With rise in new orders and exports, future business outlook remains steady.
Contemplating how to continue offering chromic acid services in an increasingly stringent regulatory world? Liquid chrome products may be the solution you’re looking for. pure nickel tubing
Looking to upgrade your coating process and possibly invest in automation solutions? This helpful Ask the Expert article from Tom Brown of Carlisle Fluid Technologies offers advice for doing your research and working with your equipment supplier.
PF editor-in-chief Scott reflects on environmental responsibility in the wake of Hurricane Helene.
Best practices for racking parts in surface finishing operations.
As a former motorcycle manufacturer, this powder coating Top Shop benefits from understanding the finishing industry from a customer’s perspective.
Although useful, chromic acid and other compounds that contain hexavalent chromium ions are highly toxic and carcinogenic. However, one company has developed an alternative for the hard chrome process that achieves thick, conformal coatings with wear and fatigue resistance comparable or superior to hexavalent chromium-based systems.
This paper provides an overview of the parallels between the synthetic order established by non-equilibrium reactions, such as anodizing, which are nano-scale, and the natural order established by equilibrium reactions in nature, many of which are on the macro-scale.
Unavoidably interrupted by the SARS CoV-2 pandemic of 2020-21, this NASF-AESF Foundation research project report R-120 has been ongoing since April 2019. Now complete, this report is the final report, reflecting 16 quarters of work.
XRF is the go-to instrument for measuring electrolytic and electroless nickel coating thicknesses, however the technology does have limitations when it comes to measuring thick coatings. This helpful Ask the Expert article from Rob Weber of Fischer Technology explores several alternative methods.
The collaboration between Hubbard-Hall and Pavco brings together cutting-edge chemistry and extensive expertise to tackle common challenges in metal finishing, particularly for zinc (Zn) and Zn alloy plating. By leveraging the combined focus on innovation and efficiency, the team delivers practical approaches that help applicators elevate their processes, reduce costs and improve overall performance. In this webinar, the presenters will explore the synergistic effects of passivates and topcoats, revealing how they provide enhanced corrosion protection for Zn and Zn alloy plating. Together, these advances enhance the quality and durability of finishes and ensure long-term competitiveness in the marketplace. Agenda: Elevated performance Common issues addressed Innovative processes
XRF measurement of the layers is also important to assure the right color and appearance of the finished goods. Join Fischer as it discusses how XRF measurements can be used for process control, quality control and incoming inspection of electroplated jewelry pieces. Agenda: The high precision of XRF Cost-reduction benefits Getting reliable results in seconds Measuring multiple layers of plating thickness Calibrating for optimal performance
Any one of these three facets will help you become a stronger powder coater, but this session will walk you through all of them and provide details that will be most valuable on a quest to develop an optimal powder operation. Agenda: The good: introduction to powder coatings The bad: common challenges The ugly: debunking myths Best practices for optimal operations Case studies
Our focus includes the use of membrane filtration systems – which can recover up to 98% of cleaning solutions – dramatically reducing the volume of concentrated waste requiring disposal. Additionally, we delve into strategies for maximizing cleaner longevity by precisely adjusting oil concentrations, leveraging the direct relationship between cleaner concentration and effective oil content management. By adopting these methods, businesses can achieve significant cost savings through reduced chemical consumption, lower waste disposal expenses and decreased energy usage – all while promoting environmental sustainability. Agenda: Membrane Filtration Systems: Learn how these systems protect industrial assets and recover a substantial percentage of cleaning solutions. Cost-Saving Strategies: Discover opportunities for savings through extended cleaner longevity and reduced chemical waste Technical Cleanliness Challenges: Understand the various challenges in achieving and maintaining technical cleanliness across processes. Establish a more sustainable and cost-efficient cleaning program that delivers superior results, reduces downtime and minimizes environmental impact
