Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 14, Article number: 5319 (2024 ) Cite this article oil seal 1728
This study investigates the impact of high-pressure hydrogen gas exposure on the structural and morphological characteristics of O-ring materials. O-ring specimens undergo two cycles of sealing under 70 MPa hydrogen gas, and their resulting variations are examined using advanced characterization techniques, including powder X-ray diffraction (PXRD), small-angle X-ray scattering (SAXS), scanning electron microscopy (SEM) and atomic force microscopy (AFM). Our findings reveal that the lattice parameters of the O-ring material show no significant changes when exposed to 70 MPa hydrogen gas. However, in the micrometre range, the formation of a hierarchical channel morphology becomes evident. This morphology is accompanied by the separation of carbon black filler from the rubber matrix, contributing to mechanical weakening of the O-ring. These observations can be attributed to the pressure gradient that develops between the inner and outer radii of the O-ring, resulting from compression forces acting perpendicularly to the radial direction due to clamp locking.
The urgency of the climate crisis has surpassed initial expectations, presenting a global challenge accelerating at an unprecedented pace. In response, human efforts are resolutely focused on achieving carbon neutrality through diverse initiatives1. A critical step in this pursuit is reducing carbon dioxide emissions2 from internal combustion engines3, with a notable strategy involving the shift to electric or hydrogen fuel cell vehicles4,5. While the transition to electric vehicles progresses smoothly, the challenge of reducing charging times remains a significant obstacle.
Hydrogen fuel cell vehicles4,6 offer environmental benefits, using eco-friendly hydrogen as fuel, contributing to air purification, and generating only water as a byproduct. However, ongoing debates persist about psychological resistance to safety issues during the expansion of hydrogen infrastructure7. Concerns also linger regarding the environmental impact of hydrogen production and the efficacy of carbon dioxide reduction. Addressing these technological and psychological challenges is crucial for implementing these solutions across terrestrial, maritime, and aerial transportation.
Currently, hydrogen fuel cell vehicles in the market use hydrogen dispensers at gas stations, storing hydrogen at a pressure of 90 MPa. The type-4 pressure vessel in these vehicles has a maximum pressure of 70 MPa, with O-rings primarily composed of rubber composites serving as the primary means to seal the hydrogen gas pressure8,9. The O-ring consists of polymer matrices, including cross-linked rubbers or amorphous fluoroelastomers, along with additives like carbon black and plasticizers. When an O-ring seals H2 gas, its effectiveness degrades over time due to cyclic pressure and temperature variations during the pressurization and depressurization process10,11,12. Eventually, the O-ring fails to maintain a proper seal9,13,14.
The mechanical damage to rubber O-rings caused by hydrogen gas includes blister fracture, overflow fracture, and buckling fracture15. At the microscopic level, hydrogen gas dissolved in polymer materials can form micro-sized clusters, known as hydrogen gas clustering. During depressurization, these clusters can coalesce to create hydrogen gas bubbles, gradually expanding over time after depressurization9,16,17. This expansion exerts stress, serving as blister initiation points. Research supports evidence of bubble formation and expansion, with the potential for cutting polymer chains during blister formation confirmed through studies introducing side-chain molecules with fluorescent characteristics18.
Ongoing studies aim to comprehensively understand the mechanical and chemical changes9,19 during hydrogen gas depressurization. To address this issue, the development of polymeric materials that exhibit long-term durability and the exploration of new processing routes for manufacturing mechanically superior polymers and composites are crucial15.
Previous research efforts have primarily focused on investigating rubber composites exposed to ambient H2 pressure20,21,22,23,24,25. However, in practical engineering applications, the O-ring seal encounters an outward H2 pressure gradient, spanning from high pressure at the inner radius to low pressure at the outer radius. Additionally, the O-ring is subjected to mechanical confinement due to normal uniaxial forces acting perpendicular to the radial direction26. Consequently, conducting studies that specifically examine the behaviour and deterioration mechanisms of polymeric materials in the context of O-ring usage in engineering practice is crucial.
PXRD analysis was performed to investigate any changes in the lattice spacing of the polymer matrix after exposure to H2 at a pressure of 70 MPa. Figure 1 presents the PXRD results obtained for the O-ring specimens before and after exposure to H2.
(a) PXRD data obtained for the O-ring before and after exposure to H2 at a pressure of 70 MPa. The names displayed at the peak positions represent the origin of each peak, while the Arabic sequences at the peak positions indicate the Miller indices for the peaks derived from Ca(OH)2. (b) SEM image of the O-ring showing a black background representing the rubber composite with the carbon black filler and white cube-like crystals indicating Ca(OH)2. The inset figure displays the EDS spectrum of the Ca(OH)2 crystal located at the uppermost position, labeled as spectrum.
