 (2021).
Zhang, Y. et al. Construction of natural fiber/polyaniline core-shell heterostructures with tunable and excellent electromagnetic shielding capability via a facile secondary doping strategy. Composites A 137, 105994 (2020).
Zhang, Y., Pan, T. & Yang, Z. Flexible polyethylene terephthalate/polyaniline composite paper with bending durability and effective electromagnetic shielding performance. Chem. Eng. J. 389, 124433 (2020).
Zhang, Y., Qiu, M. N., Yu, Y., Wen, B. Y. & Cheng, L. L. A novel polyaniline-coated bagasse fiber composite with core-shell heterostructure provides effective electromagnetic shielding performance. ACS Appl. Mater. Interfaces 9(1), 809–818 (2017).
Akman, F., Kaçal, M. R., Almousa, N., Sayyed, M. I. & Polat, H. Gamma-ray attenuation parameters for polymer composites reinforced with BaTiO3 and CaWO4 compounds. Prog. Nucl. Energy 121, 103257 (2020).
Halimah, M. K., Azuraida, A., Ishak, M. & Hasnimulyati, L. Influence of bismuth oxide on gamma radiation shielding properties of borotellurite glass. J. Non-Cryst. Solids 512, 140–147 (2019).
Article ADS CAS Google Scholar
Yılmaz, S. N., Güngör, A. & Özdemir, T. The investigations of mechanical, thermal and rheological properties of polydimethylsiloxane/bismuth (III) oxide composite for X/gamma ray shielding. Radiat. Phys. Chem. 170, 108649 (2020).
Verdipoor, K., Alemi, A. & Mesbahi, A. Photon mass attenuation coefficients of asilicon resin loaded with WO3, PbO, and Bi2O3 micro and nano-particles for radiation shielding. Radiat. Phys. Chem. 147, 85–90 (2018).
Article ADS CAS Google Scholar
Noor Azman, N. Z., Siddiqui, S. A., Hart, R. & Low, I. M. Effect of particle size, filler loadings and X-ray tube voltage on the transmitted X-ray transmission in tungsten oxide-epoxy composites. Appl. Radiat. Isot. 71, 62–67 (2013).
Pavlenko, V. I., Cherkashina, N. I. & Yastrebinsky, R. N. Synthesis and radiation shielding properties of polyimide/Bi2O3 composites. Heliyon 5, e01703 (2019).
Holynska, B. Study of the effect of grain size heterogeneity in the X-ray absorption analysis of simulated aqueous slurries. Spectrochim. Acta 27, 237 (1972).
Article ADS CAS Google Scholar
AsariShik, N. & Gholamzade, L. X-ray shielding performance of the EPVC composites with micro- or nanoparticles of WO3, PbO or Bi2O3. Appl. Radiat. Isot. 139, 61–65 (2018).
Li, R. et al. The effect of particle size on gamma radiation shielding properties of gadolinium oxide dispersed epoxy resin matrix composite. Mater. Res. Express 4, 35035 (2017).
El-Khatib, A. et al. Gamma attenuation coefficients of nano cadmium oxide/high density polyethylene composites. Sci. Rep. 9, 16012 (2019).
Zakaly, H. et al. Role of novel ternary nanocomposites polypropylene in nuclear radiation attenuation properties: In-depth simulation study. Radiat. Phys. Chem. 188, 109667 (2021).
El-Sharkawy, R. M., Allam, A. E. A., El-Taher, E. R., El Sayed Massoud, E. & Mahmoud, M. E. Synergistic effects on gamma-ray shielding by novel light-weight nanocomposite materials of bentonite containing nano Bi2O3 additive. Radiat. Phys. Chem. 188, 109667 (2021).
McAlister, R. D. Gamma Ray Attenuation Properties of Common Shielding Materials 9–14 (PG. Research Foundation, 2013).
Hubbel, J. H. & Seltzer, S. M. Tables of X-ray Mass Attenuation Coefficient and Mass Energy Absorption Coefficients 1 keV to 20 KeV for Elements Z = 1 to Z = 92 and 48 Additional Substances of Dosimetric Interest 630 (National Institute of Standards and Physics laboratory, 1995).
Elsafi, M., Sayyed, M. I., Almuqrin, A. H., Gouda, M. M. & El-Khatib, A. M. Analysis of particle size on mass dependent attenuation capability of bulk and nanoparticle PbO radiation shields. Results Phys. 26, 104458 (2021).
Rinard, P. M. Passive Nondestructive Assay of Nuclear Materials 357–378 (United States Nuclear Regulatory Commission, 1991).
Lee, J., Fan, H., Chen, J. & Liu, L. Synthesis and characterization of poly(vinyl pyrrolidone)-capped bismuth nanospheres. Colloids Surf. A 340(1–3), 66–69 (2009).
Al-Hadeethi, Y., Sayyed, M. I., Barasheed, A. Z., Ahmed, M. & Elsafi, M. Fabrication of lead free borate glasses modified by bismuth oxide for gamma ray protection applications. Materials 15(3), 789 (2022).
Article ADS CAS Google Scholar
El-Nahal, M. A. et al. Understanding the effect of introducing micro- and nanoparticle bismuth oxide (Bi2O3) on the gamma ray shielding performance of novel concrete. Materials 14(21), 6487 (2021).
Article ADS CAS Google Scholar
Elsafi, M. et al. Investigation of photon radiation attenuation capability of different clay materials. Materials 14(21), 6702 (2021).
Article ADS CAS Google Scholar
Aloraini, D. A. et al. Experimental investigation of radiation shielding competence of Bi2O3-CaO-K2O-Na2O-P2O5 glass systems. Materials 14(17), 5061 (2021).
Article ADS CAS Google Scholar
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Physics Department, Faculty of Science, Alexandria University, Alexandria, 21511, Egypt
M. Elsafi & M. I. Abbas
Department of Environmental Studies, Institute of Graduate Studies and Research, Alexandria University, Alexandria, Egypt
MA El-Nahal & IH Saleh
Department of Physics, Faculty of Science, Isra University, Amman, Jordan
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
Wrote the main manuscript text: M.E., M.I.S. and M.A.E.-N. Conceptualization: I.H.S. and M.I.A. Sofware: M.E. and M.I.S. prepared figures: M.A.E.-N. supervision: M.I.A. project administration: M.I.S. All authors reviewed the manuscript.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Elsafi, M., El-Nahal, M.A., Sayyed, M.I. et al. Novel 3-D printed radiation shielding materials embedded with bulk and nanoparticles of bismuth. Sci Rep 12, 12467 (2022). https://doi.org/10.1038/s41598-022-16317-w
DOI: https://doi.org/10.1038/s41598-022-16317-w
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
![Novel 3-D printed radiation shielding materials embedded with bulk and nanoparticles of bismuth | Scientific Reports](http://kehu02.grofrom.com/www.sailray-tube.com/a7f937c38424403ca55d45ee78310c7e.jpg)
Wedge Filter Radiography Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.