Dive into plating bath optimization. Learn about the importance of chemistry measurement, various analysis methods and real-time monitoring benefits through X-ray fluorescence (XRF) analysis with insightful case studies highlighting efficiency gains. Join Fisher Technology's Devarsh Shah and Melissa Agneta as they discuss how to improve plating efficiency by exploring essential chemistry techniques, including real-life examples. Discover why measuring plating bath chemistry matters, the different ways to analyze it and the benefits of monitoring it as it happens in real-time. With XRF analysis, you'll gain the knowledge and tools to improve your plating process, thus ensuring top-notch efficiency and quality in surface finishing. Agenda: Importance of measuring plating bath chemistry Methods for analyzing bath chemistry Benefits of monitoring bath chemistry in real-time Case studies
In this high-level overview of wastewater system maintenance and upgrades, Robin Deal and Brian Greene will review the critical components required for a fully-functional system and discuss their expected life span. Learn to navigate factors such as material degradation and technological advancements, examine the effects, and address issues of chemical usage on the equipment. This webinar is designed to equip you with the knowledge needed to ensure your wastewater system remains in optimal condition, highlighting the importance of understanding both the hardware requirements and the chemical interactions that can influence system longevity and performance. By implementing proactive maintenance strategies and informed chemical management practices, you can enhance the reliability and efficiency of your wastewater infrastructure, ultimately contributing to environmental sustainability and public health protection. Agenda: Essential equipment for wastewater systems Life span considerations for wastewater systems Impact of chemical usage on wastewater equipment
Attend the Chicago Surface Finishing Annual Holiday Party Location: Church Street Brewing 1480 Industrial Dr. Unit C Itasca, IL 60143 $75 Includes: Fun, Food, and Drinks
Celebrate the fifth anniversary of The Cool Parts Show with a special LIVE episode! In 2019, Additive Manufacturing Media (AM) launched The Cool Parts Show, a video series dedicated to end-use parts made through 3D printing. To celebrate the show’s fifth anniversary, AM will host a special livestream episode on Thursday, Dec. 12, 2024, at 8 p.m. (EST). The show’s co-hosts, Peter Zelinski and Stephanie Hendrixson, will share updates about parts featured on the show, answer audience questions and give away Cool Parts merchandise.
Don't miss this fantastic chance to dive deeper into pretreatment and powder application! Join us to learn firsthand from two seasoned industry experts who will share proven methods and practical tips to elevate the quality and performance of your current system—all while reducing waste and minimizing rejects. From troubleshooting to performance optimization, this seminar covers it all, with each expert presenting valuable insights and making time to answer your pressing questions. Bring your unique challenges and questions for a truly interactive experience, and try to stump our knowledgeable speakers! The CCAI Northern California chapter president, Jeff Rochester, will highlight the value of CCAI Membership and the Peer Group Experience. “Being a Peer Group Member has been one of the most rewarding experiences I have had as a CCAI member.” Wrap up the seminar with dinner, networking, and a fun golf experience with your industry peers. Plus, you might even walk away with an exciting raffle prize! CLICK HERE to view the event flyer. SCHEDULE: 5 – 5:45 pm: Advanced Pretreatment and Troubleshooting – Come find out what you have been missing about your pretreatment system. Learn how to troubleshoot and solve issues with your pretreatment chemicals and equipment as well as tips and tricks on improving the efficiency of what you currently have. Speaker: Jeff Blaine 5:45 – 6:30 pm: Are you grounded? – One of the most important aspects of powder coating is your ground. Learn about the most common issue and ways to solve and improve it. Improve both your consistency and through put by having your coating equipment work for you. Set your system up for success to minimize rejects and rework while improving your quality. These are just a few of the topics that will be covered. Speaker: John Cole – Parker Ionics 6:30 – 9:30 pm: Dinner and Networking - Get ready to mingle and network with peers in the finishing industry. Come for some fun and friendly competition at one of the areas premier golf entertainment centers. Top Golf blends traditional golf with exciting and interactive video game elements. Cost: $100 members / $125 non-members CLICK HERE to register.