The XRD patterns exhibit three broad peaks at approximately 2θ ≈ 17°, 25°, and 42°, as well as seven sharp peaks at 2θ values of 28°, 34°, 47°, 51°, 54°, 63°, and 65°. Among the broad peaks, the one at 2θ ≈ 25° is attributed to the presence of carbon black inclusions27,28,29, while the peak at 2θ ≈ 17° corresponds to the conventionally observed amorphous phase for polymers30. The peak at 2θ ≈ 42° is likely a second harmonic of the 2θ ≈ 25° peak. The seven sharp peaks observed may be indicative of an unknown crystalline phase within the O-ring. However, since the O-ring is reported to be an FKM copolymer consisting of VDF/HFP = 76.1/23.9 mol% (VDF: vinylidene fluoride (CF2=CH2); HFP: hexafluoropropylene (CF2=CF(CF3)))31, the presence of a crystalline phase is not expected. Therefore, the seven sharp peaks are attributed to another inorganic material rather than the polymer itself. In our case, the peaks are well matched with the Miller indices of Ca(OH)232,33 in ICDD(International Centre for Diffraction Data) card number of 00-074-0733, and this is further confirmed by the FE-SEM image32 shown in the inset picture in Fig. 1. In result, the XRD pattern analysis identified three primary influencing factors. Firstly, the sharp peaks were attributed to Ca(OH)2, supported by provided Miller indices. The second peak (2θ ≈ 25°) corresponds to carbon black inclusion within the sample, while the third peak (2θ ≈ 17°) is associated with entangled rubber polymer chains. Apart from these peaks, no significant variations are observed in the 2θ positions and intensities after exposure to H2, indicating no change in the lattice parameters of the polymer matrix34.
Subsequently, we conducted SAXS measurements to meticulously monitor and analyse the structural variations covering from a few nanometers to a hundred nanometer. Figures 2 and 3 depict the SAXS data obtained at room temperature and 80 °C before and after, respectively, exposure to H2 at a pressure of 70 MPa. Each SAXS profile exhibits the typical scattering patterns from aggregates. For data analysis, the following equations were applied35,36,37,38,39:
where F(q) represents the form factor of a solid sphere, Iagg(q) is a structure factor used to describe an aggregate, and Ib represents the experimental background. The Rc term in the form factor is the core radius, and Rg in the aggregate structure factor is the radius of gyration of an aggregate. G and B are constants, and P is a power law exponent used to describe the dimensionality of an aggregate (e.g., P = 1 for a rod, P = 2 for a disk, P = 4 for a sphere). Additionally, the form factor F(q) is convoluted with the Schulz size distribution to describe the size distribution of the carbon black (CB) particles, considering the observed presence of CB inclusion in the SEM image in Fig. 1b.
SAXS data for the O-ring collected at room temperature (upper) and 80 °C (lower) before being exposed to H2 at a pressure of 70 MPa. The black solid lines represent the fits to Eq. (1).
SAXS data for the O-ring collected at room temperature (upper) and 80 °C (lower) after being exposed to H2 at a pressure of 70 MPa. The black solid lines represent the fits to Eq. (1).
In Figs. 2 and 3, the experimental data are presented alongside the data fits (black solid lines) generated using Eq. (1). To analyse the experimental data obtained before and after exposure to H2, the fit parameters derived from the room-temperature measurements, namely, the core radius and size distribution of the core radius, were employed for the analysis of the data collected at 80 °C. This approach ensures a reliable fit by fixing the core radius and size distribution parameters based on the room-temperature measurements while allowing the other parameters (Rg, P, G and B) to vary during the fitting process for the 80 °C measurements.
Figure 4 illustrates the resulting size distributions, and the corresponding fit parameters can be found in Table 1. In the room-temperature measurements, the core radii (Rc) of the H2-exposed O-ring is clearly slightly smaller than that of the fresh O-ring. However, the polydispersity index (p.d.i.), as shown in Fig. 4 and Table 1, increases after exposure to H2. Furthermore, the radius of gyration (Rg) of the H2-exposed O-ring, which represents the size of the average aggregate, is approximately 1 nm smaller than that of the fresh O-ring. This suggests that the size of CB aggregates decreases after exposure to H2. The dimensionality of the aggregates, represented by P, shows a slight increase from 3.02 to 3.05, indicating a tendency towards a more spherical shape after exposure to H2. Similar trends are observed in the data obtained at 80 °C.
Size distribution of the core radii at room temperature for O-ring specimens before (red) and after (blue) exposure to 70 MPa hydrogen gas. The y-axis represents the size distribution, denoted n(r), and is presented in arbitrary units.