Save the date for the 2025 Florida Finishers Corp's Mid-Winter Conference. Please Register on the Florida Finishers Corp's Website https://www.floridafinisherscorp.com/ * Hotel information and discount code is on the FFC website *
Chicago Midwest Chapter of NASF Annual Business Meeting Election of Year 2025 Board of Directors Presentation of: The Bertram A. Stone Memorial Award Location: Westwood Tavern 1385 N. Meacham Rd., Schaumburg, IL Includes: Food and Drink
Each year Products Finishing partners with thousands of finishing operations in the U.S. to celebrate National Surface Finishing Day (NSFD) on the first Wednesday in March. NSFD is designed to celebrate and showcase the industry to trade schools, businesses, officials and media, as well as to celebrate employees and staff. The overarching goal of NSFD is to bring further awareness to the important roles plating and coating facilities play in their communities. Facilities are encouraged to host events and work with local media to build awareness about the contributions made by the surface finishing industry. For a helpful guide to reaching out to media outlets, download the NSFD toolkit here. How can you celebrate? Share your company’s story Hold an open house where the public can check out your facility –— either in person or virtual Offer student shop tours to local trade schools Invite local elected officials to visit and get to know your staff Celebrate your employees Share news about what you’re doing on social media and use the hashtag #NationalSurfaceFinishingDay or #NSFD
Thousands of people visit our Supplier Guide every day to source equipment and materials. Get in front of them with a free company profile.
Features stories and news on the adaptations of top shops, good habits, beneficial practices and successes that make a finishing shop a "Top Shop."
Young professionals are a vital asset to the finishing industry, and it is important to acknowledge those who are making great strides in shaping the industry's future.
Products Finishing is proud to announce a new awards program that recognizes individuals in the industry that are making important contributions to forward the surface finishing industry.
Reactive Surfaces, an innovator in bio-based coatings, works on development of Carbon Capture Coatings, which harness the natural CO2-capturing capabilities of live algae.
This Cincinnati-based plating company has experienced a 33% improvement as a result of investing in a new electroless nickel line. It continues to tweak the control technology to create the most effective coating for its customers’ needs.
Experts from MacDermid Enthone Industrial Solutions share industry insights in an interview from the SUR/FIN 2024 finishing industry tradeshow.
In these uncertain times, it is refreshing to hear from and learn about young talent in the surface finishing industry who are striving to make a difference within their organizations and the industry as a whole.
By replacing its immersion parts washer with a vacuum degreasing system, this machine shop is much more efficient, saving the company money, man hours and the health of the operators.
Finding a more accurate paint proportioner for its application enabled this auto parts manufacturer to save significant costs and labor while increasing capacity.
10 Point Checklist to Improve Your Parts Cleaning Processes
A collection of four PF features that delve into the technologies, processes and people working to provide protection for the automobiles of today.
Survey and analysis, with Hubbard-Hall, of Products Finishing Top Shops benchmarking attitudes and practices concerning parts cleaning.
Brush plating is an industrial electroplating process designed for demanding OEM and repair applications, without the use of an immersion tank. This presentation demonstrates the best practices for brush plating zinc-nickel to meet the ASTM standards of hydrogen embrittlement and corrosion protection. From preparatory steps to the application of a trivalent chromium conversion coating, the proper plating techniques needed to meet the customers’ demanding requirements are discussed.
Editor’s Note : The following is a paper based on a presentation given at NASF SUR/FIN 2019, in Rosemont, Illinois on June 5, 2019 in Session 13, Zinc Alloy Finishing Trends: Challenges & Prospects. A pdf of this paper can be accessed and printed HERE; the complete Powerpoint presentation is available by clicking HERE.
Abstract : Brush plating is an industrial electroplating process designed for demanding OEM and repair applications, without the use of an immersion tank. Many of today’s applications require well-engineered and proven deposits that pose as little risk as possible to both the operator and the environment. For the aerospace industry, zinc-nickel is a less toxic alternative to cadmium that can be used to repair damaged cadmium, zinc-nickel and IVD aluminum on high strength steels. It also meets the performance requirements of AMS 2451/9 and BAC 5664. What’s more, zinc-nickel does not require a post-plating, hydrogen embrittlement relief bake and can provide excellent corrosion protection - when properly applied. This presentation will demonstrate the best practices for brush plating zinc-nickel to meet the ASTM F519 standard of hydrogen embrittlement and corrosion protection. From preparatory steps to the application of a trivalent chromium conversion coating, the proper plating techniques needed to meet the customers’ demanding requirements are discussed.