AFM was employed to investigate the morphological changes at the nanometre scale in the O-ring after being exposed twice to hydrogen at a pressure of 70 MPa. AFM images were acquired from three distinct surfaces, as illustrated in Fig. 5.
Three different surface areas used for measuring the surface roughness: (a) cross-sectional cutting surface, (b) outer-radius surface and (c) slice cutting surface.
Figure 6 displays the AFM images obtained from the outer-radius surface of the O-ring. Before exposure to H2 (Fig. 6a), a periodic modulation of finite height and width is observed in the cross-sectional plane direction. However, this periodic modulation becomes blurred and merged after exposure to H2 (Fig. 6b). Additionally, the morphological roughness, indicated by the colour contrast (white, gold, brown and black), becomes more pronounced and defined. The lighter and darker colours correspond to higher and lower topographies, respectively.
AFM images captured on the outer-radius surface of the O-ring: (a) Image taken before exposure to H2 at a pressure of 70 MPa. (b) Image taken after two exposures to H2 at a pressure of 70 MPa. (c) Representative image displaying the rupture of the O-ring composite caused by the outburst of H2 gas along the radial direction of the O-ring. The illustration positioned in the top-left corner of (a) indicates the surface area scanned by the AFM tip.
In particular, the areas corresponding to white and black colours are expanded. These phenomena can be explained by considering both the compression stress exerted in the upward and downward directions of the cross-section and the overflow effect due to the H2 pressure gradient in the radial direction. The compression stress normal to the radial plane causes the O-ring to strain into an ellipsoidal form, resulting in a smaller distance for the periodic circumferential morphology. At the same time, H2 molecules are expected to undergo sequential processes of absorption, diffusion, and permeation through the O-ring, as a hydrogen pressure gradient is established in the inner to outer radial direction. These processes are known to induce swelling, overflow, and fracture of the O-ring composites. To facilitate the merging of the periodic circumferential morphology, narrowing of the periodic morphology due to compression stress and outward displacement of a part of the O-ring composites induced by the pressure gradient must occur simultaneously.
Figure 6c effectively illustrates this outward displacement phenomenon. The region around the black-coloured hole located immediately below the centre of the image protrudes out, forming a bundle of cusps in the outer radial direction, indicating that H2 gas burst out through the hole. Naturally, a circular morphology should be observed beneath the hole when the O-ring specimen is imaged on a slice cutting surface.
When analysing the surface roughness, the cross-sectional cutting and slice cutting surfaces are not scientifically meaningful due to the artificial effects introduced during the cutting process. However, the outer-radius surface retains the direct effects associated with the hydrogen discharge process, making it highly useful for surface roughness analysis. Therefore, a comparison of the surface roughness before and after hydrogen exposure was conducted solely based on the outer-radius surface. In this comparison, two-dimensional AFM images of the O-ring were first corrected using a plane correction process to account for the cylindrical shape of the O-ring. The average roughness value (Sa) was then measured within a 3 × 3 μm2 area to mitigate errors introduced by the cylindrical shape of the O-ring. The roughness of each group was assessed across more than 100 distinct regions, as depicted in Fig. 7a. The line profile depicts the height variation of the magnified surface image along a white line, from which the surface roughness value is derived (Fig. 7b).
(a) A representative illustration showing a sector outlined by a white rectangular box among 100 distinct regions used to calculate surface roughness from the outer surface area. (b) Height profiles obtained along the X-direction within the white rectangular box. (c) Roughness distributions obtained from the outer surface of the O-ring before (upper) and after (lower) exposure to H2 at a pressure of 70 MPa. (d) The resulting average roughness before and after exposing the O-ring to 70 MPa of H2 gas.
Figure 7c illustrates the roughness distributions of the outer-radius surface before and after exposure to H2 at a pressure of 70 MPa. Prior to H2 exposure, the roughness exhibited a single Gaussian distribution40,41. However, after exposure to H2 at a pressure of 70 MPa, a tailing distribution emerged in the high roughness region, as depicted by the blue dashed rectangular box in Fig. 7c. In other words, the low roughness region followed a Gaussian distribution, indicating a random surface roughness associated with random fracturing. In contrast, the high roughness region did not conform to a Gaussian distribution but showed a tailing distribution, suggesting the absence of random fracturing. The averaged roughness also increased by H2 exposure (Fig. 7d).
This phenomenon is believed to be related to H2 exposure. The increase in roughness primarily results from the expansion of the fracture surface area during crack propagation, leading to increased roughness on the fracture surface. Furthermore, the roughness is broadened after exposure to hydrogen at a pressure of 70 MPa.
Figure 8 presents a circular morphology on the slice cutting surface. Before exposure to H2 (Fig. 8a), the AFM images do not display any circular morphology; they only show bright spots with a gold colour. However, after exposure to H2 at a pressure of 70 MPa, numerous circles with a bright gold colour emerge, surrounding dark brown channels (indicated by green arrows in Fig. 8b). These dark brown channels are believed to correspond to pathways for H2 gas diffusion in the radial direction of the O-ring, while the bright gold circles (indicated by white arrows in Fig. 8b) mark the periphery of these channels. Interestingly, the channel-like patterns are also directly observable in the AFM images of the cross-sectional cutting surface.
AFM images obtained from the slice cutting surfaces of the O-ring (a) before and (b) after exposure to H2 at a pressure of 70 MPa.
As depicted in Fig. 9, no channel-like morphology is present on the cross-sectional cutting surface before exposure to H2 (Fig. 9a). However, after exposure to H2, a channel-like morphology becomes evident in the AFM image (Fig. 9b), with an average width of approximately 1.9 nm (± 0.76 nm).
AFM morphologies obtained from the cross-sectional cutting surface of the O-ring (a) before and (b) after exposure to H2 at a pressure of 70 MPa.
Further evidence of the channel morphology can be observed in Fig. 10 obtained using SEM. Upon exposure to H2, the formation of channel structures becomes apparent. In the SEM image of the cryo-fracture surface of the O-ring without H2 exposure (Fig. 10a), no specific directional pattern is observed in the morphology. However, in the SEM image of the O-ring subjected to H2 at a pressure of 70 MPa (Fig. 10b), a clear hierarchical development of channel structures is visible on the cryo-fracture surface. This can be observed within the rectangular red box located at the lower left of Fig. 10b. The left and right sides of Fig. 10b represent the inner and outer radial parts of the O-ring cutting plane, respectively. Under the condition of a H2 pressure of 70 MPa, the outer radial side of the O-ring is exposed to atmospheric pressure (0.1 MPa), while the left inner radial side of the cryo-fracture surface is subjected to H2 at a pressure of 70 MPa. Considering the O-ring thickness of 5.7 mm, the pressure difference per unit thickness can be calculated to be approximately 12 MPa/mm (or 12 GPa/m). The pressure difference between the inner and outer sides of the O-ring is significant, causing expansion of the O-ring. This expansion can lead to tearing due to the tensile stress experienced by the FKM composite, which typically ranges up to approximately 30 MPa.
SEM images of the cryo-fracture surface of the O-ring (a) before and (b) after exposure to H2 at a pressure of 70 MPa. (c) Enlarged view in 3-dimensional mode of the highlighted area indicated by the red rectangular box.
Furthermore, when the O-ring is constrained by a mechanical force, the blooming phenomenon predominantly occurs in the outer radial direction. As a result, the O-ring undergoes uniaxial directional cavitation. The observed damage patterns, characterized by hierarchically ordered channels, as shown in Fig. 10b,c, do not indicate isotropic cavitation induced by depressurization.
Within the channels, another notable phenomenon becomes apparent. Figure 11 presents an SEM image that captures the channels and reveals the presence of small black hollows within the channel interiors and in their surrounding areas. These hollows are marked with red circles (or ellipses) and numbered from #1 to #6. The structures resembling spherical particles observed within the channels represent CB fillers, while the background corresponds to the matrix consisting of rubber molecules. The fillers can be observed in both aggregated and primary forms. Importantly, note that these structures within the channels were not formed as a result of the cryo-fracture process, but rather, they were already present due to the hydrogen depressurization.
SEM image of the inside of a channel, showing the separation of CB fillers from the rubber matrix. Red circles and ellipses highlight representative examples of filler separation. Bilateral blue arrows indicate the corresponding counterparts of the hollows in the rubber matrix and their corresponding fillers. The symbols "#" and Arabic numbers are used to identify the pairs of rubber matrix hollows and fillers.
The red circles (or ellipses) labelled #1 to #6 represent three distinct types of separated pair structures of the hollows and their corresponding fillers. These separations correspond to the initial stage of filler separation from the rubber matrix (#1), single filler separation (#2, #3 and #4), and separation of filler aggregates (#5, #6)42. In the case where separation has just begun (#1), the filler aggregates are observed to be partially detached from the polymer matrix, providing strong evidence of their separation10. The filler aggregates partially protrude, creating holes in the rubber matrix where the fillers have been removed. In the case of single filler separation (#2, #3 and #4), the portion of the rubber matrix from which the filler left, indicated by blue arrows, exhibits a smaller hollow structure than the corresponding filler itself. This can be attributed to the elastic restoration of the rubber matrix. However, the filler aggregates (#5, #6) do not exhibit similar behaviour, as they have undergone a wider range of separation, leaving insufficient time for the disrupted structure to restore itself. Specifically, the black hollows and the corresponding CB fillers of #2, #3 and #6 are positioned on the nearly perpendicular opposite sides of the deepest valley. Furthermore, the distances between the separated CB fillers and the rubber matrix inside the channel (#2, #3, #6) are greater than the distances between the separated CB fillers and the rubber matrix outside the channel (#1, #4, #5). This observation strongly suggests that the separation between the fillers and rubber matrix occurred during the formation of the channel. If this observation holds true, then it implies that the CB fillers are not fully embedded within the polymer matrix but rather partially exposed. Consequently, the fillers cannot effectively bind with the polymer matrix, resulting in loss of their intended functionality.