For the aerospace industry, zinc-nickel is a less toxic alternative to cadmium that can be used to repair damaged cadmium, zinc-nickel and IVD aluminum on high strength steels. It meets the performance requirements of AMS 2451/9 and BAC 5664, requires no post-plating or hydrogen embrittlement relief bake, and can provide excellent corrosion protection when properly applied. This paper presents the best practices for brush plating zinc-nickel to meet the ASTM F519 standard of hydrogen embrittlement and the ASTM B117 standard of corrosion protection. A proprietary Zn-Ni process providing low hydrogen embrittlement (LHE) during brush plating is used in this study.*** From preparatory steps to the application of a trivalent chromium conversion coating, the proper plating techniques needed to meet the customers’ demanding requirements are discussed.
Selective plating, or more commonly brush plating, is a portable process for plating localized areas on a workpiece without the use of an immersion tank. There are four key elements to a brush plating set-up, shown in Fig. 1:
Figure 1 - Typical setup for selective / brush plating.
The anodes can consist of graphite, Dura-A-Form, platinum, or platinum-clad niobium or titanium. They are typically made to conform to the substrate to optimize thickness distribution. The red and black cables connect the power source to the anode and workpiece, and the green and black tubing provide solution circulation between reservoir and workpiece.
The rest of operation decisions are based on if the plating solutions need to be heated, flowed, or dipped, how the workpiece is to be masked to isolate the selected area, and whether any auxiliary equipment is needed to hold or rotate the part and/or or the plating tools.
Figure 2 - Selective plating operation.
As shown in Fig. 2, an electrolyte containing metal ions is introduced between a positively-charged anode (i.e., the preparatory or plating tool) and a negatively-charged cathode, (i.e., the workpiece). The anode itself is wrapped with a material that can be made of cotton, PermaWrap, red or white TuffWrap, etc. The wrap serves two main functions: to prevent an anode to cathode short-circuit and to act as the carrier for the solution which helps facilitate the current flow by wetting both electrodes to create the electrochemical cell. The solution can be introduced to the workpiece by flowing the solution through the anode using an external pump or by dip plating, where the anode is dipped into a beaker sitting near the workpiece.
A typical plating scheme consists of several preparatory steps that prepare the surface for the final metal deposition step. Each prep step requires a dedicated anode. The prep steps usually entail electroclean, etch, desmut and activation of the surface of the workpiece. The part is rinsed in between steps with DI water to avoid cross contamination and assure a clean work surface. After the workpiece has been properly prepared, a nickel preplate can applied and is substrate dependent.
The primary test method for evaluating hydrogen embrittlement is ASTM F519, which describes mechanical test methods and defines acceptance criteria for coating and plating processes that can cause hydrogen embrittlement in steels.† Specimens, as shown in Fig. 3 (Types 1.a1 and 1.a2 shown), are plated in accordance with the specification and maintained under sustained load in air to measure the time to rupture or completion of the test period. The entire notch and 0.5” on either side must be plated.
Figure 3- Layout of specimens used in hydrogen embrittlement testing of steels: (L)Type1.a1 and (R) 1.a2 notched bars.
Samples may be loaded individually or by multiples in a series. There is a minimum of four specimens used in each test. The samples undergo a sustained load which is maintained for a minimum of 200 hr at 75% of the tensile notched fracture strength (NFS).
In the event of one or more specimen fractures, those specimen(s) are removed and replaced with dummies and placed back under load. The total time off-load cannot exceed 10% of total test duration, and additional time in excess of 10% is added to the test. Fracture at any location other than the notch invalidates the test, and replacement testing may occur for all four specimens.
If there is no fracture, the plating process is non-embrittling. If one of the four fracture, the remaining three specimens may be step loaded every 2 hr in 5% increments to 90% of the NFS after completing the 200-hr sustained load. The process is considered non-embrittling, if the specimens survive 2 hr at 90% NFS. If two or more fracture, the plating process is considered to be embrittling.
Corrosion is evaluated according to ASTM B117, which describes the apparatus, procedure and conditions to create and maintain the salt spray test environment.†† The apparatus consists of a fog chamber, a salt solution reservoir, compressed air, an atomizing nozzle, specimen supports, chamber heating and a means of control of the salt spray environment. Test specimens are positioned 15-30º from vertical in the chamber, with no metal contact and unencumbered exposure to the salt fog. The salt solution consists of 5% sodium chloride in Type IV water and is atomized at 35 ± 2°C at pH 6.5-7.2. A minimum of two clean fog collectors are placed in the chamber. A collection rate of 1.0-2.0 mL/hr is specified. Testing is continuous, and the chamber can only be opened once daily for inspection of the samples.
There are two process/property specifications germane to this work. Boeing BAC 5664 outlines the “requirements for materials and procedures for deposition of ZnNi plating on low-alloy steel using the stylus electroplating process.” AMS 2451††† covers the “engineering requirements and process for brush plating of zinc-nickel by electrodeposition.” It is used, in conjunction with AMS 2451/9, for corrosion-protective, zinc-nickel deposits, which may allow omission of hydrogen embrittlement relief treatment of high-strength steel. The requirements of the two specifications are compared in Fig. 4.
Figure 4 - Comparison of Boeing 5664 and AMS 2451 specifications.
In BAC 5664, the anode may consist of graphite of high purity and density, or dimensionally-stable (DSA) platinum, platinum-iridium, platinum-plated titanium or platinum-plated niobium. Cotton batting and cotton or Dacron sleeving is specified. The maximum area of the ZnNi stylus plating is 5 in2, and the minimum thickness is 0.0005 in. During plating, the ZnNi is not pre-wetted and the electrolyte may be applied with a squeeze bottle or dip method. Stylus anode should be flush with the area being plated during operation and use a reciprocating back-and-forth or circular motion.
AMS 2451 covers the use of a chromate conversion coating. Types 1 and 2 designate respectively, (1) no chromate coating and (2) a chromate coating applied via a brush, spray or dip process. Further, grades A and B, designate a hexavalent or trivalent chromate process, respectively. The zinc-nickel composition range is 6 to 20% nickel, plated to a thickness of 0.0004 to 0.0007 in. Salt spray exposure time is 500 ± 1 hr, per ASTM B117. For a Type 1 finish, there should be no evidence of red corrosion after 500 hr. Type 2 should exhibit no evidence of white corrosion products after 96 hr and no evidence of red corrosion after 500 hr.
The goal of this portion of the study was for the Zn-Ni LHE coating to pass hydrogen embrittlement testing within 24 hr after plating on 1a.1 and 1a.2 bars with no post-deposition bake for hydrogen embrittlement relief. Even with the use of a “low hydrogen embrittlement” process, an amount of hydrogen is present in the deposit, albeit much reduced. Over time under ambient conditions after plating, a portion of the hydrogen will be released. The longer the time between plating, the lower the residual hydrogen. Production efficiencies are improved if this “relief” time can be reduced to 24 hr, while still passing the embrittlement test.
Specimen preparation was as follows:
The operational configuration is shown in Fig. 5.
Figure 5 - Zn-Ni brush plating configuration.
The experimental design involved the effect of a number of variables on hydrogen embrittlement performance. Constant current densities of 3 and 6 A/in2 were compared, along with a constant voltage of 6V. An anode conforming to the curvature of the test bar, with 50% effective electrical contact, was compared to the stylus type of anode, with 25% effective contact. The anode materials, graphite and DSA, were also compared. The tests were conducted in three phases, each one more stringent than the last. The goal of Phase 1 was to pass hydrogen embrittlement testing within 72 hr or less after plating at 3 and 6 A/in2. Phase 2 was intended to pass within (a) 48 hr and (b) 24 hr after plating at 6V (as per BAC 5664) and 6 A/in2. Phase 3 sought to pass in under 24 hr after plating at 6 A/in2.
Phase 1 compared post-plating times to test: ≤72 hr and approximately one week. In addition to the 3 and 6 A/in2 current density comparison, two test bar configurations (1.a1 and 1.a2) were compared. The effect of full and partial plating of the test bar was also explored, with samples prepared both fully plated from end to end and with plating only within ½” of the notch. All samples were plated with a 50% contact conforming, graphite anode. The results in Fig. 6 indicate that all samples passed ASTM F519.
Figure 6 - HE Phase 1 results per ASTM F519.