In summary, exposure to hydrogen gas at 70 MPa does not significantly affect the lattice parameters of the O-ring material. However, in the range of micrometres, the formation of a hierarchical channel morphology becomes evident. This channel formation process is accompanied by the separation of fillers from the rubber matrix, leading to mechanical failure.
This phenomenon can be explained by the pressure gradient established between the inner and outer radii of the O-ring under the compression pressure perpendicular to the radius due to clamp locking. Typically, the application and release of hydrogen pressure in a simulated ambient H2 pressure environment are carried out under surrounding ambient pressure conditions. This results in the formation of voids uniformly in all directions during the depressurization process.
However, in real operating conditions, the O-ring is mechanically constrained perpendicular to its diameter, leading to a pressure gradient between the inner and outer sides of the O-ring. As a consequence, the voids formed in the O-ring during actual usage encounter difficulties in expanding uniformly. Consequently, the expansion process is more likely to occur in an anisotropic manner along the radial direction, even though the expansion volume remains the same as that observed in isotropic expansion.
The O-ring material used in this study was commercially available (VEA1049-12 O-ring P112, PRETECH CO. LTD., Japan). The O-ring specimen (thickness: 5.7 mm) was subjected to two cycles of sealing with high-pressure hydrogen gas at 70 MPa. After this exposure, the O-ring experienced a loss in its sealing performance.
Powder X-ray diffraction (PXRD) analysis was conducted using a model X’pert Pro X-ray diffractometer (PANalytical Co., Netherlands). The X-ray generator was set to 30 mA and 40 kV, with a receiving slit size of 0.300 mm. The O-ring sample was placed on the goniometer, and a 2θ Bragg angle scan was performed from 10.0100° to 79.9900° with a step size of 0.0200° and a measurement time of 1 s at room temperature.
Small-angle X-ray scattering (SAXS) experiments were carried out at the 4C SAXS II beamline of the Pohang Light Source II (PLS II). Monochromatic X-rays with a wavelength (λ) of 0.7560 Å were used. The beam path was maintained under vacuum to minimize air scattering, and the sample-to-detector distance was 4 m. A two-dimensional charge-coupled detector (Mar USA, Inc.) was used, and the samples were directly placed on the sample holder. The two-dimensional scattered intensity was azimuthally averaged to obtain the one-dimensional intensity as a function of q, covering a q range of 0.007 < q (Å−1) < 0.14. The raw data were corrected for detector noise, background scattering, and transmission. The experiments were conducted at both room temperature and 80 °C, and the SAXS intensity was not converted to absolute intensity. The temperature was controlled using a Eurotherm, and the heating rate was approximately 10 K/min. For the measurements at 80 °C, the sample was kept at this temperature for two minutes before the measurements were performed. The measurement time was 3 s for room temperature and 2 s for the 80 °C measurements.
The SAXS data were fitted to Eq. (1) in the manuscript, where Rc represents the core radius derived from the solid sphere form factor, and p.d.i. signifies the size distribution of the core radius, as implemented in the Schulz-Zimm distribution function. It's crucial to note that the Rc value was computed under the condition that the background value is not treated as a fitting parameter but is fixed at zero. In fact, the background itself, particularly near the high q maximum, exhibits noise, a detail that was evident in our data but not explicitly visible in the log–log plot. Furthermore, it is accurate that the core radius obtained from the fit closely aligns with the maximum high q. In response to this, we attempted to concentrate the fit on the low q range of the solid sphere form factor, which typically reveals an oscillating pattern in the form factor. The standard deviation for both Rc and Rg was determined as the fit error from the function incorporated into the NIST SANS package. This fit error was cross-verified by fixing one fit parameter while allowing others to vary within the program.
Field emission-scanning electron microscopy (FE-SEM) images were acquired using a Hitachi S-4800 microscope operating at 15 kV and 5.1 μA at room temperature. The imaging mode used was mixed lower–upper mode.