Given the results of Phase 1, the next phase was more stringent to decrease total process time. The plate-to-test times were shortened to 24 and 48 hr. The higher constant current density of 6 A/in2 was compared to a constant voltage of 6V (BAC 5664). Comparison of the two test bars and the two types of anode geometries was continued into this test. The 1a.2 bars were plated along the full length. All samples were plated with a graphite anode.
Figure 7 - HE Phase 2 results per ASTM F519.
The results are shown in Fig. 7, where the yellow highlighted conditions were found to pass ASTM F519. It can be seen that only three of the nine groupings passed. Of the three, only one was plated as planned (conforming anode at 6 A/in2). One (non-conforming stylus anode used at 6V) was delayed for 96 hr between plating and HE testing. The other (non-conforming stylus anode used at 6 A/in2) was plated at a higher current density (10-12 A/in2). It is notable that the 1a.2 test bars all showed failure with the shortened plate-to-test times.
Phase 3 took the results of the two previous experiments, optimizing conditions to reach the target of a 24-hr plate-to-test interval. With the shortest interval studied, comparisons were made of the anode material (DSA versus graphite) and the anode geometry (conforming with 50% contact area and the stylus). Additional variables were introduced, including the use of a neutral nickel strike prior to Zn-Ni LHE plating, a 20-V Zn-Ni strike prior to Zn-Ni LHE, and heating the of Zn-Ni LHE solution during plating. All specimens were plated at 6 A/in2.
Figure 8 - HE Phase 3 results per ASTM F519.
The results are shown in Fig. 8, where the yellow highlighted conditions passed ASTM F519. Here, five of eight groups passed. These groups all utilized the conforming anode geometry. Both DSA and graphite anodes met the standard with the conforming geometry at the CD of 6 A/in2 with the 24-hr waiting period. The three new variables with conforming graphite anodes and a current density of 6 A/in2 were successful. Again, using the 1.a1 test bars were superior to 1.a2 test bars, possibly related to geometric factors.
In summary, selectively plating Zn-Ni LHE can meet the requirements of ASTM F519 within 24 hr after plating under the following conditions:
The goal of the corrosion testing of Zn-Ni LHE was to pass the requirements of AMS 2451, i.e., no red corrosion at 500 hr for the plated coating without a conversion coating, and no white corrosion at 96 hr / no red corrosion at 500 hr with the conversion coating. The testing followed ASTM B117. Plate thickness was set at 0.00065 in. The following evaluation and comparisons were undertaken:
All photos of the salt spray results to follow show specimens that were rinsed with DI water, dried, then photographed. The dried surface is a more accurate representation of the severity of the corrosion result.
BAC 5664 process with Zn-Ni LHE
Specimens were prepared via BAC 5664. A stylus-type of graphite anode was used and a constant voltage of 6V was applied throughout the plating cycle. The minimum thickness was 0.0005 in. A trivalent conversion coating was applied after plating. Two methods of applying the conversion coating were compared: (a) immersion (dipping in a beaker containing the solution) and (b) squirting the coating solution of the surface from a squeeze bottle alternating 5 seconds of squirt and 15 seconds off until 90 seconds was reached. The results are shown in Fig. 9.
(a) Trivalent conversion coating applied by a 90-sec dip.
(b) Trivalent conversion coating applied by a 90-sec squirt/spray application.
Figure 9 - ASTM B117 corrosion test results for Zn-Ni LHE samples plated according to BAC 5664: (a) immersion and (b) sprayed trivalent conversion coating; Zn-Ni plating at a constant voltage of 6V, solution at room temperature; target thickness of 0.00065 in.
The dipped trivalent conversion coating produced slightly better results as compared to the squirted/sprayed trivalent conversion coating. All samples passed AMS 2451 - Type 2. A slight blushing was observed but no white corrosion at 96 hr and no red corrosion at 500 hr were observed. The average alloy composition with the BAC 5664 process was 8.8% Ni, with the balance zinc.