Atomic force microscopy (AFM) was performed to examine the morphology of the O-ring using a NANO Station II instrument (Surface Imaging Systems, Herzogenrath, Germany). The AFM system consisted of an AFM scanner with dimensions of 92.5 × 92.5 × 6.0 µm3 in the x, y, and z directions and a Zeiss optical microscope (Epiplan 500×). A TS-150 active vibration isolation table (S.I.S., Herzogenrath, Germany) was used to reduce the noise signals from vibrations. The surface images were acquired in noncontact mode with a scan resolution of 512 × 512 pixels and a scan speed of 0.7 line/s. The AFM probe used consisted of a force-sensing or -imposing cantilever with a silicon material, a spring constant of 0.2 N/m (± 0.15 N/m), a length of 450 µm (± 10 µm), a width of 30 µm, and a thickness of 2 µm (± 1 µm). The tip used had a radius of 5–6 nm and a height of 14 µm (± 2 µm).
The datasets generated and/or analyzed during the current study are available from the corresponding author on reasonable request.
Intergovernmental Panel on Climate Change. Climate Change 2022—Impacts, Adaptation and Vulnerability: Working Group II Contribution to the Sixth Assessment Report of the Intergovernmental Panel on Climate Change (Cambridge University Press, 2023).
Peters, G. P. et al. Rapid growth in CO2 emissions after the 2008–2009 global financial crisis. Nat. Clim. Change 2, 2–4. https://doi.org/10.1038/nclimate1332 (2012).
Article ADS CAS Google Scholar
Funk, J. L. IT and sustainability: New strategies for reducing carbon emissions and resource usage in transportation. Telecommun. Policy 39, 861–874. https://doi.org/10.1016/j.telpol.2015.07.007 (2015).
Selmi, T., Khadhraoui, A. & Cherif, A. Fuel cell-based electric vehicles technologies and challenges. Environ. Sci. Pollut. Res. 29, 78121–78131. https://doi.org/10.1007/s11356-022-23171-w (2022).
Gajanayake, S., Thilakshan, T., Sugathapala, T. & Bandara, S. 2020 Moratuwa Engineering Research Conference (MERCon) 494–498.
Alvarez-Meaza, I., Zarrabeitia-Bilbao, E., Rio-Belver, R. M. & Garechana-Anacabe, G. Fuel-cell electric vehicles: Plotting a scientific and technological knowledge map. Sustainability 12, 2334 (2020).
Osman, A. I. et al. Hydrogen production, storage, utilisation and environmental impacts: A review. Environ. Chem. Lett. 20, 153–188. https://doi.org/10.1007/s10311-021-01322-8 (2022).
Balasooriya, W., Clute, C., Schrittesser, B. & Pinter, G. A review on applicability, limitations, and improvements of polymeric materials in high-pressure hydrogen gas atmospheres. Polym. Rev. 62, 175–209. https://doi.org/10.1080/15583724.2021.1897997 (2022).
Zheng, Y. R. et al. A review on effect of hydrogen on rubber seals used in the high-pressure hydrogen infrastructure. Int. J. Hydrog. Energy 45, 23721–23738. https://doi.org/10.1016/j.ijhydene.2020.06.069 (2020).
Briscoe, B. J., Savvas, T. & Kelly, C. T. “Explosive decompression failure” of rubbers: A review of the origins of pneumatic stress induced rupture in elastomers. Rubber Chem. Technol. 67, 384–416. https://doi.org/10.5254/1.3538683 (1994).
Ono, H., Nait-Ali, A., Diallo, O. K., Benoit, G. & Castagnet, S. Influence of pressure cycling on damage evolution in an unfilled EPDM exposed to high-pressure hydrogen. Int. J. Fracture 210, 137–152. https://doi.org/10.1007/s10704-018-0266-y (2018).
Castagnet, S., Mellier, D., Nait-Ali, A. & Benoit, G. In-situ X-ray computed tomography of decompression failure in a rubber exposed to high-pressure gas. Polym. Test. 70, 255–262. https://doi.org/10.1016/j.polymertesting.2018.07.017 (2018).
Yamabe, J., Koga, A. & Nishimura, S. Failure behavior of rubber O-ring under cyclic exposure to high-pressure hydrogen gas. Eng. Fail. Anal. 35, 193–205. https://doi.org/10.1016/j.engfailanal.2013.01.034 (2013).
Zhou, C. L., Chen, G. H., Xiao, S., Hua, Z. L. & Gu, C. H. Study on fretting behavior of rubber O-ring seal in high-pressure gaseous hydrogen. Int. J. Hydrog. Energy 44, 22569–22575. https://doi.org/10.1016/j.ijhydene.2019.02.224 (2019).
Koga, A. et al. In International Hydrogen Conference (IHC 2012): Hydrogen-Materials Interactions (eds Somerday, B. P. & Sofronis, P.) (ASME Press, 2014).
Kulkarni, S. S. et al. Damage evolution in polymer due to exposure to high-pressure hydrogen gas. Int. J. Hydrog. Energy 46, 19001–19022. https://doi.org/10.1016/j.ijhydene.2021.03.035 (2021).
Ono, H., Fujiwara, H., Onoue, K. & Nishimura, S. Influence of repetitions of the high-pressure hydrogen gas exposure on the internal damage quantity of high-density polyethylene evaluated by transmitted light digital image. Int. J. Hydrog. Energy 44, 23303–23319. https://doi.org/10.1016/j.ijhydene.2019.07.035 (2019).
Morelle, X. P., Sanoja, G. E., Castagnet, S. & Creton, C. 3D fluorescent mapping of invisible molecular damage after cavitation in hydrogen exposed elastomers. Soft Matter 17, 4266–4274. https://doi.org/10.1039/D1SM00325A (2021).
Article ADS CAS PubMed Google Scholar
Kim, M. & Lee, C. H. Hydrogenation of high-density polyethylene during decompression of pressurized hydrogen at 90 MPa: A molecular perspective. Polymers-Basel 15, 2880 (2023).
Article ADS CAS PubMed PubMed Central Google Scholar
Yamabe, J. & Nishimura, S. Influence of fillers on hydrogen penetration properties and blister fracture of rubber composites for O-ring exposed to high-pressure hydrogen gas. Int. J. Hydrog. Energy 34, 1977–1989. https://doi.org/10.1016/j.ijhydene.2008.11.105 (2009).
Fujiwara, H., Yamabe, J. & Nishimura, S. Evaluation, of the change in chemical structure of acrylonitrile butadiene rubber after high-pressure hydrogen exposure. Int. J. Hydrog. Energy 37, 8729–8733. https://doi.org/10.1016/j.ijhydene.2012.02.084 (2012).
Shen, M. X., Peng, X. D., Meng, X. K., Zheng, J. P. & Zhu, M. H. Fretting wear behavior of acrylonitrile-butadiene rubber (NBR) for mechanical seal applications. Tribol. Int. 93, 419–428. https://doi.org/10.1016/j.triboint.2015.09.029 (2016).
Ono, H., Fujiwara, H. & Nishimura, S. Penetrated hydrogen content and volume inflation in unfilled NBR exposed to high-pressure hydrogen—What are the characteristics of unfilled-NBR dominating them?. Int. J. Hydrog. Energy 43, 18392–18402. https://doi.org/10.1016/j.ijhydene.2018.08.031 (2018).
Jung, J. K. et al. H-2 uptake and diffusion characteristics in sulfur-crosslinked ethylene propylene diene monomer polymer composites with carbon black and silica fillers after high-pressure hydrogen exposure reaching 90 MPa. Polymers-Basel 15, 162. https://doi.org/10.3390/polym15010162 (2023).
Jung, J. K. et al. Correlations between H-2 permeation and physical/mechanical properties in ethylene propylene diene monomer polymers blended with carbon black and silica fillers. Int. J. Mol. Sci. 24, 2865. https://doi.org/10.3390/ijms24032865 (2023).
Article CAS PubMed PubMed Central Google Scholar
Yamabe, J., Fujiwara, H. & Nishimura, S. Fracture analysis of rubber sealing material for high pressure hydrogen vessel. J. Environ. Eng. 6, 53–68. https://doi.org/10.1299/jee.6.53 (2011).
Lee, S.-M., Lee, S.-H. & Roh, J.-S. Analysis of activation process of carbon black based on structural parameters obtained by XRD analysis. Crystals 11, 153 (2021).
Rao Penki, T., Kishore, N., Munichandraiah, B. & Shanmughasundaram, D. High rate capability of coconut kernel derived carbon as an anode material for lithium-ion batteries. Adv. Mater. Lett. 5, 184–190. https://doi.org/10.5185/amlett.2013.8530 (2014).
Darmstadt, H. et al. Solid state 13C-NMR spectroscopy and XRD studies of commercial and pyrolytic carbon blacks. Carbon 38, 1279–1287. https://doi.org/10.1016/S0008-6223(99)00259-6 (2000).
Ebert, L. B., Scanlon, J. C. & Mills, D. R. X-ray diffraction of n-paraffins and stacked aromatic molecules: Insights into the structure of petroleum asphaltenes. Liq. Fuels Technol. 2, 257–286. https://doi.org/10.1080/07377268408915353 (1984).
Lee, C. H., Jung, J. K., Jeon, S. K., Ryu, K. S. & Baek, U. B. Nuclear magnetic resonance study of o-ring polymer exposed to high-pressure hydrogen. J. Magn. 22, 478–482. https://doi.org/10.4283/Jmag.2017.22.3.478 (2017).