Traditional plating with Zn-Ni LHE
The next phase of the study dealt with traditional “dip” plating of Zn-Ni LHE, where the anode is repeatedly dipped into a beaker of solution every 5 seconds to ensure enough solution is present at the surface of the workpiece. A cotton wrap was used on the anode and a current density of 6 A/in2 was applied. The objective was to compare corrosion results for plated Zn-Ni LHE (a) with no conversion coating, (b) with a trivalent conversion coating and (c) with a hexavalent conversion coating. The conversion coating was applied with the squirt/spray method for 90 sec followed by a rinse and air dry. In the case of the hexavalent conversion process, the solution was heated to 95-100°F during application. The target thickness was 0.00065 in. These results would be compared with specimens plated with a brush or flow-plated regimen.
Figure 10 - Comparison of ASTM B117 corrosion performance for traditional dip plated Zn-Ni LHE: (a) with no conversion coating, (b) with a trivalent conversion coating and (c) with a hexavalent conversion coating.
The results are shown in Fig. 10. Both conversion coatings passed AMS 2451, with no white corrosion after 96 hr, and no red corrosion after 500 hr of ASTM B117 salt spray exposure. Specimens with no conversion coating failed AMS 2451, with red corrosion visible between 100 and 230 hr.
The nickel content in these samples plated at 6 A/in2 averaged 11.5%, higher than the 8.8% value produced at a constant 6V per BAC 5664.
Flow (brush) plating with Zn-Ni LHE
The next phase of study examined flow (brush) plating, where the solution was pumped through the anode for a constant supply at the work surface, with the goal of comparing the anode wrap and the question of constant voltage versus constant current density addressed in the previous phases of work. The anode wrap compared corrosion results for cotton, White Tuff and Red Tuff wraps. Results for the BAC 5664 constant 6V were compared with those for 6 A/in2. The target thickness was 0.00065 in. The trivalent conversion coating was used for all conditions, with the solution applied by a 90-sec squirt/spray application. The results are shown in Fig. 11.
(a) Cotton wrap with Tri Cr; 6V.
(b) Cotton wrap with Tri Cr; 6 A/in2.
(c) White Tuff wrap with Tri Cr; 6V.
(d) White Tuff wrap with Tri Cr; 6 A/in2.
(e) Red Tuff wrap with Tri Cr; 6V.
(f) Red Tuff wrap with Tri Cr; 6 A/in2.
Figure 11 - ASTM B117 corrosion test results for flow (brush) plated Zn-Ni LHE with a trivalent Cr conversion coating: comparison of cotton, White Tuff and Red Tuff anode wrap materials (top to bottom pairs); comparison of constant voltage (6V)(a, c, e) versus constant current density (6 A/in2)(b, d, f).
In general, the panels plated at a constant 6 A/in2 performed better than those plated at a constant 6V.
Comparing with the traditional plating results of Fig. 10, cotton wrap, white tuff wrap, and red tuff wrap all performed better than traditional dip plating at 250, 500 and 1000 hr of salt spray.
Figure 12 - Best results from ASTM B117 testing.
Analyzing all panels, the best corrosion results (Fig. 12) were obtained with flow (brush) plating at a constant current density of 6 A/in2, using cotton or White Tuff Wrap anode materials.
Future work with hydrogen embrittlement performance will focus on the inferior performance observed with the 1.a2 notched bars, including the those added processes that worked with 1.a1 bars: the neutral nickel strike, 20V Zn-Ni strike, and heating the Zn-Ni plating solution. Corrosion work will include studies of alternatives to the trivalent chromium conversion process. Studies on the lifetime of the Zn-Ni solution and how well it performs over the long term are planned.
Acknowledgements : The authors are indebted to the efforts of Teri Zarnesky, Lab Technician, Derek Vanek, Technical Manager, Derek Kilgore, Design and Project Engineer, Ken Mabe, Solution Manufacturing Technician, Mike Torma, Solution Manufacturing Technician and Jeff McArthur, Technical Service Representative.
Sarah Medeiros works as a Corrosion Engineer at Sifco ASC. She graduated from the University of Akron with a Bachelor of Science in Corrosion Engineering. Prior to joining Sifco ASC in 2018, Sarah had several co-op rotations at The Lubrizol Corporation working with rust preventives, corrosion inhibitors, and organic coatings and resins with experience in corrosion test methods.
Danijela Milosevic-Popovich, R&D Manager at Sifco ASC, joined the company in 2005. She is responsible for the design and execution of lab programs to develop and evaluate current products, new products and plating applications. She also provides the technical support and assistance to the quality, contract service and solutions manufacturing groups. She graduated from the State University of New York at Buffalo with a Bachelor of Science and Master of Engineering in chemical engineering. She then continued to earn her Master of Engineering Management from Ohio University. Prior to joining Sifco ASC, she worked in the semiconductor (IBM) and rubber industries.
*Compiled by Dr. James H. Lindsay, Technical Editor - NASF
** Corresponding authors:
*** Zinc-Nickel LHE® 4018/5970, Sifco ASC, Independence, Ohio, USA
† ASTM F519-18, Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments, ASTM International, West Conshohocken, PA, 2018, http://www.astm.org/cgi-bin/resolver.cgi?F519 .
†† ASTM B117-18, Standard Practice for Operating Salt Spray (Fog) Apparatus, ASTM International, West Conshohocken, PA, 2018, http://www.astm.org/cgi-bin/resolver.cgi?B117 .
††† AMS 2451, Plating, Brush General Requirements; AMS 2451/9C, Plating, Brush, Zinc-Nickel Low Hydrogen Embrittlement, SAE International, Warrendale, PA, 2019: https://www.sae.org/standards/content/ams2451 ; 2018: https://www.sae.org/standards/content/ams2451/9/ .
The National Association for Surface Finishing SUR/FIN 2023 surface finishing industry trade show will take place June 6-8, 2023 in Cleveland, Ohio.
Atlanta, Georgia, is the home to this year’s NASF SUR/FIN conference and trade show.
Hexavalent chromium is a known carcinogen, repro-toxin and mutagen. Its elimination is of high importance to the aerospace industry, which has struggled to find high performing alternatives. Legacy aluminum sacrificial paints have traditionally utilized hexavalent chromium to prevent corrosion and coatings which are equal to or better than have been difficult. This second of two papers discusses the hexavalent-chromium-free process from the user point-of-view in terms of the process validation work by Rolls Royce Corporation.
In the first part, a summary is presented on recently established nanotechnology initiatives in various countries around the world. Program funding levels and core activities will be compared to provide a basis for assessing business opportunities for various industries. The second part of the paper looks at specific examples of nanostructures made by electrochemical methods currently at various stages in their development, or already in use.
Debuting new speakers and cleaning technology content during this half-day workshop co-located with IMTS 2024.
According to Custom Fabricating and Supplies, a cleanroom is ideal for converting, die cutting, laminating, slitting, packaging and assembly of medical-grade products.
Baystar's Borstar technology is helping customers deliver better, more reliable production methods to greenhouse agriculture.
Dear Products Finishing Audience Member:
Starting on Thursday August 8, 2024, PF will begin “gating” its premium content, asking all new website users to provide some information about themselves — name, title, employer, email address — before they are provided free access to the content.
We are doing this because the ways PF’s audience finds and accesses our content is changing. Google’s search algorithms, increasingly, make it difficult to connect PF’s content with the people who might make use of it. On top of that, generative AI like ChatGPT is serving up PF content to internet users without attributing that content to PF.
As a result, it has become increasingly important for PF evolve its audience development strategy and learn as much as possible about who is accessing our content, what content they are accessing and how they are accessing it.
With this audience development strategy, we hope to do two things:
PF plays a distinctive role and has earned a place of esteem within the focused and specialized industry it serves. Large developments in the media landscape are forcing us to change the way we communicate with our audience. We are confident that our audience values the role PF plays in their professional lives and will join us in this effort to stay connected to them.
We thank you for your continued interest in and support of PF and welcome any questions you might have about the brand’s new content gating strategy.
Welcome! You’ve unlocked premium content.
If you have time, please tell us a little more about yourself.
Unlimited access to our free premium content requires a little more information from you.
Your email address will be used to communicate with you about Products Finishing subscription offers, related products and services. Refer to our Privacy Policy for more information. Wondering why you’re seeing this? Read more here.
inconel 600 625 718 nickel sheet Products Finishing is the media brand devoted to all things finishing. Electroplaters, anodizers, liquid and powder coaters have all come to rely on Products Finishing magazine as their No. 1 source for surface finishing news and technology for more than 80 years. About Us