Ma, X. et al. The influence of calcium hydroxide crystal morphology on the desulfurization of cement kiln flue gas. J. Mater. Sci. 57, 18287–18297. https://doi.org/10.1007/s10853-022-07801-9 (2022).
Article ADS CAS Google Scholar
Zhang, H., Wang, W. B., Li, L. & Liu, J. P. Starch-assisted synthesis and characterization of layered calcium hydroxide particles. J. Inorg. Organomet. Polym. Mater. 28, 2399–2406. https://doi.org/10.1007/s10904-018-0895-7 (2018).
Sadeghtabaghi, Z., Rabbani, A. R. & Hemmati-Sarapardeh, A. A review on asphaltenes characterization by X-ray diffraction: Fundamentals, challenges, and tips. J. Mol. Struct. 1238, 130425. https://doi.org/10.1016/j.molstruc.2021.130425 (2021).
Takenaka, M. Analysis of structures of rubber-filler systems with combined scattering methods. Polym. J. 45, 10–19. https://doi.org/10.1038/pj.2012.187 (2013).
Mondal, T., Bhowmick, A. K., Ghosal, R. & Mukhopadhyay, R. Expanded graphite as an agent towards controlling the dispersion of carbon black in poly (styrene -co-butadiene) matrix: An effective strategy towards the development of high performance multifunctional composite. Polymer 146, 31–41. https://doi.org/10.1016/j.polymer.2018.05.031 (2018).
Manoharan, P. & Naskar, K. Biologically sustainable rubber resin and rubber-filler promoter: A precursor study. Polym. Adv. Technol. 28, 1642–1653. https://doi.org/10.1002/pat.4034 (2017).
Gundlach, N. & Hentschke, R. Modelling filler dispersion in elastomers: Relating filler morphology to interface free energies via SAXS and TEM simulation studies. Polymers-Basel 10, 446. https://doi.org/10.3390/polym10040446 (2018).
Article CAS PubMed PubMed Central Google Scholar
Genix, A. C., Baeza, G. P. & Oberdisse, J. Recent advances in structural and dynamical properties of simplified industrial nanocomposites. Eur. Polym. J. 85, 605–619. https://doi.org/10.1016/j.eurpolymj.2016.08.028 (2016).
Liu, Y., Li, J. F., Sun, S. Y. & Yu, B. Advances in Gaussian random field generation: A review. Comput. Geosci. 23, 1011–1047. https://doi.org/10.1007/s10596-019-09867-y (2019).
Carbonell, F. & Worsley, K. J. On the geometry of a generalized cross-correlation random field. Stat. Probab. Lett. 78, 3129–3134. https://doi.org/10.1016/j.spl.2008.05.033 (2008).
Menon, N. C. et al. in Proceedings of the ASME Pressure Vessels and Piping Conference Vol. 6b (2016).
We extend our gratitude to Dr. Min Hwan Jung for his invaluable assistance in facilitating the data collection process at the 4C SAXS II beamline of the Pohang Light Source II (PLS II). His expertise and support have been instrumental in our research endeavours, and we sincerely appreciate his contributions. This research was supported by Development of Reliability Measurement Technology for Hydrogen Refueling Station funded by Korea Research Institute of Standards and Science (KRISS-2024-GP2024-0010).
Department of Biochemical Engineering, Chosun University, Chosundae-5-gil, Dong-gu, Gwangju, 61452, Republic of Korea
Hydrogen Energy Materials Research Team, Korea Research Institute of Standards and Science, Daejeon, 34113, Republic of Korea
Department of Biomedical Engineering, College of Medicine, Kyung Hee University, Seoul, 02447, Republic of Korea
LG Chem Europe GmbH, Adolph-Prior-Straße 16, 65936, Frankfurt am Main, Germany
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
C.H.L. conducted XRD and SEM experiments, completed the draft of this paper, and engaged in discussions after consultation with Dr. J.K.J. and Dr. K.S.K. Dr. K.S.K. led the AFM measurements and initiated initial discussions of the data. Dr. J.K.J. commissioned this experiment, provided the necessary samples, supplied the results of the SAXS experiments, and offered the funds required for the experimentation. C.J.K. conducted and analyzed the SAXS experiment, and authored the corresponding sections of the manuscript.
Correspondence to Jae Kap Jung.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Lee, C.H., Jung, J.K., Kim, K.S. et al. Hierarchical channel morphology in O-rings after two cycling exposures to 70 MPa hydrogen gas: a case study of sealing failure. Sci Rep 14, 5319 (2024). https://doi.org/10.1038/s41598-024-55101-w
DOI: https://doi.org/10.1038/s41598-024-55101-w
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
silicone sealing gasket Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.